Neutron activation analysis for chromium(III) and (VI) in lixiviated liquid through a calcined chromium(VI) adsorbed hydrotalcite

Summary

Electrophoresis followed by neutron activation analysis was utilized to determine chromium(III) and (VI) in mixed solutions. These solutions proceeded from Cr(VI) adsorbed hydrotalcites heated at 800 °C to partially immobilize Cr in the Mg-Al oxide solid solution. Immobilization was studied by Cr lixiviation with NaCl solutions through the heated hydrotalcites. The results have shown that Cr lixiviated was in the form of CrO₄^2- ions, mainly because some Cr(VI) was not completely reduced to Cr(III) during heating. Chromium lixiviated from HT-Cr sample, heated at 800 °C and γ-irradiated at 1000 kGys, was found, as well, in the form of CrO₄^2- ions. Although γ-irradiation increases Cr immobilization in the solid, it does not reduce completely all CrO₄^2- ions present in the solid and, therefore, some Cr is lixiviated through the solid in the form of CrO₄^2- ion.