Abstract
A simple approach namely sol-coated technique has been developed for the low cost fabrication of macroporous ceramic under a far below common sintering temperature of alumina with large dimension grains. The prepared green support shows higher sinteractive than the one treated by wet impregnation method under the same sintering conditions. The support possesses great potential applications with 6.63–7.71 μm in pore size, 39% open porosity as well as >45 MPa mechanical strength at the sintering temperature range of 1350°– 1500°C. The results indicate that the nitrogen gas flux and pure water permeation value was 51 252.35 m3 m−2 h−1 bar−1, 98.43 m3 m−2 h−1 bar−1, respectively, which were more dependent on the pore structure and pore size distribution than open porosity.
Similar content being viewed by others
References
Burggraaf A-J, Cot L (eds) (1996) Fundamentals of inorganic membrane science and technology. Elsevier, Amsterdam
Kima K-H, Choa S-J, Yoon K-J, et al (2002) J Membr Sci 199:69
Ayral A (2004) In: Akin FT, Lin YS (eds) Proceedings of the Eighth International Conferences on Inorganic Membranes (ICIM 8th-2004), Cincinnati, Ohio, USA
Nijmeijer A, Huiskes C, Sibelt NGM, Kruidhof H, Verwei H (1998) J Am Ceram Soc Bull 77:95
Lee S-H, Chung K-C, Shin M-C, Dong J-I, Lee H-S, Auh KH (2002) Mater Lett 52:266
Cosentino IC, Muccillo ENS, Muccillo R, Vichi FM (2006) J Sol-Gel Sci Tech 37:31
Shqau K, Mottern ML, Yu D, Verweijw H (2006) J Am Ceram Soc 89(6):1790
Lu J, Gao L, Gui L, Guo J (2001) Mater Chem Phys 72:352
Gu HM, Shih WY, Shih WH (2005) J Am Ceram Soc 88(6):1435
Zhang J-X, Gao L-Q (2001) Ceram Inter 27:143
Prabhakaran K, James J, Pavithran C (2003) J Eur Ceram Soc 23:379
Ananthakumar S, Raja V, Warrier KGK (2000) Mater Lett 43:174
Ananthakumar S, Menon ARR, Prabhakaran K, Warrier KGK (2001) Ceram Inter 27:231
Livage J, Henry M, Sanchez C (1988) Progr Solid State Chem 18:259
Sathiyakumar M, Gnanam FD (2002) Ceram Inter 28:195
Erkalfa H, Misirli Z, Baykara T (1998) Ceram Inter 24:81
Yang J, Ferreira JMF (1998) Mater Lett 36:320
De Arenas IB, Gil O (2003) J Mater Process Tech 143–144:838
Khan MI, Tabussum S (2004) Inorg Chem 43:5850
Jung M (2001) Inter J Inorg Mater 3:471
Sivakumar S, Pillai PK et al. (2002) Mater Lett 57:330
Iwamoto SI, Iwamoto S, Inoue M (2005) Chem Mater 17:650
Huang YH, Senos AMR, Baptista JL (1997) J Eur Ceram Soc 17:1239
Shojai F, Ä TAM, Ä Ntyl (2001) J Mater Sci 36:3437
Liu Y, Liu X, Li G, Meng GY (2001) J Mater Sci 36:3687
Uhlhorn RJ, Huis MHBJ, In'Tveld , Keizer K, Burggraaf AJ (1992) J Mater Sci 27:527
Falamaki C, Afarani MS, Aghaie A (2004) J Eur Ceram Soc 24:2285
Acknowledgment
This work was supported by the Natural Science Foundation of China (contract No. 20271047) and the Ministry of Science and Technology of China (contract No. 2003CB615700).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Wang, Y.H., Zhang, Y., Liu, X.Q. et al. Sol-coated preparation and characterization of macroporous α-Al2O3 membrane support. J Sol-Gel Sci Technol 41, 267–275 (2007). https://doi.org/10.1007/s10971-006-1504-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10971-006-1504-8