Dependence of the Strength of Powder Steel Formed by Electro-Contact Compaction on Iron Powder Preparation Method

  • T. A. Litvinova
  • S. N. Egorov

Results are presented for the dependence of ultimate strength on electro-contact compaction parameters for an iron-graphite composite based on sprayed and reduced powders. A production regime is determined for electro-contact compaction providing the formation of powder steel with maximum ultimate strength. The dependence of ultimate strength on residual porosity is considered.


compactability interparticle consolidation iron-graphite composite ultimate strength porosity 


  1. 1.
    S. N. Egorov, Yu. Yu. Medvedev, M. S. Egorov, and I. F. Egorova, Patent 2210460 RF, IPC B22F3/105, “Method for preparing objects from a charge based on metal powder,” subm. 12.06.2001, publ. 08.20.2003.Google Scholar
  2. 2.
    T. A. Litvinova and S. N. Egorov, “Mechanical properties of powder steel prepared by electro-contact compaction,” Metallurg, No. 1, 65–67 (2010).Google Scholar
  3. 3.
    A. A. Metsler, Structure and Properties of Powder Bronzes Formed with Electro-Contact Compaction: Auth. Abstr. Dissert. Cand. Techn. Sci., Novocherkassk (2007).Google Scholar
  4. 4.
    T. A. Litvinova and S. N. Egorov, “Effect of method for preparing iron powder on powder steel formation by electro-contact compaction,” Metallurg, No. 3, 57–60 (2015).Google Scholar
  5. 5.
    D. V. Volzhin, Increase in the Efficiency of Charge Preparation and Formation of Porous Workpieces for Providing the Required Powder Component Quality: Dissert. Cand. Sci., Novocherkassk (2001).Google Scholar
  6. 6.
    T. A. Litvinova, Yu. Yu. Medvedev, and S. N. Egorov, “Device and technology for ultrasonic electro-contact compaction,” Kontsept: Nauch.-Metod. Elktron. Zh., No. 3 (2015),
  7. 7.
    T. A. Litvinova, Formation of Powder Steel by Electro-Contact Compaction: Auth. Abstr. Diss. Cand. Techn. Sci., Novocherkassk (2010).Google Scholar
  8. 8.
    V. Yu. Dorofeev and S. N. Egorov, Interparticle Contact during Formation of Powder Hot-Worked Materials, Metallurgizdat, Moscow (2003).Google Scholar
  9. 9.
    S. N. Egorov and M. S. Egorov, New Hot-Worked Powder Low-Alloy Structural Steels, YuRGTU(NPI), Novocherkassk (2008).Google Scholar

Copyright information

© Springer Science+Business Media, LLC, part of Springer Nature 2018

Authors and Affiliations

  1. 1.Sevastopol State UniversitySevastopolRussia
  2. 2.Platov South-Russia State Polytechnic University (NPI)NovocherkasskRussia

Personalised recommendations