Isothermal crystallisation kinetics of poly(3-hydroxybutyrate) using step-scan DSC

Abstract

The crystallisation kinetics, melting behaviour and morphology, of bacterial poly(3-hydoxybutyrate) (PHB) have been investigated by using differential scanning calorimetry (DSC), step-scan DSC (SDSC), wide angle X-ray diffraction (WAXRD) and hot stage polarised optical microscopy (HSPOM). DSC imparted isothermal crystallisation thermal history. The subsequent melting behaviour revealed that all PHB materials experienced secondary crystallisation during heating and the extent of secondary crystallisation varied depending on the crystallisation temperature. PHB samples were found to exhibit double melting behaviour due to melting of SDSC scan-induced secondary crystals, while considerable secondary crystallisation or annealing took place under the modulated heating conditions. The overall melting behaviour was rationalised in terms of recrystallisation and/or annealing of crystals. Interestingly, the PHB materials analysed by SDSC showed a broad exotherm before the melting peak in the non-reversing curve and a multiple melting peak reversing curve, verifying that the melting-recrystallisation and remelting process was operative. HSOM studies supported the conclusions from DSC that the radial growth rate of the PHB spherulites was significantly varied upon the crystallisation conditions. One form of crystals was shown by WAXRD from isothermally crystallised PHB.