Features of nonmetallic inclusion formation and evolution in the course of treating spring steel of 54SiCr6 (60S2KhA) grade are studied. It is established that the majority of nonmetallic inclusions (NI) present within steel are complex oxides of the composition SiO2–MnO–Al2O3–CaO–MgO, at whose surface during steel crystallization and cooling as a rule there is a deposit of MnS. NI composition changes in the course of metal treatment. At the start of treatment, their base is MnO–SiO2–Al2O3, and subsequently there is an increase in content of CaO and MgO as a result of molten metal reaction with slag and lining. The average NI size and overall oxygen content decrease in the course of steel treatment, and this points to effective refining. The composition of NI present is close to that of the slag cover assimilating layer used in the intermediate ladle. A more significant increase is noted in MgO and Al2O3 content within it, and this points to effective assimilation of NI of the most unfavorable types.
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs11015-016-0194-x/MediaObjects/11015_2016_194_Fig1_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs11015-016-0194-x/MediaObjects/11015_2016_194_Fig2_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs11015-016-0194-x/MediaObjects/11015_2016_194_Fig3_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs11015-016-0194-x/MediaObjects/11015_2016_194_Fig4_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs11015-016-0194-x/MediaObjects/11015_2016_194_Fig5_HTML.gif)
Similar content being viewed by others
References
A. I. Zaitsev, K. A. Kosyrev, and I. G. Rodionova, “Contemporary trends in development of metallurgical technology for achieving a good set of service properties and high quality steel indices,” Probl. Chern. Metal. Materialoved., No. 3, 5–15 (2012).
A. I. Zaitsev, A. B. Stepanov, V. A. Sarychev, and A. Yu. Dzyuba, “Study of types, reasons for occurrence of defects of continuously cast billet rolled product and finished objects of spring steels, including nonmetallic inclusion formation,” Probl. Chern. Metal. Materialoved., No. 1, 35–45 (2015).
A. I. Zaitsev, A. B. Stepanov, V. A. Sarychev, et al., “Study of the effect of content and form of impurities present, nonmetallic inclusions on qualitative properties of spring steels,” Metallurg, No. 3, 40–47 (2015).
Slag Atlas [Russian translation], Metallurgiya, Moscow (1985).
E. Kh. Shakhpazov, A. I. Zaitsev, I. G. Rodionova, and G. V. Semerkin, “Key areas of development of metallurgical technology for satisfying an increasing requirement for steel quality,” Elektrometallurgiya, No. 2, 2012 (2011).
A. I. Zaitsev, I. G. Rodionova, G. V. Semernin, et al., “New types of unfavorable nonmetallic inclusions based MgO−Al2O3 and metallurgical factors governing their content within metal. Pt. 1,” Metallurg, No. 2, 50–55 (2011).
T. Fujisawa and H. Sakao, “Equilibrium relations between the liquid iron alloys and deoxidation products resulting from Mn–Si–Al complex deoxidation,” Tetsu-to-Hagane, 63, No. 9, 1494–1503 (1977).
Author information
Authors and Affiliations
Corresponding author
Additional information
Translated from Metallurg, No. 10, pp. 45–49, October, 2015.
Rights and permissions
About this article
Cite this article
Stepanov, A.B., Zaitsev, A.I., Sarychev, B.A. et al. Evolution of Nonmetallic Inclusions During Spring Steel Treatment. Metallurgist 59, 917–922 (2016). https://doi.org/10.1007/s11015-016-0194-x
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11015-016-0194-x