Abstract
Acrylic resin/nano-SiO2 (AR/nano-SiO2) composite was prepared by physical blends of acrylic resin (AR) and nano-SiO2, which was synthesized via the sol-gel method of tetraethoxysilane (TEOS) catalyzed with alkali. The synthetic conditions, such as surfactant type, the content of nano-SiO2 sol, stirring speed, mixed temperature and ultrasonic treatment, on nanocomposites’ property were studied in detail. DSC indicated the glass transition temperature of AR/nano-SiO2 (Tg = −26.7°C) was a little higher than that of the acrylic resin (Tg= −29.6°C). Water uptake confirmed that the water resistance of AR/nano-SiO2 was improved by 55.94% and the solvent resistance by 54.79% when compared with AR. The improved properties of leather finished by AR/nano-SiO2 were shown, in contrast to AR treatment; water vapor permeability was increased by 9.15% and the finish adhesion by 10.35%.
Similar content being viewed by others
Reference
Zhang Z-K, Cui Z-L (2001) Nanotechnology and nanomaterials. National Defence Industry Press, Beijing
Li L, Xiang H (2002) Functional materials and nanomaterials. Chemical Industry Press, 7, Beijing
Xu G-C, Xing H-L, Min F-F (1999) Application of nano-SiO2 in violet outer solidified coating. Paint Coat Ind 3(7)
Zuo M-X, Ma Q-L, Huang J-J (1998) Multicolor rubber goods modified by nano-SiO2. New Chem Mater 27(4):18
Christine R, Hefetz M (1998) Fabrication of dense nanocrystalline ZrO2-3 mol% Y2O3 by hot-isostatic pressing. J Mater Res 13(7):24
Liu J-C, Han J-C (1998) Nano-SiO2 of nanomaterials in advanced science and technology. Paint Coat Ind (1):34
Bruce MN (1993) Hybrid nanocomposite materials-between inorganic glasses and organic polymers. Adv Mater 5(6):422
Xu G-C, Zhang L-D (2002) Nanocomposites. Chemical Industry Press, Beijing
Zhang L-D, Moji Mei (2001) Nanomaterials and nanostructure. Science Press, Beijing
Cao Z-Y (2000) Chemical application and exploitation of nanomaterials. New Chem Mater 28(11):30
Ma J-Z, Liu L-Y, Zhang Z-J (2004) Study on acrylic resin modified by nano-SiO2. China Leather 33(9):31
Ma J-Z, Zhang Z-J, Liu L-Y et al (2005) Application of leather finishing agent synthesized by acrylic-resin and nano-SiO2 derived from acidic sol-gel. China Leather 34(19):23
Jiang W-Q (1999) Physical and chemical Analysis of leather. China Light Industry Press
Acknowledgment
This investigation was supported by National Natural Science Foundation of China (No.: 20674047), Ministry of Education New Century Excellent Talents Foundation of China (Item No.: NCET-04-0973), Shaanxi Province Natural Science Foundation (Item No.: 2004E114) and the Team Work Project of Science Innovation of Shannxi University of Science and Technology (Item No.: SUST-A03).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Ma, J.Z., Hu, J., Yang, Z.S. et al. Preparation of acrylic resin/modified nano-SiO2 via sol-gel method for leather finishing agent. J Sol-Gel Sci Technol 41, 209–216 (2007). https://doi.org/10.1007/s10971-006-1506-6
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10971-006-1506-6