Abstract
One objective of this work was to study the corrosion resistance of the new implant Ti–10Zr–5Ta–5Nb alloy in physiological fluids of different pH values, simulating the extreme functional conditions. Another objective was in vitro biocompatibility evaluation of the new alloy using human fetal osteoblast cell line hFOB 1.19. Cytocompatibility was assessed by determination of possible material cytotoxic effects, cell morphology and cell adhesion. The thermo-mechanical processing of the new implant alloy consisted in plastic deformation (almost 90%) performed by hot rolling accompanied by an initial and final heat treatment. The new Ti–10Zr–5Ta–5Nb alloy presented self-passivation, with a large passive potential range and low passive current densities, namely, a very good anticorrosive resistance in Ringer solution of acid, neutral and alkaline pH values. Cell viability was not affected by the alloy substrate presence and a very good compatibility was noticed.
Similar content being viewed by others
References
Thomsen P, Larsson C, Ericson LE, Sennerby L, Lausama J, Kasemo B. Structure of the interface between rabbit cortical bone and implants of gold, zirconium and titanium. J Mater Sci. 1997;8:653–65.
Kim H-K, Jang J-W. Surface modification of implant materials and its effect on attachment and proliferation of bone cells. J Mater Sci. 2004;15:825–30.
Anselme K, Bigerelle M, Noel B, Dufresne E, Judas D, Iost A, et al. Qualitative and quantitative study of human osteoblast adhesion on materials with various surface roughnesses. J Biomed Mater Res. 2000;49:155–66.
Briem D, Strametz S, Schroder K, Meenen NM, Lechmann W, Linhart W, et al. Response of primary fibroblasts and osteoblasts to plasma treated polyetheretherketone (PEEK) surfaces. J Mater Sci. 2005;16:671–7.
Mendes SC, Tibbe JM, Veenhof M, Both S, Oner FC, Van Blitterswijk CA, et al. Relation between in vitro and in vivo osteogenic potential of cultured human bone marrow stromal cells. J Mater Sci. 2004;15:1123–8.
Miyamoto S, Teramoto H, Coso QA, Gutkind JS, Burbelo PD, Akiyama SK, et al. Integrin function: molecular hierarchies of cytoskeletal and signalling molecules. J Cell Biol. 1995;131:791–805.
Boudreau NJ, Jones PL. Extracellular matrix and integrin signalling: the shape of things to come. Biochem J. 1999;339:481–8.
Schneider GB, Zaharia R, Stanford C. Osteoblast integrin adhesion and signalling regulate mineralization. J Dent Res. 2001;80:1540–4.
Souto RM, Burstein GT. A preliminary investigation into the microscopic depassivation of passive titanium implant materials in vitro. J Mater Sci. 1996;7:337–43.
Spriano S, Bronzoni M, Verne E, Maina G, Bergo V, Windler M. Characterization of surface modified Ti-6Al-7Nb alloy. J Mater Sci. 2005;16:301–12.
Martins DQ, Osorio WR, Souza EP, Caram R, Garcia A. Effects of Zr content on microstructure and corrosion resistance of Ti-30Nb-Zr casting alloys for biomedical applications. Electrochim Acta. 2008;53:2809–17.
Geetha M, Kamachi Mudali U, Gogia AK, Asokamani RE, Raj B. Influence of microstructure and alloying elements on corrosion behaviour of Ti-13Nb-13Zr alloy. Corros Sci. 2004;46:877–92.
Lavos-Valereto IC, Wolynec S, Ramires I, Guastaldi AC, Costa I. Electrochemical impedance spectroscopy characterization of passive film formed on implant Ti-6Al-7Nb alloy in Hank’s solution. J Mater Sci. 2004;15:55–9.
Yu SY, Scully JR. Corrosion and passivity of Ti-13%Nb-13%Zr in comparison to other biomedical implant alloys. Corrosion 1997;53:965–76.
Gutierrez A, Lopez MF, Jimenez JA, Morant C, Paszti R, Climent A. Surface characterization of the oxide layer grown on Ti-Nb-Zr and Ti-Nb-Al alloys. Surf Interface Anal. 2004;36:977–80.
Zhecheva A, Malino S, Tha W. Surface gas nitrating of Ti-6Al-4 V and Ti-6Al-2Sn-4Zr-2Mo-0.08Si alloys. Z Metallkd. 2003;94:19–24.
Trentani L, Pelillo F, Pavesi FC, Ceciliani L, Cetta G, Forlino A. Evaluation of the TiMo12Zr6Fe2 alloy for orthopaedic implants: in vitro biocompatibility study by using primary human fibroblast and osteoblasts. Biomaterials. 2002;23:2863–9.
Nag S, Banerjee R, Stechschulte J, Fraser HL. Comparison of microstructural evolution in Ti-Mo-Zr-Fe and Ti-15Mo biocompatible alloys. J Mater Sci. 2005;16:679–85.
Lopez MF, Gutierrez JA, Jimenez JA. In vitro corrosion behaviour of titanium alloys without vanadium. Electrochim Acta. 2002;47:1359–64.
Eisenbarth E, Velten D, Mueller M, Thull R, Breme J. Biocompatibility of β-stabilizing elements of titanium alloys. Biomaterials 2004;25:5705–13.
Okazaki Y, Nishimura E, Nakada H, Kobaiashi K. Surface analysis of Ti-15Zr-4Nb-4Ta alloy after implantation in rat tibia. Biomaterials. 2001;22:599–607.
Okazaki Y. A new Ti-15Zr-4Nb-4Ta alloy for medical application. Curr Opin Solid St M. 2001;5:45–53.
Lopez MF, Jimenez JA, Gutierrez A. Corrosion study of surface modified vanadium free titanium alloys. Electrochim Acta. 2003;48:1395–401.
Khan MA, Williams RL, Williams DF. In vitro corrosion and wear of titanium alloys in the biological environment. Biomaterials. 1996;17:2117–26.
Assis SL, Costa I. Electrochemical evaluation of Ti-13Nb-13Zr, Ti-6Al-4 V and Ti-6Al-7Nb alloys for biomedical application by long-term immersion tests. Mater Corros. 2007;58:329–33.
Lopez MF, Soriano L, Palomares FJ, Sanchez-Agudo M, Fuentes GG, Gutierrez A, et al. Soft X-ray absorption spectroscopy study of oxide layers on titanium alloys. Surf Interface Anal. 2002;33:570–6.
Morant C, Lopez MF, Gutierrez A, Jimenez JA. AFM and SEM characterization of non-toxic vanadium-free Ti alloys used as biomaterials. Appl Surf Sci. 2003;220:79–87.
Tamilselvi S, Rajendran N. In vitro corrosion behaviour of Ti-5Al-2Nb-1Ta alloy in Hank’s solution. Mater Corros. 2007;58:285–9.
Robin A, Meirelis JP. Influence of fluoride concentration and pH on corrosion behavior of Ti-6Al-4 V and Ti-23Ta alloys in artificial saliva. Mater Corros. 2007;58:173–80.
Cai Z, Nakajima N, Woldu M, Berglund A, Bergmon M, Okabe T. In vitro corrosion resistance of titanium made using different fabrication methods. Biomaterials. 1999;20:183–90.
Gluszek J, Masalski J, Furman P, Nitsch K. Structural and electrochemical examinations of PACVD TiO2 films in Ringer solutions. Biomaterials 1997;18:789–94.
Popa MV, Demetrescu I, Vasilescu E, Drob P, Santana Lopez A, Mirza-Rosca J, et al. Corrosion susceptibility of implant materials Ti-5Al-4 V and Ti-6Al-4Fe in artificial extra-cellular fluids. Electrochim Acta. 2004;49:2113–9.
Popa MV, Demetrescu I, Suh S-H, Vasilescu E, Drob P, Ionita D, et al. Monitoring of titanium base alloys−biofluids interface. Bioelectrochemistry. 2007;71:126–34.
Popa MV, Vasilescu E, Drob P, Vasilescu C, Demetrescu I, Ionita D. Long-term assessment of the implant titanium material–artificial saliva interface. J Mater Sci. 2008;19:1–9.
Vasilescu E, Drob P, Raducanu D, Dan I, Vasilescu C. Corrosion resistance of some thermo-mechanical treated titanium bioalloy depending on pH of Ringer solution. Rev Chim. (Bucharest). 2009;60:241–7.
Van Kesteren IEH. Product designers’ information needs in materials selection. Mater Des. 2008;29:133–45.
Elias LM, Schneider SG, Schneider S, Silva HM, Malvisi F. Microstructural and mechanical characterization of biomedical Ti–Nb–Zr(–Ta) alloys. Mat Sci Eng A-Struct. 2006;432:108–12.
Li S, Xiong B, Hui S, Ye W, Yu Y. Comparison of the fatigue and fracture of Ti–6Al–2Zr–1Mo–1V with lamellar and bimodal microstructures. Mat Sci Eng A Struct. 2007;460–461:140–5.
Kima HS, Limb SH, Yeo ID, Kima WY. Stress-induced martensitic transformation of metastable-titanium alloy. Mat Sci Eng A-Struct. 2007;449–451:322–5.
Popa MV, Raducanu D, Vasilescu E, Drob P, Cojocaru VD, Vasilescu C, et al. Mechanical and corrosion behaviour of a Ti-Al-Nb alloy after deformation at elevated temperatures. Mater Corros. 2008;59:919–28.
Gordin DM, Gloriant T, Texier G, Thibon I, Ansel D, Duval JL, et al. Development of a β-type Ti-12Mo-5Ta alloy for biomedical applications: cytocompatibility and metallurgical aspects. J Mater Sci. 2004;15:885–91.
Bastos AC, Somoes AM, Gonzalez S, Gonzalez-Garcia Y, Souto RM. Imaging concentration profiles of redox-active species in open-circuit corrosion processes with the scanning electron microscope. Electrochem Commun. 2004;6:1212–5.
Souto RM, Laz MM, Reis RL. Degradation characteristics of hydroxyapatite coatings on orthopaedic TiAlV in simulated physiological media investigated by electrochemical impedance spectroscopy. Biomaterials. 2003;24:4213–21.
Pourbaix M. Atlas of electrochemical equilibria in aqueous solutions. Houston, TX: NACE;1974. p. 213–221, 223–229, 246–250 and 251–255.
ISO TR 10271:2001, Dental metallic materials – Corrosion test methods.
Thomson NG, Buchanan RA, Lemons JE. In vitro corrosion of Ti-6Al-4 V and type 316L stainless steel when gallvanically coupled with carbon. J Biomed Mater Res. 1979;13:35–44.
Shlaby LA. Galvanic coupling of Ti with Cu and Al alloys in chloride media. Corros Sci. 1971;11:767–78.
Guo OK, Du M, Zhou CJ. Study of galvanic corrosion of carbon steel/titanium and carbon steel/titanium/navel brass in seawater. In: Proceedings of 16th International Corrosion. 1–8, September 2005, Beijing, China, Ed. International Corrosion Council, paper 11–3.
Thian S, Huang J, Best SM, Barber ZH, Brooks RA, Rushton N, et al. The response of osteoblasts to nanocrystalline silicon-substituted hydroxyapatite thin films. Biomaterials. 2006;27:2692–8.
Prado Da Silva MH, Soares GDA, Elias CN, Best SM, Gibson IR, Di Silvio L, et al. In vitro cellular response of titanium electrochemically coated with hydroxyapatite compared to titanium with three different levels of surface roughness. J Mater Sci. 2003;14:511–9.
Navarro M, Ginebra MP, Planell JA. Cellular response to calcium phosphate glasses with controlled solubility. J Biomed Mater Res. A. 2004;67:1009–15.
Hynes RO. Integrins: versatility, modulation and signaling in cell adhesion. Cell. 1992;69:11–25.
Giancotti FG, Ruoslahti E. Integrin signals. Science. 1999;285:1028–31.
Rea SM, Brooks RA, Schneider A, Best SM, Bonfield W. Osteoblast-like cell response to bioactive composites-surface-topography and composition effects. J Biomed Mater Res. B. 2004;70:250–61.
Milosev I, Kosec T, Strehblow H-H. XPS and EIS study of the passive film formed on orthopaedic Ti-6Al-7Nb alloy in Hank’s physiological solution. Electrochim Acta. 2008;53:3547–58.
Black J. Biological performance of materials: fundamentals of biocompatibility. New York: Decker M Inc; 1992.
Blackwood DJ, Chua AWC, Seah KHW, Thampuran R, Teoh SH. Corrosion behaviour of porous titanium-graphite composites designed for surgical implants. Corros Sci. 2003;42:481–503.
Acknowledgment
This work was supported by Romanian MEC-CNMP: PN II 07/Contract Number 71-021/2007.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Vasilescu, E., Drob, P., Raducanu, D. et al. In vitro biocompatibility and corrosion resistance of a new implant titanium base alloy. J Mater Sci: Mater Med 21, 1959–1968 (2010). https://doi.org/10.1007/s10856-010-4057-x
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10856-010-4057-x