The chemical composition, morphology, and microstructure of peeling defects formed on the surface of sheets from steel 2205 under hot rolling are studied. The microstructure of the surface is analyzed using scanning electron and light microscopy. The zones affected are shown to contain nonmetallic inclusions of types Al2O3 and CaO – SiO2 – Al2O3 – MgO in the form of streak precipitates and to have an unfavorable content of austenite, which causes decrease in the ductility of the area. The results obtained are used to derive a five-stage phenomenological model of formation of such defects.
Similar content being viewed by others
References
V. A. Pirtskhalaishvili, Double-phase ferritic-austenitic chromium-manganese steel and its corrosion resistance as a function of the proportion of the structural components,” Metally, No. 3, 52 – 58 (2004).
I. Alvarez-Armas and S. Degallaix-Moreuil, Duplex Stainless Steels, Wiley-ISTE, London (2009).
A. P. Shlyamnev, O. V. Novichkova, and L. A. Pisarevskii, “Nitrogen-containing stainless steels: promising materials for manufacturin pipes resistant to hydrogen sulfide corrosion,” Probl. Chern. Metall. Matalloved., No. 1, 57 – 59 (2010).
S. Moir and J. Preston, “Surface defects evolution and behavior from cast slab to coated strip,” J. Mater. Proc. Technol., 125 – 126, 720 – 724 (2002).
Yuan Fang-ming, Liu Xiu-mei, and Wang Xin-hua, “Detection of surface upwarping and line defects for hot rolled plates,” Phys. Exam. Test., 22(6), 31 – 34 (2004).
WuCai-hong, Han Jing-tao, Liujing, et al., “Analysis on the edge surface upwarping of hot rolled strip,” J. Plast. Eng., 12(6), 23 – 25 (2005).
Cai Cai, Song Homg-mei, and Luo Su-zheng, “Analysis of surface cracks on duplex stainless steel 2205,” Shang Hai Metals, 33(1), 22 – 25 (2011).
Chen Shu-hao, Wang Xin-hua, Huang Fu-xiang, et al., “Characteristics and formation mechanisms of surface upwarp defects of hot rolled plate,” Special Steel, 32(5), 47 – 50 (2011).
Guilhem Martin, Sampath Kumar Yerra, and Yves Brecheta, “A macro- and micromechanics investigation of hot cracking in duplex steels,” Acta Mater., 60(11), 4646 – 4560 (2012).
Author information
Authors and Affiliations
Corresponding author
Additional information
Translated from Metallovedenie i Termicheskaya Obrabotka Metallov, No. 1, pp. 29 – 32, January, 2017.
Rights and permissions
About this article
Cite this article
Yong-jun, Z., Hui, Z. & Jing-tao, H. Phenomenological Model Describing the Formation of Peeling Defects on Hot-Rolled Duplex Stainless Steel 2205. Met Sci Heat Treat 59, 30–33 (2017). https://doi.org/10.1007/s11041-017-0097-x
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11041-017-0097-x