Abstract
We report the synthesis of under-doped non-superconducting parent compound of iron chalcogenide, i.e, FeTe 1−xSe x (x =0.0, 0.01, 0.03, 0.05) single crystals by flux-free method. These FeTe 1−xSe x (x =0.0, 0.01, 0.03, 0.05) single crystals are crystallized in the tetragonal structure with space group P4/nmm at room temperature. Detailed scanning electron microscopy (SEM) results showed that the crystals are formed in slab-like morphology structure. Powder X-ray diffraction (XRD) results show that (0 0 l) peaks are shifted towards higher angel with increasing Se concentration. Coupled magnetic and structural phase transition temperature, being seen as a step in resistivity, decreases from around 67K for x =0.0 to 55K for x =0.05 crystal. Further, the step in resistivity is seen to be hysteric (ΔT) in nature, i.e., different step temperatures in cooling and warming cycles. Interestingly, the hysteric (ΔT) becomes narrower from around 5.8 K for x =0.0 to 0.95 K for x = 0.05 crystal.
References
Kamihara, Y., Watanabe, T., Hirano, M., Hosono, H.: J. Am. Chem. Soc 130, 3296 (2008)
Ren, Z.-A., Lu, W., Yang, J., Yi, W., Shen, X.-L., Li, Z.-C., Che, G.-C., Dong, X.-L., Sun, L.-L., Zhou, F., Zhao, Z.-X.: Chin. Phys. Lett. 25, 2215 (2008)
Chen, X. H., Wu, T., Wu, G., Liu, R. H., Chen, H., Fang, D. F.: Nature 453, 761 (2008)
Chen, G. F., Li, Z., Wu, D., Li, G., Hu, W. Z., Dong, J., Zheng, P., Luo, J. L., Wang, N. L.: Phys. Rev. Lett. 100, 247002 (2008)
Chen, G.F., Chen, Z.G., Dong, J., Hu, W.Z., Li, G., Zhang, X.D., Zheng, P., Luo, J.L., Wang, N.L.: Phys. Rev. B. 79, 140509(R) (2009)
Maheshwari, P. K., Jha, R., Gahetori, B., Awana, V. P. S.: J. Supecond. & Novel Mag. 28, L2893–2897 (2015)
Maheshwari, P.K., Rajveer, J., Gahtori, B., Awana, V.P.S.: AIP Advances 5, 097112–10 (2015)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Maheshwari, P.K., Jha, R., Gahtori, B. et al. Structural and Transport Studies of Under-Doped FeTe 1 − x Se x (x =0.0, 0.01, 0.03, 0.05) Single Crystals. J Supercond Nov Magn 29, 543–545 (2016). https://doi.org/10.1007/s10948-016-3403-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10948-016-3403-8