Improved Superconducting Properties of Thick YBa2Cu3O7−δ Film by Adding Amino-Rich Polyethyleneimine in Precursor Solution

  • Jing Wang
  • Xiuping Yin
  • Yue-Ling Bai
  • Wei Du
  • Jianhui Fang
  • Zhi-Yong Liu
  • Yanqun Guo
  • Chuanbing Cai
Original Paper
  • 36 Downloads

Abstract

Polyethyleneimine (PEI) with an amount of –NH2 groups used in precursor solution could effectively reduce Cu2+ volatilization during the pyrolysis process. Thermogravimetric analysis shows that the temperature window of low-temperature pyrolysis for precursor solution with PEI (PEI-YBCO) is widened significantly. The slower pyrolysis process can enrich Cu2+ and improve critical current density (Jc) of PEI-YBCO films. The highest Jc is 3.03 MA/cm2 at 77 K when the amount of PEI is 0.5 g/10 mL and the film thickness is 400 nm. Then the thickness increases from 0.4 to 2.0 μm by changing the coating times. The Jc values of PEI-YBCO films decrease gradually with the thickness increase. However, the critical current (Ic) can be up to 197 A/cm (at 77 K, self-field) and Jc can still keep 1.68 MA/cm2 at 1.2 μm.

Keywords

Polyethyleneimine Metalorganic deposition method Thick film 

Notes

Funding Information

This work was supported by the National Natural Science Foundation of China (21571126, 51572165, 11174193 and 51202141) the Shanghai Key Laboratory of High Temperature Superconductors (14DZ2260700) and the Science and Technology Commission of Shanghai Municipality (16521108400, 16DZ0504300 and 14521102800).

References

  1. 1.
    Foltyn, S., Civale, L., MacManus-Driscoll, J., Jia, Q., Maiorov, B., Wang, H., et al.: Materials science challenges for high-temperature superconducting wire. Nat. Mater. 6, 631–642 (2007)ADSCrossRefGoogle Scholar
  2. 2.
    Obradors, X., Puig, T.: Coated conductors for power applications: Materials challenges. Supercond. Sci. Technol. 27, 044003 (2014)ADSCrossRefGoogle Scholar
  3. 3.
    Chen, D.-X., Pardo, E., Sanchez, A., Bartolome, E., Puig, T., Obradors, X.: Magnetic properties of a melt-textured YBa2Cu3 O x ring with a perpendicular crack. Appl. Phys. Lett. 90, 072501 (2007)ADSCrossRefGoogle Scholar
  4. 4.
    Shiohara, Y., Taneda, T., Yoshizumi, M.: Overview of materials and power applications of coated conductors project. Jpn. J. Appl. Phys. 51, 010007 (2011)CrossRefGoogle Scholar
  5. 5.
    Palmer, X., Pop, C., Eloussifi, H., Villarejo, B., Roura, P., Farjas, J., et al.: Solution design for low-fluorine trifluoroacetate route to YBa2Cu3 O 7 films. Supercond. Sci. Technol. 29, 024002 (2015)ADSCrossRefGoogle Scholar
  6. 6.
    Nakaoka, K., Yoshizumi, M., Usui, Y., Izumi, T., Shiohara, Y.: Improvement of production rate of YBCO coated conductors fabricated by TFA-MOD method. Phys. Procedia 58, 134–137 (2014)ADSCrossRefGoogle Scholar
  7. 7.
    Maiorov, B., Baily, S., Zhou, H., Ugurlu, O., Kennison, J., Dowden, P., et al.: Synergetic combination of different types of defect to optimize pinning landscape using BaZrO3,-doped YBa2Cu3 O 7. Nat. Mater. 8, 398–404 (2009)ADSCrossRefGoogle Scholar
  8. 8.
    Foltyn, S., Wang, H., Civale, L., Jia, Q., Arendt, P., Maiorov, B., et al.: Overcoming the barrier to 1000 A/cm width superconducting coatings. Appl. Phys. Lett. 87, 162505 (2005)ADSCrossRefGoogle Scholar
  9. 9.
    Wuwei, Y., Chengxiao, Z., Guofang, Z., Lihua, J., Chengshan, L., Guo, Y., et al.: Preparation of YBCO superconducting film by chemical solution deposition using a novel copper precursor derived from PEG (200) and sucrose. Rare Metal Mater. Eng. 40, 346–349 (2011)Google Scholar
  10. 10.
    Xu, W.C., Bai, Y.L., Fang, J.H., Cai, C.B.: The effect of polyethyleneimine (PEI) on the texture and morphology of YBCO films. In: Advanced Materials Research, pp. 103–106 (2014)Google Scholar
  11. 11.
    Jia, QX, McCleskey, TM, Burrell, AK, et al.: Polymer-assisted deposition of metal-oxide films. Nat. Mater., 529–532 (2004)Google Scholar
  12. 12.
    Dawley, J., Clem, P., Boyle, T., Ottley, L., Overmyer, D., Siegal, M.: Rapid processing method for solution deposited YBa2Cu3 O 7−δ thin films. Physica C: Supercond. 402, 143–151 (2004)ADSCrossRefGoogle Scholar
  13. 13.
    Wang, W., Li, G., Pu, M., Sun, R., Zhou, H., Zhang, Y., et al.: Chemical solution deposition of YBCO thin film by different polymer additives. Physica C: Supercond. 468, 1563–1566 (2008)ADSCrossRefGoogle Scholar
  14. 14.
    Erbe, M., Hänisch, J., Freudenberg, T., Kirchner, A., Mönch, I., Kaskel, S., et al.: Improved REBa2Cu3 O 7−x(RE = Y, Gd) structure and superconducting properties by addition of acetylacetone in TFA-MOD precursor solutions. J. Mater. Chem. 2, 4932–4944 (2014)CrossRefGoogle Scholar
  15. 15.
    Chen, Y., Pan, B., Li, H., Zhang, W., Lv, L., Wu, J.: Selective removal of Cu(II) ions by using cation-exchange resin-supported polyethyleneimine (PEI) nanoclusters. Environ. Sci. Technol. 44, 3508–3513 (2010)ADSCrossRefGoogle Scholar
  16. 16.
    Lee, J.-W., Joo, Y.-S., Choi, S.-M., Yoo, S.-I.: Enhanced flux pinning properties of MODprocessed YBa2Cu3O7-delta thin films with BaZrO3 nanoparticles using a Ba-deficient coating solution. IEEE Trans. Appl. Supercond. 23, 4 (2013)CrossRefGoogle Scholar
  17. 17.
    An, F.-q., Gao, B.-j., Liu, Q.: Determining structure of chelate complex of polyethyleneimine with cupric ion and its analysis application. Chin. J. Anal. Labor. 25, 115 (2006)Google Scholar

Copyright information

© Springer Science+Business Media, LLC, part of Springer Nature 2018

Authors and Affiliations

  1. 1.Department of Chemistry, College of ScienceShanghai UniversityShanghaiChina
  2. 2.Shanghai Key Laboratory of High Temperature Superconductors, Department of Physics, College of ScienceShanghai UniversityShanghaiChina

Personalised recommendations