Abstract
The phase stability of the system Gd2O3-Nd2O3 up to 1350°C was studied. Mixed oxides were synthesized by coprecipitation of mixed oxalates. Depending on the thermal treatment, three possible structures of the oxides, namely the A (hexagonal, P63/mmm), B (monoclinic, C2/m) and C (cubic, Ia3) forms, were obtained. Below 1300°C the system Gd2O3-Nd2O3 shows three monophasic (A, B and C phase) and three biphasic regions (A+B, B+C and A+C phase). Below 550°C the C phase is stable over the whole composition range. A validation procedure for the existence of the C phase in pure Nd2O3 was also set up.
Similar content being viewed by others
References
A. G. Dedov and A. S. Loktev, Appl. Catal. A: Gen., 245 (2003) 209.
R.-Q. Liu, Y.-H. Xie, J.-D. Wang, Z.-J. Li and B.-H. Wang, Solid State Ion., 177 (2006) 73.
R. Reisfeld and K. Jorgensen, Lasers and excited states of rare earths, Springer, New York 1978.
E. Antic-Fidancev, J. Hölsa and M. Lastusaari, J. Alloys Compd., 341 (2002) 82.
P. Mele, C. Artini, R. Masini, G. A. Costa, A. Hu, N. Chikumoto and M. Murakami, Physica C, 391 (2003) 49.
A. Ubaldini, F. Giovannelli and I. Monot-Laffez, Phys. C, 383 (2003) 107.
L. Eyring, Handbook of Physics and Chemistry of Rare Earths, K. A. Gschneidner and L. Eyring, Eds, North Holland 1979, Vol. 3, p. 337.
G. Adachi and N. Imanaka, Chem. Rev., 98 (1998) 1479.
H. R. Hoekstra, Inorg. Chem., 5 (1966) 754.
N. Imanaka, T. Masui and Y. Kato, J. Solid State Chem., (2005) 395.
J. P. Traverse and M. Foëx, Rev. Int. Hautes Temp. Refract., 3 (1966) 429.
N. Hirosaki, S. Ogata and C. Kocer, J. Alloys Compd., 351 (2003) 31.
J. Tong and L. Eyring, J. Alloys Compd., 225 (1995) 139.
M. Zinkevich, Prog. Mater. Sci., 52 (2007) 597.
V. M. Goldschmidt, T. Barth, G. Lunde and W. Zachariasen, Skr. Norske Vidensk.-Akad. Oslo I. Mat. Naturvidensk. Kl., 2 (1926).
L. Eyring, Handbook of Physics and Chemistry of Rare Earths, K. A. Gschneidner and L. Eyring, Eds, North Holland 1979, Vol. 3., 401E I. Warshaw and R. Roy, J. Phys. Chem., 65 (1961) 2048.
J. P. Coutures, R. Verges and M. Foëx, Rev. Int. Hautes Temp. Refract., 12 (1975) 181.
J. C. Panitz, J. C. Mayor, B. Grob and W. Durisch, J. Alloys Compd., 303–304 (2000) 340.
P. Mele, C. Artini, R. Masini, G. A. Costa, A. Hu, N. Chikumoto and M. Murakami, Phys. C, 412–414 (2004) 196.
A. Ubaldini, C. Artini, G. A. Costa, M. M. Carnasciali and R. Masini, J. Therm. Anal. Cal., in press.
J. O. Sawyer, B. R. Hyde and L. Eyring, Inorg. Chem., 3 (1965) 426.
G. Brauer and E. Mohr-Rosenbaum, Z. Anorg. Allg. Chem., 394 (1972) 301.
K. Lohberg, Z. Phys. Chem., [B] 28 (1935) 402.
H. Bommer, Z. Anorg. Allg. Chem., 241 (1939) 273.
A. Iandelli, Gazz. Chim. Ital., 77 (1947) 312.
C. Boulesteix, Handbook of Physics and Chemistry of Rare Earths, K. A. Gschneidner and L. Eyring, Eds, North Holland 1982, Vol. 5, p. 321.
J. Felsche, Naturwissenschaften, 4 (1969) 212.
P. P. Fedorov, M. V. Nazarkin and R.M. Zakalyukin, Crystallography Reports, 47 (2002) 316.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Costa, G.A., Artini, C., Ubaldini, A. et al. Phase stability study of the pseudobinary system Gd2O3-Nd2O3 (T≙1350°C). J Therm Anal Calorim 92, 101–104 (2008). https://doi.org/10.1007/s10973-007-8744-x
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10973-007-8744-x