We study the crack resistance of 20 and 30KhМА steels in a NACE hydrogen-sulfide solution under static and repeated static stresses and found their threshold stress intensity factors. A conclusion is made that these steels almost satisfy the criteria of their applicability in hydrogen-sulfide media accepted in the engineering practice.
Similar content being viewed by others
References
NACE Standard TM 0177-90. Standard Test Method Laboratory of Metals for Resistance to Sulfide Stress Corrosion Cracking in H 2 S Environments, National Association of Corrosion Engineering (NACE), Houston, TX. (1990).
M. S. Khoma, M. R. Chuchman, V. R. Ivashkiv, and H. M. Sysyn, “Influence of cyclic loads on the fracture resistance of pipe steels and their welded joints in hydrogen-sulfide media,” Fiz.-Khim. Mekh. Mater., 49, No. 3, 52–57 (2013); English translation: Mater. Sci., 49, No. 3, 334–340 (2013).
V. I. Pokhmurs’kyi, M. S. Khoma, H. V. Krutsan, and M. R. Chuchman, “Influence of the conditions of loading on the resistance of structural steels to stress-corrosion fracture in hydrogen-sulfide solutions,” in: V. V. Panasyuk (editor), Fracture Mechanics of Materials and Strength of Structures [in Ukrainian], Karpenko Physicomechanical Institute, Ukrainian National Academy of Sciences, Lviv (2009), pp. 765–770.
MSKR-01-85. Procedure of Testing for the Resistance to Hydrogen-Sulfide Corrosion Cracking [in Russian], Izd. GKNT SSSR, Moscow (1985).
B. Graig, “Limitations of alloying to improve the threshold for hydrogen stress cracking of steels,” in: Hydrogen Effects on Material Behavior, Proc. of the 4th Internat. Conf. on the Effect of Hydrogen on the Behavior of Materials (Wyoming, Sept. 12–15, 1989), pp. 223–230 (1989).
M. S. Khoma, M. R. Chuchman, and B. M. Datsko, “Degree of hydrogenation of 17G1SU steel in the process of its corrosion in solutions in the presence of hydrogen sulfide,” in: Contemporary Problems of Electrochemistry: Education, Science, Industry [in Ukrainian], “Kharkiv Politekh. Inst.” Nats. Tekh. Univ., Kharkiv (2015), pp. 24–25.
Author information
Authors and Affiliations
Corresponding author
Additional information
Translated from Fizyko-Khimichna Mekhanika Materialiv, Vol. 52, No. 4, pp. 76–78, July–August, 2016.
Rights and permissions
About this article
Cite this article
Chuchman, М.R. Static Crack Resistance of 20 and 30KhMA Steels in a Nace Solution. Mater Sci 52, 530–532 (2017). https://doi.org/10.1007/s11003-017-9986-9
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11003-017-9986-9