Abstract
The effect of YBCO adding on the superconducting of BPSCCO system with nominal starting composition of (Bi1.6Pb0.4Sr2Ca2Cu3O δ )1−x(YBCO) x with x = 0.00−0.10 was studied. The preparation methods used to prepare the samples are the conventional solid-state techniques. From the XRD data, it is observed that the percentage of the Bi-2223 phase increases and Bi-2212 decreases for addition x = 0.02–0.04, respectively. The effect of YBCO addition on the BPSCCO system also has been investigated in term of AC susceptibility study. We have studied the various applied field dependence of the AC susceptibility in polycrystalline samples. The AC susceptibility measurements in the range 0.05 to 2.00 Oe show that as the applied fields increases, the intergranular AC loss peaks move to lower temperature, and also height decreases and width increases. The effect of YBCO addition for the intergranular critical current J cm, and the presence of weak links that coupled the superconducting grains were defined.
Similar content being viewed by others
References
Lau, K.T., Chen, S.K., Abd-Shukor, R.: Physica C 377, 547–552 (2002)
Celebi, S., Malik, A.I., Inanir, F., Halim, S.A.: J. Alloys Compd. 370, 69–74 (2004)
Azhan, H., Halim, S.A., Nazree, A., Azman, K., Syamsyir, S.A.: Adv. Mater. Res. 895, 99–104 (2014)
Yildirim, G., Zalaoglu, Y., Akdogan, M., Altintas, S.P., Varilci, A., Terzioglu, C.: J. Supercond. Nov. Magn. doi:10.1007/s10948-011-11174-9 (2011)
Hein, R.A.: Phys. Rev. B 33, 7539 (1986)
Chen, D.X., Nogues, J., Roa, K.V.: Cryogenics 29, 800 (1989)
Gomory, F., Lobotka, P.: Solid State Commun. 66, 645 (1988)
Bean, C.P.: Rev. Mod. Phys. 36, 31 (1964)
Goldfarb, R.B., Leirental, M., Thomson, C.A. In: Hein, R.A., Francavilla, T.L., Leinbenberg, D.H. (eds.): Book Magnetic susceptibility of superconductor and other spin system, pp 49–81, Plenum, New York (1991)
Kong, W., Abd-Shukor, R.: J. Supercond. Nov. Magn. 23, 257 (2010)
Celebi, S., Karaca, I., Aksu, E., Grenser, A.: Physica C 307, 131 (1998)
Abou-Aly, A.I., Gawad, M.M.H.A., Awad, R., G-Eldeen, I.: J. Supercond. Nov. Magn. doi:10.1007/s10948-0111-1171-z (2011)
Annabi, M., M’Chirgui, A., Azzouz, F.B., Zouaoui, M., Salem, M.B.: Physica C 25, 405 (2004)
Kong, W., Abd-Shukor, R.: Solid State Sci. Technol. 1, 15 (2007)
Huang, W.H., Song, Z., Cui, B., Zhao, M.H., Pu, X.C., Wu, Y., Sun, P., Du, J.J.: Phys. Status Solidi. 179, 189 (2000)
Halim, S.A., Khawaldeh, S.A., Mohamed, S.B., Azhan, H.: Mater. Chem. Phys. 61, 251–259 (1999)
Acknowledgments
The authors of the present study wish to express their thanks to the Superconductivity and Thin Film Laboratory, Department of Physics, Universiti Putra Malaysia for aiding with the experimental procedures and the University Malaysia Kelantan for the financial support under the study leave scheme
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Arlina, A., Halim, S.A., Awang Kechik, M.M. et al. AC Losses in YBCO-Added Bi1.6Pb0.4Sr2Ca2Cu3O δ Superconductors. J Supercond Nov Magn 28, 1953–1958 (2015). https://doi.org/10.1007/s10948-014-2936-y
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10948-014-2936-y