Silicon crystallization in nanodot arrays organized by block copolymer lithography

  • Research Paper
  • Published:
Journal of Nanoparticle Research Aims and scope Submit manuscript

Abstract

Asymmetric polystyrene-b-polymethylmethacrylate (PS-b-PMMA) block copolymers are used to fabricate nanoporous PS templates with different pore diameter depending on the specific substrate neutralization protocol. The resulting polymeric templates are used as masks for the subsequent deposition of a thin (h = 5 nm) amorphous Si layer by electron beam evaporation. After removal of the polymeric film and of the silicon excess, well-defined hexagonally packed amorphous Si nanodots are formed on the substrate. Their average diameter (d < 20 nm), density (1.2 × 1011 cm−2), and lateral distribution closely mimic the original nanoporous template. Upon capping with SiO2 and high temperature annealing (1050 °C, N2), each amorphous Si nanodot rearranges in agglomerates of Si nanocrystals (d < 4 nm). The average diameter and shape of these Si nanocrystals strongly depend on the size of the initial Si nanodot.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Subscribe and save

Springer+ Basic
$34.99 /Month
  • Get 10 units per month
  • Download Article/Chapter or eBook
  • 1 Unit = 1 Article or 1 Chapter
  • Cancel anytime
Subscribe now

Buy Now

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6

Similar content being viewed by others

Explore related subjects

Discover the latest articles, news and stories from top researchers in related subjects.

References

  • Andreozzi A, Lamagna L, Seguini G, Fanciulli M, Schamm-Chardon S, Castro C, Perego M (2011a) The fabrication of tunable nanoporous oxide surfaces by block copolymer lithography and atomic layer deposition. Nanotechnology 22:335303

    Article  Google Scholar 

  • Andreozzi A, Poliani E, Seguini G, Perego M (2011b) The effect of random copolymer on the characteristic dimensions of cylinder-forming PS-b-PMMA thin films. Nanotechnology 22:185304

    Article  Google Scholar 

  • Bates FS, Fredrickson GH (1999) Block copolymers-designer soft materials. Phys Today 52(2):32–38

    Article  Google Scholar 

  • Castro C, Schamm-Chardon S, Pecassou B, Andreozzi A, Seguini G, Perego M, BenAssayag G (2013) In-plane organization of silicon nanocrystals embedded in SiO2 thin films. Nanotechnology 24:075302

    Article  Google Scholar 

  • Cheng JY, Ross CA, Smith HI, Thomas EL (2006) Templated self-assembly of block copolymers: top-down helps bottom-up. Adv Mater 18:2505–2521

    Article  Google Scholar 

  • Farrell RA, Petkov N, Morris MA, Holmes JD (2010) Self-assembled templates for the generation of arrays of 1-dimensional nanostructures: from molecules to devices. J Coll Int Sci 349:449–472

    Article  Google Scholar 

  • Gay G, Baron T, Agraffeil C, Salhi B, Chevolleau T, Cunge G, Grampeix H, Tortai J-H, Martin F, Jalaguier E, De Salvo B (2010) CMOS compatible strategy based on selective atomic layer deposition of a hard mask for transferring block copolymer lithography patterns. Nanotechnology 21:435301

    Article  Google Scholar 

  • Grom GF, Lockwood DJ, McCaffrey JP, Labbé HJ, Fauchet PM, White B Jr, Diener J, Kovalev D, Koch F, Tsybeskov L (2000) Ordering and self-organization in nanocrystalline silicon. Nature 407:358–361

    Article  Google Scholar 

  • Guarini KW, Black CT, Zhang Y, Babich IV, Sikorski EM, Gignac LM (2003) Low voltage, scalable nanocrystal flash memory fabricated by templated self assembly. In: Electron devices meeting, 2003. IEDM ‘03 technical digest. IEEE international, pp 22.2.1–22.2.4

  • Hazelton AJ, Wakamoto S, Hirukawa S, McCallum M, Magome N, Ishikawa J, Lapeyre C, Guilmeau I, Barnola S, Gaugiran S (2009) Double-patterning requirements for optical lithography and prospects for optical extension without double patterning. J Micro/Nanolith MEMS MOEMS 8:011003

    Article  Google Scholar 

  • Hong AJ, Liu C-C, Wang Y, Kim J, Xiu F, Ji S, Zou J, Nealey PF, Wang KL (2010) Metal nanodot memory by self-assembled block copolymer lift-off. Nano Lett 10:224–229

    Article  Google Scholar 

  • Hu H, Gopinadhan M, Osuji CO (2014) Directed self-assembly of block copolymers: a tutorial review of strategies for enabling nanotechnology with soft matter. Soft Matter 10:3867–3889

    Article  Google Scholar 

  • Jeong S-J, Xia G, Kim BH, Shin DO, Kwon S-H, Kang S-W, Kim SO (2008) Universal Block Copolymer Lithography for Metals, Semiconductors, Ceramics, and Polymers. Adv Mater 20:1898–1904

    Article  Google Scholar 

  • Jeong S-J, Kim JY, Kim BH, Moon H-S, Kim SO (2013) Directed self-assembly of block copolymers for next generation nanolithography. Mater Today 16:468–476

    Article  Google Scholar 

  • Kang GB, Kim YT, Park JH, Kim S-I, Sohn Y-S (2009) Fabrication of silicon nanodots on insulator using block copolymer thin film. Curr Appl Phys 9:e197–e200

    Article  Google Scholar 

  • Koo K, Ahn H, Kim S-W, Ryu DY, Russell TP (2013) Directed self-assembly of block copolymers in the extreme: guiding microdomains from the small to the large. Soft Matter 9:9059–9071

    Article  Google Scholar 

  • Li W, Yang S (2007) Creation of sub-20-nm contact using diblock copolymer on a 300 mm wafer for complementary metal oxide semiconductor applications. J Vac Sci Technol, B 25:1982–1984

    Article  Google Scholar 

  • Lupi FF, Giammaria TJ, Ceresoli M, Seguini G, Sparnacci K, Antonioli D, Gianotti V, Laus M, Perego M (2013) Rapid thermal processing of self-assembling block copolymer thin films. Nanotechnology 24:315601

    Article  Google Scholar 

  • Lupi FF, Giammaria TJ, Seguini G, Laus M, Enrico E, De Leo N, Boarino L, Ober CK, Perego M (2014a) Thermally induced orientational flipping of cylindrical phase diblock copolymers. J Mater Chem C 2:2175–2182

    Article  Google Scholar 

  • Lupi FF, Giammaria TJ, Seguini G, Vita F, Francescangeli O, Sparnacci K, Antonioli D, Gianotti V, Laus M, Perego M (2014b) Fine tuning of lithographic masks through thin films of PS-b-PMMA with different molar mass by rapid thermal processing. Appl Mater Interfaces 6:7180–7188

    Article  Google Scholar 

  • Park S, Kim B, Wang JY, Russell TP (2008) Fabrication of highly ordered silicon oxide dots and stripes from block copolymer thin films. Adv Mater 20:681–685

    Article  Google Scholar 

  • Perego M, Andreozzi A, Vellei A, Lupi FF, Seguini G (2013) Collective behavior of block copolymer thin films within periodic topographical structures. Nanotechnology 24:245301

    Article  Google Scholar 

  • Ross CA, Berggren KK, Cheng JY, Jung YS, Chang J-B (2014) Three-dimensional nanofabrication by block copolymer self-assembly. Adv Mater 26:4386–4396

    Article  Google Scholar 

  • Ruiz R, Sandstrom RL, Black CT (2007a) Induced orientational order in symmetric diblock copolymer thin films. Adv Mater 19:587–591

    Article  Google Scholar 

  • Ruiz R, Ruiz N, Zhang Y, Sandstrom RL, Black CT (2007b) Local defectivity control of 2D self-assembled block copolymer patterns. Adv Mater 19:2157–2162

    Article  Google Scholar 

  • Schamm S, Bonafos C, Coffin H, Cherkashin N, Carrada M, Assayag GB, Claverie A, Tencé M, Colliex C (2008) Imaging Si nanoparticles embedded in SiO2 layers by (S)TEM-EELS. Ultramicroscopy 108:346–357

    Article  Google Scholar 

  • Segalman RA, Yokoyama H, Kramer EJ (2001) Graphoepitaxy of spherical domain block copolymer films. Adv Mater 13:1152–1155

    Article  Google Scholar 

  • Seguini G, Giammaria TJ, Lupi FF, Sparnacci K, Antonioli D, Gianotti V, Vita F, Placentino IF, Hilhorst J, Ferrero C, Francescangeli O, Laus M, Perego M (2014) Thermally induced self-assembly of cylindrical nanodomains in low molecular weight PS-b-PMMA thin films. Nanotechnology 25:045301

    Article  Google Scholar 

  • The International Technology Roadmap for Semiconductors (ITRS) (2011) Emerging research materials. http://www.itrs.net/

  • Tsai H, Pitera JW, Miyazoe H, Bangsaruntip S, Engelmann SU, Liu C-C, Cheng JY, Bucchignano JJ, Klaus DP, Joseph EA, Sanders DP, Colburn ME, Guillorn MA (2014) Two-dimensional pattern formation using graphoepitaxy of PS-b-PMMA block copolymers for advanced FinFET device and circuit fabrication. ACS Nano 8:5227–5232

    Article  Google Scholar 

  • Tsybeskov L, Hirschman KD, Duttagupta SP, Zacharias M, Fauchet PM, McCaffrey JP, Lockwood DJ (1999) Phonon-assisted tunneling and interface quality in nanocrystalline Si/amorphous SiO2 superlattices. Appl Phys Lett 75:2265

    Article  Google Scholar 

  • Tsybeskov L, Kamenev BV, Sirenko AA, McCaffrey JP, Lockwood DJ (2010) Strain-induced lateral self-organization in Si/SiO2 nanostructures. Appl Phys Lett 96:013105

    Article  Google Scholar 

  • Xiao S, Yang XM, Edwards EW, La YH, Nealey PF (2005) Graphoepitaxy of cylinder-forming block copolymers for use as templates to pattern magnetic metal dot arrays. Nanotechnology 16:S324

    Article  Google Scholar 

  • Xu J, Hong SW, Gu W, Lee KY, Kuo DS, Xiao S, Russell TP (2011) Fabrication of silicon oxide nanodots with an areal density beyond 1 teradots inch−2. Adv Mater 23:5755–5761

    Article  Google Scholar 

  • Zacharias M, Streitenberger P (2000) Crystallization of amorphous superlattices in the limit of ultrathin films with oxide interfaces. Phys Rev B 62:8391–8396

    Article  Google Scholar 

  • Zacharias M, Blasing J, Veit P, Tsybeskov L, Hirschman K, Fauchet PM (1999) Thermal crystallization of amorphous Si/SiO2 superlattices. Appl Phys Lett 74:2614

    Article  Google Scholar 

  • Zucchi IA, Poliani E, Perego M (2010) Microdomain orientation dependence on thickness in thin films of cylinder-forming PS-b-PMMA. Nanotechnology 21:185304

    Article  Google Scholar 

Download references

Acknowledgments

This research activity was financially supported by the ERANET PLUS “NanoSci-E+” consortium through the NANO-BLOCK (“NANO-device fabrication using BLOCK-copolymer based technology”) project.

Author information

Authors and Affiliations

  1. Laboratorio MDM, IMM-CNR, Via C. Olivetti 2, 20864, Agrate Brianza, Italy

    Michele Perego, Andrea Andreozzi & Gabriele Seguini

  2. nMat Group, CEMES-CNRS, Université de Toulouse, 29 Rue J. Marvig, 31055, Toulouse Cedex 4, France

    Sylvie Schamm-Chardon, Celia Castro & Gerard BenAssayag

Authors
  1. Michele Perego
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Andrea Andreozzi
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Gabriele Seguini
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Sylvie Schamm-Chardon
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Celia Castro
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. Gerard BenAssayag
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Michele Perego.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Perego, M., Andreozzi, A., Seguini, G. et al. Silicon crystallization in nanodot arrays organized by block copolymer lithography. J Nanopart Res 16, 2775 (2014). https://doi.org/10.1007/s11051-014-2775-6

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1007/s11051-014-2775-6

Keywords

Search

Navigation