Buckling Modes of Structural Elements of Off-Axis Fiber-Reinforced Plastics

  • V. N. Paimushin
  • N. V. Polyakova
  • S. A. Kholmogorov
  • M. A. Shishov
Article
  • 50 Downloads

The structures of two types of unidirectional fiber-reinforced composites — with an ELUR-P carbon fiber tape, an XT-118 cold-cure binder with an HSE 180 REM prepreg, and a hot-cure binder — were investigated. The diameters of fibers and fiber bundles (threads) of both the types of composites were measured, and their mutual arrangement was examined both in the semifinished products (in the uncured state) and in the finished composites. The defects characteristic of both the types of binder and manufacturing technique were detected in the cured composites. Based on an analysis of the results obtained, linearized problems on the internal multiscale buckling modes of an individual fiber (with and without account of its interaction with the surrounding matrix) or of a fiber bundle are formulated. In the initial atate, these structural elements of the fibrous composites are in a subcritical (unperturbed) state under the action of shear stresses and tension (compression) in the transverse direction. Such an initial stress state is formed in them in tension and compression tests on flat specimens made of off-axis-reinforced composites with straight fibers. To formulate the problems, the equations derived earlier from a consistent variant of geometrically nonlinear equations of elasticity theory by reducing them to the one-dimensional equations of the theory of straight rods on the basis of a refined Timoshenko shear model with account of tensile-compressive strains in the transverse direction are used. It is shown that, in loading test specimens, a continuous rearrangement of composite structure can occur due to the realization and continuous change of internal buckling modes as the wave-formation parameter varies continuously, which apparently explain the decrease revealed in the tangential shear modulus of the fibrous composites with increasing shear strains.

Keywords

fiber-reinforced plastic structural elements fiber binder test specimen off-axis reinforcement tension-compression linearized equations buckling modes wave parameter critical load 

Notes

Acknowledgements

The results of this research are obtained within the framework of State Task of the Ministry of Education and Science of Russia No. 9.5762.2017/VU (project No. 9.1395.2017/PCh).

References

  1. 1.
    A. N. Guz, Stability of Elastic Bodies at Finite Strains [in Russian], Naukova Dumka, Kiev (1973).Google Scholar
  2. 2.
    V. V. Bolotin and Yu. N. Novichkov, Mechanics of Multilayered Structures [in Russian], Mashinostoyenie, Moscow (1980).Google Scholar
  3. 3.
    A. N. Polilov, Etudes on Mechanics of Composites [in Russian], Fizmatlit, Moscow (2015).Google Scholar
  4. 4.
    M. A. Alimov, A. M. Dumanskii, and A. A. Radchenko, “An analysis of the nonlinear deformation of an angle-ply CFRP in uniaxial tension,” Probl. Mashinostr. Nadezhn. Mashin, No. 2, 39-44 (2012).Google Scholar
  5. 5.
    A. M. Dumanskii, M. A. Alimov, and A. A. Radchenko, “An analysis of the nonlinear behavior of a composite material in uniaxial tension,” Inform. Svyaz’, No. 1, 69-72 (2013).Google Scholar
  6. 6.
    V. N. Paimushin, D. V. Tarlakovskii, and C. A. Kholmogorov, “On a nonclassical buckling form and failure of composite tests-specimens in three-point bending,” Uch. Zap. Kazan Universitiy, Ser. Phys.-Mat. Nauki, 158, No. 3, 350-375 (2016).Google Scholar
  7. 7.
    V. N. Paimushin and S. A. Kholmogorov, “Physical-mechanical properties of a fiber-reiforced composite based on an ELUR-P carbon tape and an ХТ-118 binder,” Mech. Compos. Mater., 54, No. 1, 2-12 (2017).CrossRefGoogle Scholar
  8. 8.
    B. W. Rosen, “Mechanics of composite strengthening in fiber composite materials,” Am. Soc. Metals, Metals Park, Ohio, 37-75 (1965).Google Scholar
  9. 9.
    B. Budiansky and N. A. Fleck, “Compressive failure of fiber composites,” J. Mech. Phys. Solids, 41, No. 1, 183-211 (1993).CrossRefGoogle Scholar
  10. 10.
    K. H. Lo and E. S. M. Chim, “Compressive strength of unidirectional composites,” J. Reinf. Plast. Compos., 11, No. 8, 838-896 (1992).CrossRefGoogle Scholar
  11. 11.
    Y. L. Xu and K. L. Reifsnider, “Micromechanical modeling of composite compressive strength,” J. Compos. Mater., 27, No. 6, 572-588 (1993).CrossRefGoogle Scholar
  12. 12.
    A. Jumahat, C. Soutis, F. R. Jones, and A. Hodzic, “Fracture mechanisms and failure analysis of carbon fibre/toughened epoxy composites subjected to compressive loading,” Compos. Struct., 92, No. 2, 295-305 (2010).CrossRefGoogle Scholar
  13. 13.
    M. Meng, H. R. Le, M. J. Rizvi, and S. M. Grove, “The effects of unequal compressive/tensile moduli of composites,” Compos. Struct., 126, 207-215 (2015).CrossRefGoogle Scholar
  14. 14.
    J. Ye, Y. Qiu, X. Chen, and J. Ma, “Initial and final failure strength analysis of composites based on a micromechanical method,” Compos. Struct., 125, 328-335 (2015).CrossRefGoogle Scholar
  15. 15.
    T. J. Vaughan and C. T. McCarthy, “A combined experimental-numerical approach for generating statistically equivalent fibre distributions for high strength laminated composite materials,” Compos. Sci. Technol., 70, 291-297 (2010).CrossRefGoogle Scholar
  16. 16.
    R. Talreja, “Assessment of the fundamentals of failure theories for composite materials,” Compos. Sci. Technol., 105, 190-201 (2014)CrossRefGoogle Scholar
  17. 17.
    M. Hojo, M. Mizuno, T. Hobbiebrunken, T. Adachi, M. Tanaka, and S. K. Ha, “Effect of fiber array irregularities on microscopic interfacial normal stress states of transversely loaded UD-CFRP from viewpoint of failure initiation,” Compos. Sci. Technol., 69, Nos. 11-12, 1726-1734 (2009).CrossRefGoogle Scholar
  18. 18.
    D790-03 2005. Standard Test Methods for Flexural Properties of Unreinforced and Reinforced Plastics and Electrical Insulating Materials, Vol. 08.01, Plastics. ASTM Int., West Conshohocken, PA.Google Scholar
  19. 19.
    D2344/D2344M-00, 2005. Standart Test Method for Short-Beam Strength of Polymer Matrix Composite Materials and their Laminates, Vol. 15.03, Space Simulation; Aerospace and Aircraft; Composite Materials. ASTM Int., West Conshohocken, PA.Google Scholar
  20. 20.
    GOST 32659−2014. Polymer Composites. Test Methods. Determination of the Apparent Ultimate Strength in Interlaminar Shear by Testing a Short Beam.Google Scholar
  21. 21.
    V. N. Paimushin and V. I. Shalashilin, “The relations of deformation theory in the quadratic approximation and the problems of constructing improved versions of the geometrically non-linear theory of laminated structures,” J. Appl. Math. Mech., 69, No. 5, 773-791 (2005).CrossRefGoogle Scholar
  22. 22.
    V. N. Paimushin, “Problems of geometric non-linearity and stability in the mechanics of thin shells and rectilinear columns,” J. Appl. Math. Mech., 71, No. 5, 772-805 (2007).CrossRefGoogle Scholar
  23. 23.
    V. N. Paimushin and N. V. Polyakova, “The consistent equations of the theory of plane curvilinear rods for finite displacements and linearized problems of stability,” J. Appl. Math. Mech., 73, No. 2, 220-236 (2009).CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC, part of Springer Nature 2018

Authors and Affiliations

  • V. N. Paimushin
    • 1
    • 2
  • N. V. Polyakova
    • 1
    • 2
  • S. A. Kholmogorov
    • 1
  • M. A. Shishov
    • 1
  1. 1.A. N. Tupolev Kazan National Research Technical UniversityKazanRussia
  2. 2.Kazan (Volga region) Federal UniversityKazanRussia

Personalised recommendations