Abstract
Hydroxyapatite (HA) ceramic has been used in tissue engineering and orthopedics for its good biocompatibility and osteoconductivity. However, its clinical applications are usually limited by the low strength and brittleness. The objective of this research was to develop a new kind of HA composites in which multi-wall carbon nanotubes (MWNTs) were introduced to the HA ceramic matrix to improve the mechanical properties of the resulting composites. A simple chemical wet method was applied to synthesize the HA ceramic particles with the aid of surfactant and ultrasonication technique at normal atmospheric pressure. The morphology and microstructure of the synthesized HA were characterized by XRD and TEM as a function of treatment time. The results showed that the synthesized HA particles are needle-like with a length of 80–160 nm along the (211) direction and an aspect ratio of 5–15. MWNTs were treated with a mixture of nitric acid and sulfuric acid. The HA/MWNT composites were prepared by solution blending. The composites were sintered using a hot-press method. The mechanical properties of the HA/MWNT composites with different volume percentages of MWNTs were examined. The fracture toughness and flexural strength were improved by 50% and 28% separately when the volume percentage of MWNTs reached 7%.
Similar content being viewed by others
References
L. L. HENCH and J. WILSON, An introduction to bioceramics, (Singapore: World Scientific, 1993)
V. SHINY, P. RAMESH, M. C. SUNNY and H. K. VARMA, Mater. Lett. 46 (2000) 142
W. SUCHANEK, M. YOSHIMURA, M. KAKIHANA and M. YOSHIMURA, Biomaterials 17 (1996) 1715
M. BONNER, I. M. WARD, W. MCGREGOR, K. E. TANNER and W. BONFIELD, J. Mater. Sci. Lett. 20 (2001) 2049
T. N. OPARA, M. J. DALBY, E. J. HARPER, L. DI SILVIO and W. BONFIELD, J. Mater. Sci.: Mater. Med. 14 (2003) 277
E. J. HARPER, M. BRADEN and W. BONFIELD, J. Mater. Sci.: Mater. Med. 11 (2000) 491
S. R. RADIN and P. DUCHEYNE, J. Biomed. Mater. Res. 27 (1994) 35
D. M. LIU, T. TROCZYNSKI and W. J. TSENG, Biomaterials 22 (2001) 1721
J. P. FAN, C. P. TSUI, C. Y. TANG and C. L. CHOW, Biomaterials 25 (2004) 5363
J. P. FAN, C. P. TSUI and C. Y. TANG, Mater. Sci. Eng. A 382 (2004) 341
X. L. XIE, C. Y. TANG, K. Y. Y. CHAN, X. C. WU, C. P. TSUI and C. Y. CHEUNG, Biomaterials 24 (2003) 1889
T. J. WEBSTER, C. ERGUN, R. H. DOREMUS and R. W. SIEGEL, Biomaterials 21 (2000) 1803
T. J. WEBSTER, C. ERGUN, R. H. DOREMUS, R. W. SIEGEL and R. BIZIOS, Biomaterials 22 (2001) 1327
T. IKOMA and A. YAMAZAKI, J. Solid State Chem. 144 (1999) 272
F. ZHANG, Z. H. ZHOU, S. P. YANG, L. H. MAO, H. M. CHEN and X. B. YU, Mater. Lett. 59 (2005) 1422
G. BEAAI, G. CELOTTI, E. LANDI, T. M. G. LA TORRETTA, I. SOPYAN and A. TAMPIERI, Mater. Chem. Phys. 78 (2003) 816
M. OMORI, T. ONOKI, T. HASHIDA, A. OKUBO and Y. MURAKAMI, Ceram. Int. 1 (2005) 1
P. LUO and T. G. NIEH, Mater. Sci. Eng. C3 (1995) 75
A. CUNEYT TAS, J. Eur. Ceram. Soc. 20 (2000) 2389
K. KENDALL, Powder Technol. 58 (1989) 151
C. K. WANG, C. P. JU and J. H. CHERN LIN, Mater. Chem. Phy. 53 (1998) 138
H. X. JI and P. M. MARQUIS, Biomaterials 13 (1992) 744
H. JI and P. M. MARQUIS, J. Mater. Sci. 28 (1993) 1941
A. RAPACZ-KMITA, A. SLOSARCZYK and Z. PASZKIEWICZ, J. Eur. Ceram. Soc. 1 (2005) 1
S. IIJIMA, Nature 354 (1991) 56
K. L. ELIAS, R. L. PRICE and T. J. WEBSTER, Biomaterials 23 (2002) 3279
R. L. PRICE, M. C. WAID, K. M. HABERSTROH and T. J. WEBSTER, Biomaterials 24 (2003) 1877
T. K. ANEE, M. ASHOK, M. PALANICHAMY and S. N. KALKURA, Mater. Chem. Phys. 80 (2003) 725
S. RAYNAUD, E. CHAMPION, D. BERNACHE-ASSOLLANT and P. THOMAS, Biomaterials 23 (2002) 1065
A. RAPACZ-KMITA, C. PALUSZKIEWICZ, A. SLOSARCZYK and Z. PASZKIEWICZ, J. Mol. Struct. 744–747 (2005) 653
K. TANAKA, J. Mater. Sci. 22 (1987) 1501
Z. LI, A. GHOSH, A. S. KOBAYASHI and R. C. BRADT, J. Am. Ceram. Soc. 72 (1989) 904
Y. B. BAO, C. P. A. T. KLEIN, X. D. ZHANG, K. de GROOT and Y. B. KLEIN, Biomaterials 5 (1994) 835
H. L. DAI, X. Y. WANG, J. HUANG, Y. H. YAN and S. P. LI, Trans. Nonferrous Met. Soc. China 14 (2004) 769
Acknowledgement
The authors would like to thank for the support from the Research Committee of The Hong Kong Polytechnic University (Project code: RGU2). The authors wish to thank Prof. J.H. Zhang and Miss C.X. Liu for their assistance in sample preparation.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Meng, Y.H., Tang, C.Y., Tsui, C.P. et al. Fabrication and characterization of needle-like nano-HA and HA/MWNT composites. J Mater Sci: Mater Med 19, 75–81 (2008). https://doi.org/10.1007/s10856-007-3107-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10856-007-3107-5