Fabrication and Characterization of Poly(lactic acid) Biocomposites Reinforced by Calcium Sulfate Whisker
- 92 Downloads
The biodegradable poly(lactic acid) (PLA) composites filled with calcium sulfate whisker (CSW) were fabricated via melt-blending and subsequent injection molding. Surface organification of γ-aminopropyltriethoxysilane (APTES) on CSW was applied to accelerate the wettability of PLA to CSW. The mechanical properties, morphological structures, crystallization behaviors and thermal stabilities of PLA/CSW composites were investigated in detail. Results showed that modification of APTES changed the surface morphologies and element compositions, helping to form the well bonded interfaces. By adding CSW, the elastic modulus of PLA/CSW composites presented a sustained increment, while tensile strength, elongation at break and impact toughness were increased first and then decreased. The presence of CSW impeded the melt-crystallization but accelerated the cold-crystallization process. On the whole, the actual crystallinity for the composites was suppressed except for the case with 20% CSW. The thermal stability was enhanced by CSW as expected, and all the samples showed the exact same reaction order (n = 1) according to Carrasco method. Nevertheless, the activation energies were declined, indicating CSW was in favor of thermal decomposition of PLA phases. Finally, it was interestingly found that CSW could improve the comprehensive properties of PLA without deteriorating the processibility.
KeywordsPoly(lactic acid) Crystallization Thermal property Kinetic analysis Processibility
This work was supported by the National Natural Science fund of China (Nos. 51775001 and 51303004), the Anhui Province Post Doctoral Researchers in Scientific Research Projects (No. 2014B006) and the Pre-research Project on Natural (Social) Science Fund of Anhui University of Science and Technology (No. 2016yz003).
- 15.Yang JN, Nie SB, Zhu JB (2016) A comparative study on different rubbery modifiers: effect on morphologies, mechanical, and thermal properties of PLA blends. J Appl Polym Sci 133:43340Google Scholar
- 29.Wang JC, Tang LJ, Wu D, Guo X, Hao WL (2012) Application of modified calcium sulfate whisker in methyl vinyl silicone rubber composites. Polym Polym Compos 20:453–461Google Scholar
- 30.Zhou J (2010) Property and microstructure of ABS composite modified with salt sulfate whisker. CIESC J 61:243–248 (in Chinese)Google Scholar
- 31.Chen RY, Zou W, Wu CR, Jia SK, Huang Z, Zhang GZ, Yang ZT, Qu JP (2014) Poly(lactic acid)/poly(butylene succinate)/calcium sulfate whiskers biodegradable blends prepared by vane extruder: analysis of mechanical properties, morphology, and crystallization behavior. Polym Test 34:1–9CrossRefGoogle Scholar
- 34.Wei ZY, Zhang WX, Chen GY, Liang JC (2011) Nonisothermal crystallization kinetics and melting behavior of isotactic polypropylene/calcium sulfate whisker composites. Polym Mater Sci Eng 27:66–69 (in Chinese)Google Scholar
- 35.Hu XL, Yu MF (2006) Study of calcium sulphate whiskers modified bismaleimide resin by friction and wear properties. Acta Polym Sin 5:686–691Google Scholar
- 53.Wang G, Li AM, Jiang RX (2010) Application of peak property method in research of polylactic acid pyrolysis properties. Acta Energiae Solaris Sinica 31:497–500 (in Chinese)Google Scholar