Abstract
Electrodeposited thick films of FePt (with the nominal composition 50 % Fe/50 % Pt) on three metallic (Au, Ag, Au) underlayers were annealed at various temperatures. The magnetic and morphological properties of the resulting films were then monitored. The Au and Ag underlayers promoted the growth of the (bct) L10 FePt phase. The greater growth of this phase in the films deposited on the Ag underlayer led to the crystallographic texturing in the (001) direction. This was accompanied by a significant magnetic anisotropy and a negative shift of the remanent magnetization in the presence of an applied field. The coercivity of the Ag underlayer films increased to 18 kOe while the coercivity of the Au underlayer films decreased to ∼2 kOe when the annealing temperature was increased to 800 ∘C.
Similar content being viewed by others
References
Baibich, M.N., Broto, J.M., Fert, A.: Giant magnetoresistance of (001)Fe/(001)Cr magnetic superlattices. Phys. Rev. Lett. 61, 2472–2475 (1988)
Binasch, G., Grünberg, P., Saurenbach, F., Zin, W.: Field-induced nonequilibrium periodic structures in nematic liquid crystals: nonlinear study of the twist Frederiks transition. Phys. Rev. A 39, 4828–4834 (1989)
Cao, G.Z., Wang, Y.: Nanostructures and Nanomaterials. Imperial College Press, London (2004)
Gutfleisch, O., Lyubina, J., Müller, K.H., Schultz, L.: FePt hard magnets. Adv. Eng. Mater. 7, 208–212 (2005)
Maeda, T., Kai, T., Kikitsu, A., Akiyame, J.I.: Reduction of ordering temperature of an FePt-ordered alloy by addition of Cu. Appl. Phys. Lett. 80, 2147–2149 (2002)
Inoue, S., Namazu, T., Inoue, K.: Mater. Res. Soc. Symp. Proc. 426, 2213 (2003)
Zhao, Z.L., Ding, J., Inaba, K., Chen, J.S., Wang, J.P.: Promotion of L10 ordered phase transformation by the Ag top layer on FePt thin films. Appl. Phys. Lett. 83, 2196–2198 (2003)
Rhen Fernando, M.F., Hinds, G., O’Reilly, C., Coey, J.M.D.: Electrodeposited FePt films. IEEE Trans. Magn. 39, 2699–2701 (2003)
Leistner, K., Thomas, J., Schlörb, H., Weisheit, M., Schultz, L., Fähler, S.: Highly coercive electrodeposited FePt films by postannealing in hydrogen. Appl. Phys. Lett. 85, 3498–3500 (2004)
Thongmee, S., Ding, J., Lin, J.Y., Blackwood, D.J., Yi, J.B., Yin, J.H.: FePt films fabricated by electrodeposition. J. Appl. Phys. 101, 09K519–09K519-3 (2007)
Ristau, R.A., Barmak, K., Lewis, L.H., Colley, K.R., Howard, J.K.: On the relationship of high coercivity and L10 ordered phase in CoPt and FePt thin films. J. Appl. Phys. 86, 4527–4533 (1999)
Skomski, R., Sellmyer, D.J.: Cooperative magnetism and the Preisach model. J. Appl. Phys. 89, 7263–7265 (2001)
Zhao, Z.L., Chen, J.S., Ding, J., Yi, J.B., Liu, B.H., Wang, J.P.: Fabrication and microstructure of high coercivity FePt thin films at 400 ∘C. Appl. Phys. Lett. 88, 052503 (2006)
Acknowledgements
The authors would like to thank Prof. Ding Jun and Dr. Yi Jiabao for their help and discussions in this work.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Thongmee, S., Tang, I.M. Magnetic and Morphological Properties of Electrodeposited Thick FePt Films on Metallic (Au, Ag, Cu) Underlayers. J Supercond Nov Magn 26, 3263–3269 (2013). https://doi.org/10.1007/s10948-013-2137-0
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10948-013-2137-0