We develop a method for the evaluation of the influence of hydrogen on the strength and durability of the drum of a high-pressure steam boiler subjected to thermal cycling and hydrogenation. We analyze the influence of hydrogen on the accumulation of damage to the metal and the duration of operation of the drum for different modes of damage. It is established that hydrogen accelerates the accumulation of damage and reduces the period of operation of metals by 25–30% for planned shutdowns of the boilers and by 40–50% for their emergency shutdowns.
Similar content being viewed by others
References
Instruction SOU 40.1-21677681-02:2009. Procedure of Prolongation of the Service Life of the Drums of High-Pressure Boilers [in Ukrainian], Haluzevyi Rezervno-Investytsiinyi Fond Rozvytku Enerhetyky, Kyiv (2009).
H. M. Nykyforchyn, O. Z. Student, H. V. Krechkovs’ka, and A. D. Markov, “Evaluation of the influence of shutdowns of a technological process on changes in the in-service state of the metal of main steam pipelines of thermal power plants,” Fiz.-Khim. Mekh. Mater., 46, No. 2, 42–54 (2010); English translation: Mater. Sci., 46, No. 2, 177–189 (2010).
B. Drobenko and O. Buryk, “Mathematical modeling of the processes of deformation of structural element under thermal-and-force loading,” Fiz.-Mat. Model. Inform. Tekhnol., Issue 20, 117–126 (2014).
I. I. Ovchinnikov, “Influence of hydrogen-containing media at high temperatures and pressures on the behavior of metals and metal structures,” Internet J. Naukovedenie, No. 4, 1–28 (2012).
V. Panasyuk, Ya. Ivanytskyi, and O. Hembara, “Assessment of hydrogen effect on fracture resistance under complex-mode loading,” Eng. Fract. Mech., 83, 54–61 (2012).
V. V. Panasyuk, Ya. L. Ivanyts’kyi, O. V. Hembara, and V. M. Boiko, “Influence of the stress-strain state on the distribution of hydrogen concentration in the process zone,” Fiz.-Khim. Mekh. Mater., 50, No. 3, 7–14 (2014); English translation: Mater. Sci., 50, No. 3, 315–323 (2014).
Ya. L. Ivanyts’kyi, O. V. Hembara, and O. Ya. Chepil’, “Determination of the durability of elements of power-generating equipment with regard for the influence of working media,” Fiz.-Khim. Mekh. Mater., 51, No. 1, 93–101 (2015); English translation: Mater. Sci., 51, No. 1, 104–113 (2015).
M. Stashchuk and M. Dorosh, “Evaluation of hydrogen stresses in metal and redistribution of hydrogen around cracklike defects,” Int. J. Hydrogen Energy, 37, 14687–14696 (2012).
Ya. L. Ivanyts’kyi, P. S. Kun’, S. T. Shtayura, and V. M. Mochul’s’kyi, “Theoretical-experimental approach to the analysis of fatigue crack propagation in hydrogenated materials,” Fiz.-Khim. Mekh. Mater., 46, No. 2, 77–82 (2010); English translation: Mater. Sci., 46, No. 2, 213–220 (2010).
O. E. Andreikiv and O. V. Hembara, Fracture Mechanics and Durability of Metallic Materials in Hydrogen-Containing Media [in Ukrainian], Naukova Dumka, Kyiv (2008).
Ya. L. Ivanyts’kyi, S. T. Shtayura, Yu. V. Mol’kov, and T. M. Lenkovs’kyi, “Influence of hydrogen on the fracture resistance of 65G sheet steel,” Fiz.-Khim. Mekh. Mater., 47, No. 4, 36–40 (2011); English translation: Mater. Sci., 47, No. 4, 457–461 (2012).
Y. Ivanytskyj, S. Shtayura, Y. Molkov, and T. Lenkovskyi, “Hydrogen influence on fracture of sheet carbon steel,” Int. J. Fracture, 176, No. 1, 17–23 (2012).
Author information
Authors and Affiliations
Corresponding author
Additional information
Translated from Fizyko-Khimichna Mekhanika Materialiv, Vol. 53, No. 1, pp. 90–95, January–February, 2017.
Rights and permissions
About this article
Cite this article
Hembara, О.V., Chepil’, О.Y. & Hembara, Т.V. Application of the Energy Approach to the Evaluation of the Serviceability of the Drum of a Steam Boiler Subjected to Thermal Cycling and Hydrogenation. Mater Sci 53, 102–108 (2017). https://doi.org/10.1007/s11003-017-0049-z
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11003-017-0049-z