Abstract
ZnO nanofibers were prepared from zinc acetate/polyvinyl alcohol (PVA) by electrospun method. The morphological features, crystallinity, mechanical and optical properties of the ZnO nanofibers were studied. The results show the specific surface area of the ZnO nanofibers was influenced by the electrospun conditions. The specific surface area reached 389.7 m2g−1 as the average diameter was 232 nm. The XRD date reveals the nanofibers consist of a single phase of well-crystallized ZnO with hexagonal structure. The elastic modulus of a single ZnO nanofiber was also characterized by nano-scale three-point bending test.
Similar content being viewed by others
References
Chou TP, Zhang QF, Fryxell GE, Cao GZ (2007) Adv Mater 19:2588–2592. doi:10.1002/adma.200602927
Yu WD, Li XM, Gao XD (2005) Cryst Growth Des 5(1):151–155. doi:10.1021/cg049973r
Gao T, Li QH, Wang TH (2005) Chem Mater 17:887–892. doi:10.1021/cm0485456
Gorla CR, Emanetoglu NW, Liang S, Mayo WE, Lu Y, Wraback M, Shen H (1999) J Appl Phys 85:2595–2602. doi:10.1063/1.369577
Ding Y, Zhang P, Long Z, Jiang Y, Xu F, Lei J (2008) J Sol-Gel Sci Technol 46:176–179. doi:10.1007/s10971-008-1683-6
Azad AM (2006) Mater Sci Eng A A 435–436:468–473. doi:10.1016/j.msea.2006.07.075
Yuh J, Nino JC, Sigmund M (2005) Mater Lett 59:3645–3647. doi:10.1016/j.matlet.2005.07.008
Dharmaraj N, Park H, Kim C, Kim H, Lee D (2004) Mater Chem Phys 87:5–9. doi:10.1016/j.matchemphys.2004.05.005
Kameoka J, Verbridge S, Liu H, Czaplewski D, Craighead H (2004) Nano Lett 4:2105–2108. doi:10.1021/nl048840p
Shen Z, Thompson B, Mchugh M (2006) Macromolecules 39:8553–8555. doi:10.1021/ma062155i
Wu J, Coffer J (2007) J Phys Chem C 111:16088–16091. doi:10.1021/jp076338y
Schiffman J, Schauer C (2007) Biomacromolecules 8:2665–2667. doi:10.1021/bm7006983
Periasamy V, Narayan B, Hak-Yong K, Douk-Rae L (2004) Nanotechnology 15:320–323. doi:10.1088/0957-4484/15/3/015
Il-Doo K, Jae-Min H, Byong Hong L, Dong Young K, Eun-Kyung J, Duck-Kyun C, Dae-Jin Y (2007) Appl Phys Lett 91:163109. doi:10.1063/1.2799581
Yang X, Shao C, Guan H, Li X, Gong J (2004) Inorg Chem Commun 7:176. doi:10.1016/j.inoche.2003.10.035
Ding Y, Zhang P, Long Z, Jiang Y, Huang J, Yan W, Liu G (2008) Mater Lett 62:3410–3412. doi:10.1016/j.matlet.2008.03.033
Ding Y, Zhang P, Long Z, Jiang Y, Yin J, Xu F, Zuo Y (2009) J Alloy Comp 474:223–225. doi:10.1016/j.jallcom.2008.06.068
Hari SN (2004) Dekker Encyclopedia of Nanoscience and Nanotechnology. American Scientific, California
Acknowledgments
The financial support from the Scientific Research Foundation of Hunan Provincial Education Department (No: 07A071, 08C892, 08C893), the Scientific Research Foundation of Xiangtan University (No: 08XZX28), and Undergraduate Innovation Foundation of Education Ministry of China (No: 081053019) is greatly acknowledged.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Ren, H., Ding, Y., Jiang, Y. et al. Synthesis and properties of ZnO nanofibers prepared by electrospinning. J Sol-Gel Sci Technol 52, 287–290 (2009). https://doi.org/10.1007/s10971-009-2030-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10971-009-2030-2