Abstract
The aluminum-containing polycarbosilane (Al-PCS) with various quantities of aluminum was obtained by adding aluminium acetylacetonate (Al(AcAc)3) as an aluminum source to polysilacarbosilane (PSCS). Subsequently, thermal decomposition and condensation at various conditions were carried out. The molecular weight \( \left( {\overline{\text{Mn}} } \right),\,\overline{\text{Mn}} \) distribution, yield and softening point of the resulting Al-PCS differ with the Al(AcAc)3:PSCS weight ratio, the thermolysis temperature and the reaction time. The larger the Al(AcAc)3:PSCS weight ratio, the higher the thermolysis temperature and the longer the reaction time, the greater the \( \overline{\text{Mn}} , \) yield and softening point of Al-PCS. In addition, the oxygen and aluminum contents of Al-PCS increase at higher Al(AcAc)3:PSCS weight ratios. As the mixing weight ratio of Al(AcAc)3:PSCS increased, additional oxygen was introduced into Al-PCS with the increased Al content. The structure of Al-PCS was characterized by the FT-IR. These results show that Al-PCS is very similar to polycarbosilane in structure.
Similar content being viewed by others
References
S. Yajima, J. Hayashi, M. Omori, K. Okamura, Nature 261, 683 (1976)
R.M. Laine, F. Babonneau, Chem. Mater 5, 260 (1993)
M. Birot, J.-P. Pillot, J. Dunogues, Chem. Rev 95, 1443 (1995)
L.V. Interrante, W.R. Schmidt, P.S. Marchetti, G.E. Maciel, Mater. Res. Soc. Symp. Proc 271, 739 (1992)
H. Ichikawa, K. Okamura, T. Seguchi, in Proceedings of the Second International Conference on High-Temperature Ceramic-Matrix Composites II, The American Ceramic Society, Santa Barbara, USA, 1995, pp. 65–74
T. Ishikawa, S. Kajii, T. Hisayuki, K. Matsunaga, T. Hogami, Y. Kohtoku, in High Temperature Ceramic Matrix Composites III. ed by K. Niihara, K. Nakano, T. Sekino, E. Yasuda (Trans. Tech. Publications Ltd, USA, 1998), pp. 15–18
J. Lipowitz, J.A. Rabe, K.T. Nguyen, L.D. Orr, R.R. Androl, Ceram. Eng. Sci. Proc 16, 55 (1995)
F. Babonneau, G.D. Soraru, K.J. Thorne, J.D. Mackenzie, J. Am. Ceram. Soc 74, 1725 (1991)
G.D. Soraru, A. Ravagni, R. Campostrini, F. Babonneau, J. Am. Ceram. Soc 74, 2220 (1991)
T. Ishikawa, Y. Kohtoku, K. Kumagawa, T. Yamamura, T. Nagasawa, Nature 391, 773 (1998)
A.R. Bunsell, A. Plant, J. Mater. Sci 41, 823 (2006)
J.A. DiCarlo, H.M. Yun in Handbook of Ceramic Composites, ed by N.P. Bansal (Kluwer Academic Publishers, New York, 2005), pp. 33–52
Y. Hasegawa, C.X. Feng, Y.C. Song, Z.L. Tan, J. Mater. Sci 26, 3657 (1991)
C. Vahalas, M. Monthioux, J. Europ. Ceram. Soc 15, 445 (1995)
T. Ishikawa, Compos. Sci. Tech 51, 135 (1994)
M. Takeda, J. Sakamoto, Y. Imai, H. Ichikawa, Compos. Sci. Tech 59, 813 (1999)
M. Takeda, A. Urano, J. Sakamoto, Y. Imai, J. Nucl. Mater 258–263, 1594 (1998)
K. Kumagawa, H. Yamaoka, M. Shibuya, T. Yamamura, Ceram. Eng. Sci. Proc 19, 65 (1998)
T. Ishikawa, M. Sato, S. Kajii, Y. Tanaka, M. Suzuki, Ceram. Eng. Sci. Proc 22, 471 (2001)
S.M. Dong, G. Chollon, C. Labrugere, M. Lahaye, A. Guette, J.L. Bruneel, M. Couzi, R. Naslain, D.L. Jiang, J. Mater. Sci 36, 2371 (2001)
Y.X. Yu, X.D. Li, F. Cao, J. Mater. Sci 40, 2093 (2005)
K. Suzuki, K. Kumagawa, T. Kamiyama, M. Shibuya, J. Mater. Sci 37, 949 (2002)
Y.X. Yu, Y. Zhang, J.M. Yang, M. Tang, J. Inorg. Organometall. Polym 17, 569 (2007)
F. Cao, D.-P. Kim, X.D. Li, C.X. Feng, J. Appl. Polym. Sci 85, 2787 (2002)
Acknowledgment
This work was supported by the National Science Foundation for Post-doctoral Scientists of China (Grant No. 20060390704).
Author information
Authors and Affiliations
Corresponding authors
Rights and permissions
About this article
Cite this article
Yu, Y., Tang, X. Ceramic Precursor Aluminum-Containing Polycarbosilane: Preparation and Structure. J Inorg Organomet Polym 19, 389–394 (2009). https://doi.org/10.1007/s10904-009-9284-6
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10904-009-9284-6