Abstract
In this work, spinels with the general formula Zn2−xCoxTiO4 were synthesized by the polymeric precursor method and thermally treated at 1,000 °C. The powder precursors were characterized by TG/DTA. A decrease in the DTA peak temperature with the amount of zinc was observed. After the thermal treatment, the characterizations were performed by XRD, IR, colorimetry and UV/VIS spectroscopy. The XRD patterns of all the samples showed the presence of the spinel phase. Infrared spectroscopy showed the presence of ester complexes for Zn2TiO4 after thermal treatment at 500 °C, which disappeared after cobalt addition, indicating that organic material elimination was favored.
Similar content being viewed by others
References
Müller-Buschbaum Hk. The crystal chemistry of AM2O4 oxometallates. J Alloy Compd. 2003;349:49–104.
Leite ER, Souza CMG, Longo E, Varela JÁ. Influence of the polymerization on the synthesis of SrTiO3: Part I, characteristics of the polymerics precursors and its thermal decomposition. Ceram Int. 1995;21:143–52.
Pechini MP. US Patent, No. 3.330.697 (1967).
Alves MCF, Souza SC, Lima SJG, Longo E, Souza AG, Santos IMG. Influence of the precursor salts in the synthesis of CaSnO3 by the polymeric precursor method. J Therm Anal Calorim. 2007;87:763–6.
Silva MRS, de Miranda LCO, Cassia-Santos MR, Lima SJG, Soledade LEB, Longo E, et al. Influence of the network former on the properties of magnesium spinels. J Therm Anal Calorim. 2007;87:753–7.
Souza SC, Souza MAF, Lima SJG, Santos MRC, Fernandes VJ Jr, Soledade LEB, et al. The effects of Co, Ni and Mn on the thermal processing of Zn2TiO4 pigments. J Therm Anal Calorim. 2005;79:455–9.
Silva MRS, Souza SC, Santos IMG, Santos MRC, Soledade LEB, Souza AG, et al. Stability studies on undoped and doped Mg2TiO4 obtained by the polymeric precursor method. J Therm Anal Calorim. 2005;79:421–4.
Souza MAF, Candeia RA, Lima SJG, Santos MRC, Santos IMG, Longo E, et al. Thermal and structural characterization of Sr1−xCoxTiO3 obtained by polymeric precursor method. J Therm Anal Calorim. 2005;79:407–10.
Gouveia DS, Rosenhaim R, Lima SJG, Longo E, Souza AG, Santos IMG. The characterization of CoxZn7−xSb2O12 spinel obtained by the Pechini method. Mater Res. 2005;8:213–9.
Nakamoto K. Infrared and Raman spectra of inorganic and coordination compounds. New York: Willey; 1986.
Dibb A, Tebcherani SM, Lacerda W Jr, Santos MRC, Cilense M, Varela JA, et al. Influence of simultaneous addition of MnO2 and CoO on properties of SnO2-based ceramics. Mater Lett. 2000;46:39–43.
Chiang YM, Birnie DIII, Kingery WD. Physical ceramics—principles for ceramic science and engineering. New York: Wiley; 1997.
Wood DL, Tauc J. Weak absorption tails in amorphous semi-conductors. Phys Rev B. 1972;5:3144–51.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Santos, C.L., Capistrano, B.J.S., Vieira, F.T.G. et al. Structural and thermal characterization of Zn2−xCoxTiO4 . J Therm Anal Calorim 97, 137–141 (2009). https://doi.org/10.1007/s10973-009-0240-z
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10973-009-0240-z