Abstract
With an industrial trend of going green, the use of natural fibers in polymer composites is growing rapidly, especially in the automotive industry. The objectives of this research are to investigate mechanical performance of kenaf/polypropylene nonwoven composites (KPNCs) in production of automotive interior parts, and to develop preliminary linear models for quantifying elastic range of the KPNCs under various loading conditions. Using polypropylene (PP) fiber as bonding fiber, the KPNCs were fabricated with 50/50 blend ratio by weight. Unlike the manufacturing method of fiber reinforced plastics, all KPNCs were produced by carding and needle-punching techniques and thermally bonded by a panel press with 3-mm thickness gauge. Mechanical properties of the KPNCs in terms of uniaxial tensile, open-hole tensile, tensile at different strain rates, flexural, and in-plane shear were measured instrumentally. It was found that sample which was processed at higher temperature (230 °C) but shorter time (60 s) had the best mechanical performance. KPNCs were relatively insensitive to the notch but sensitive to strain rates. The linear elastic finite element model of KPNCs agreed well with the experimental results in the valid strain range of 0–0.5 % for uniaxial tensile test and 0–1 % for flexural test.
Similar content being viewed by others
References
Hao A, Geng Y, Xu Q, Lu Z, Yu L (2008) J Appl Polym Sci 109:2679
Jiang W, Sun L, Hao A, Chen JY (2011) Text Res J 81:1949
Hao A, Jiang W, Chen J (2010) In: Liu F (ed), Proceedings of international symposium on renewable feedstock for biofuel and bio-based products. Austin, TX
Singh BP (ed) (2010) Industrial crops and uses, bast fibers: from plants to products. CABI
Sherman LM (1999) Plast Technol 45:62
Sydenstricker THD, Mochnaz S, Amico SC (2003) Polym Test J 22:375
Nair KCM, Diwan SM, Thomas S (1996) J Appl Polym Sci 60:1483
Chapman RA (ed) (2010) Applications of nonwovens on technical textiles, nonwoven textiles in automotive interiors. CRC Press LLC, Boca Raton
Wang Y (1999) Appl Compos Mater 6:19
Song F, Zhao H, Hu G (2012) Comput Mater Sci 51:353
Wang Y, Li J (1995) J Adv Mater 26:28
Davoodi MM, Sapuan SM, Ahmad D, Ali A, Khalina A, Jonoobi M (2010) Mater Des 31:4927
Shinji O (2008) Mech Mater 40:446
Shibata S, Cao Y, Fukumoto I (2008) Compos A Appl Sci Manuf 39:640
Hao A, Zhao H, Jiang W, Chen JY (2012) Proceedings of 56th society for advancement of material and process engineering (SAMPE) symposium and exhibition. Baltimore, MD
Chen Y, Chiparus O, Sun L, Negulescu I, Parikh DV, Calamari TA (2005) J Ind Text 35:47
Chen Y, Sun L, Negulescu I, Wu Q, Henderson G (2007) J Ind Hemp 12:27
Chen Y, Sun LF, Chiparus O, Negulescu I, Yachmenev V, Warnock M (2005) J Polym Environ 13:107
Hao A, Sun B, Qiu Y, Gu B (2008) Compos A Appl Sci Manuf 39:1073
Shahkarami A, Vaziri R (2007) Int J Impact Eng 34:104
Hou X, Acar M, Silberschmidt VV (2009) Comput Mater Sci 46:700
Bais-Singh S, Biggers SB, Goswami BC (1998) Text Res J 68:327
Liao T, Adanur S (1999) Text Res J 69:489
Mueller DH, Kochmann M (2004) Int Nonwovens J 13:56
Acknowledgments
The authors would like to thank Mr. Gregory L. Thompson, Department of Geological Sciences, Jackson School of Geosciences at University of Texas, Austin for the preparation of 150 μm KPNC slides. Thanks are also extended to Mr. Yizhuo Chen, Department of Textile and Apparel, School of Human Ecology at University of Texas, Austin for the help with nonwoven fabrication.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Hao, A., Zhao, H., Jiang, W. et al. Mechanical Properties of Kenaf/Polypropylene Nonwoven Composites. J Polym Environ 20, 959–966 (2012). https://doi.org/10.1007/s10924-012-0484-8
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10924-012-0484-8