Peculiarities of Magnetic Behavior of CuO Nanoparticles Produced by Plasma-Arc Synthesis in a Wide Temperature Range


Copper oxide nanoparticles, produced by direct plasmochemical synthesis in a low-pressure arc discharge plasma, show a wide variety of magnetic properties depending on the strength of the external magnetic field and the temperature. At low strength of the field and throughout the studied temperature range, the ferromagnetic state dominates. This state is caused by disordering of the spins on the surface of the nanoparticles. At high strength of the field and under temperatures of less than 200 K, nanoparticles exhibit a paramagnetic state due to the spin-glass behavior of copper atoms. At high strength of the field (more than 3 kOe) and under temperatures of above 300 K, the diamagnetic state of nanoparticles is observed, due to local eddy currents caused by oxygen vacancies. The temperature of antiferromagnetic ordering under study is significantly lowered (down to ∼ 100 K).

This is a preview of subscription content, access via your institution.

Fig. 1
Fig. 2
Fig. 3


  1. Ushakov, A.V., Karpov, I.V., Lepeshev, A.A., Petrov, M.I.: J. Appl. Phys. 118, 023907 (2015).

    ADS  Article  Google Scholar 

  2. Ushakov, A.V., Karpov, I.V., Lepeshev, A.A., Petorv, M.I., Fedorov, L.Yu.: JETP Lett. 99, 99 (2014).

    ADS  Article  Google Scholar 

  3. Lepeshev, A.A., Ushakov, A.V., Karpov, I.V., Balaev, D.A., Krasikov, A.A., Dubrovskiy, A.A., Velikanov, D.A., Petrov, M.I.: J. Supercond. Nov. Magn. 30, 931 (2017).

    Article  Google Scholar 

  4. Karpov, I.V., Ushakov, A.V., Lepeshev, AA., Fedorov, Yu. L.: Tech. Phys. 62, 168 (2017).

    Article  Google Scholar 

  5. Ushakov, A.V., Karpov, I.V., Lepeshev, A.A., Petrov, M.I.: Vacuum 133, 25 (2016).

    ADS  Article  Google Scholar 

  6. Ushakov, A.V., Karpov, I.V., Lepeshev, A.A., Petrov, M.I., Fedorov, Yu. L.: Phys. Solid State 57, 919 (2015).

    ADS  Article  Google Scholar 

  7. Karpov, I.V., Ushakov, A.V., Fedorov, L. Yu., Lepeshev, A.A.: Tech. Phys. 84, 559 (2014).

    Article  Google Scholar 

  8. Dobretsov, K., Stolyar, S., Lopatin, A.: Acta Otorhinolaryngol. Ital. 35, 97 (2015)

    Google Scholar 

  9. Punnoose, A., Magnone, H., Seehra, M.S., Bonevich, J.: Phys. Rev. B 64, 174420 (2001).

    ADS  Article  Google Scholar 

  10. Zheng, X.G., Xu, C.N., Nishikubo, K., Nishiyama, K., Higemoto, W., Moon, W.J., Tanaka, E., Otabe, E.S.: Phys. Rev. B 72, 014464 (2005).

    ADS  Article  Google Scholar 

  11. Kumzerov, Yu. A., Kartenko, N.F., Parfen’eva, L.S., Smirnov, I.A., Sysoeva, A.A., Misiorek, H., Jezowski, A.: Phys. Solid State 54, 1066 (2012).

    ADS  Article  Google Scholar 

  12. Thota, S., Shim, J.H., Seehra, M.S.: J. Appl. Phys. 114, 214307 (2013).

    ADS  Article  Google Scholar 

  13. Arbuzova, T.I., Naumov, S.V., Samokhvalov, A.A., Gizhevskii, B.A., Arbuzov, V.L., Shal’nov, K.V.: Phys. Solid State 43, 878 (2001).

    ADS  Article  Google Scholar 

  14. Arbuzova, T.I., Naumov, S.V., Arbuzov, V.L., Shal’nov, K.V., Ermakov, A.E., Mysik, A.A.: Phys. Solid State 45, 304 (2003).

    ADS  Article  Google Scholar 

  15. Asharf Shah, M., Al-Ghamdi, M.S.: Mater. Sci. Appl. 2, 977 (2011).

    Google Scholar 

  16. L. Néel: CR Acad. Sci. Paris 252, 4075 (1961)

    Google Scholar 

  17. Kondo, O., Ono, M., Sugiura, E., Sugiyama, K., Date, M.: J. Phys. Soc. Jpn. 57, 3293 (1988).

    ADS  Article  Google Scholar 

Download references


This study was supported by the Russian Science Foundation (Project No 16-19-10054).

Author information

Authors and Affiliations


Corresponding author

Correspondence to A. A. Lepeshev.

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Ushakov, A.V., Karpov, I.V. & Lepeshev, A.A. Peculiarities of Magnetic Behavior of CuO Nanoparticles Produced by Plasma-Arc Synthesis in a Wide Temperature Range. J Supercond Nov Magn 30, 3351–3354 (2017).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:


  • CuO nanoparticles
  • Vacuum arc
  • Ferromagnetism
  • Diamagnetism