Abstract
The isothermal oxidation behavior at 1000, 1050 and 1100°C and the cyclic oxidation behavior at 1000°C of the directionally solidified Ni-base superalloy DS951 were investigated. The oxidized samples were characterized by SEM, EDAX, XRD. The alloy DS951 obeyed a two-stage parabolic rate law during isothermal oxidation at 1000–1100°C. In cyclic conditions, the alloy showed no weight loss even after 1100 cycles. Cross-sectional examination revealed the development of faceted and needle-shaped AlN precipitates in the alloy subsurface region during cyclic oxidation, while no internal corrosion products were found in isothermal tests. Furthermore, a selective oxidation of MC carbides (M was predominately niobium with some chromium and tungsten) was observed along alloy grain boundaries and in interdendritic areas.
Similar content being viewed by others
References
B. A. Pint M. Treska L. W. Hobbs (1997) Oxidation of Metals 47 1 Occurrence Handle10.1007/BF01682369
G. C. Rybicki J. L. Smialek (1989) Oxidation of Metals 31 275 Occurrence Handle10.1007/BF00846690
S. C. Choi H. J. Cho Y. J. Kim D. B. Lee (1996) Oxidation of Metals 46 51 Occurrence Handle10.1007/BF01046884
J. Litz A. Rahmel M. Schorr (1988) Oxidation of Metals 30 95 Occurrence Handle10.1007/BF00656646
C. S. Giggins F. S. Pettit (1971) Journal of Electrochemical Society 118 1782
G. R. Wallwork A. Z. Hed (1971) Oxidation of Metals 3 171 Occurrence Handle10.1007/BF00603485
M. H. Li X. F. Sun T. Jin H. R. Guan Z. Q. Hu (2003) Oxidation of Metals 60 195 Occurrence Handle10.1023/A:1024629716452
W. Beele N. Czech W. J. Quadakkers W. Stamm (1997) Surface Coatings Technology 94 IssueID95 41 Occurrence Handle10.1016/S0257-8972(97)00473-8
S. Han D. J. Young (2001) Oxidation of Metals 55 223 Occurrence Handle10.1023/A:1010304026026
F. H. Yuan E. H. Han C. Y. Jo T. F. Li Z. Q. Hu (2003) Oxidation of Metals 60 211 Occurrence Handle10.1023/A:1026077417712
U. Krupp H.-J. Christ (2000) Metallurgical Transactions A 31 47
C. Wagner (1959) Zeitschrift Fur Elektrochemie 63 772
D. L. Douglass (1995) Oxidation of Metals 44 81 Occurrence Handle10.1007/BF01046724
J. Megusar G. H. Meier (1976) Metallurgical Transactions A 7 1133
F. H. Stott G. C. Wood D. P. Whittle B. D. Bastow Y. Shida A. Martinez-Villafane (1984) Solid State Ionics 12 365 Occurrence Handle10.1016/0167-2738(84)90166-8
M. Gobel A. Rahmel M. Schutze (1993) Oxidation of Metals 39 231 Occurrence Handle10.1007/BF00665614
T. F. An H. R. Guan X. F. Sun Z. Q. Hu (2001) Oxidation of Metals 54 301 Occurrence Handle10.1023/A:1004654429687
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Huang, L., Sun, X.F., Guan, H.R. et al. Oxidation Behavior of the Directionally Solidified Ni-base Superalloy DS951 in Air. Oxid Met 64, 303–318 (2005). https://doi.org/10.1007/s11085-005-8529-1
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/s11085-005-8529-1