Abstract
TiO2 nanofibers were prepared from tetrabutyl titanate sol precursors by using electrospun method. X-ray diffraction (XRD) and atomic force microscope (AFM) were used to characterize their crystal structure and morphology feature. The results demonstrated that TiO2 nanofibers possessed anatase phase and the average diameter of TiO2 nanofibers was about 150 nm. The photocatalytic property of TiO2 nanofibers was evaluated for the photodecomposition of methyl orange solution. And TiO2 nanofibers exhibited high photocatalytic activities with transfer efficiency about 100% after 20 min.
Similar content being viewed by others
References
Trung T, Cho W-J, Ha C-S (2003) Mater Lett 57:2746
Sugimoto T, Zhou X, Muramatsu A (2002) J Colloid Interface Sci 252:339
Arnal P, Corriu RJP, Leclercq D et al (1997) Chem Mater 9:694
Nian J-N, Teng H (2006) J Phys Chem B 110:4193
Kim DH, Hong HS, Kim SJ et al (2004) J Alloys Compd 375:259
Choi SW, Jo SM, Lee WS et al (2003) Adv Mater 15(23):2027
Kim JR, Choi SW, Jo SM et al (2004) Electrochim Acta 50:69
Kim JR, Choi SW, Jo SM et al (2005) J Electrochem Soc 152(2):A295
Choi SW, Kim JR, Jo SM et al (2005) J Electrochem Soc 152(5):A989
Azad AM (2006) J Mater Sci Eng A 435–436:468
Fu Z, Ma J, Qin Q (2005) Solid State Ionics 176:1635
Madhugiri S, Zhou W, Ferraris JP et al (2003) Microporous Mesoporous Mater 63:75
Li D, Xia YN (2004) Nano lett 4:933
Jiang Y, Zhang P, Liu Z et al (2006) Mater Chem Phys 99:498
Acknowledgments
This work was performed by the financial support of Natural Science Foundation of China (No. 10672138), Department of Science and Technology of Hunan Province of China (No. 03JZY1002) and Department of Education of Hunan Province of China (No. 07A071).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Ding, Y., Zhang, P., Long, Z. et al. Fabrication and photocatalytic property of TiO2 nanofibers. J Sol-Gel Sci Technol 46, 176–179 (2008). https://doi.org/10.1007/s10971-008-1683-6
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10971-008-1683-6