Abstract
The wettability, water sorption and solubility of silicone elastomers used for maxillofacial prostheses were studied. The hypothesis was, that a material that has absorbed water would show an increase in the wettability and thus also the surface free energy of the material.
Seven silicone elastomers, both addition- and condensation type polymers, were included. Five specimens of each material were subjected to treatment according to ISO standards 1567:1999 and 10477: 2004 for water sorption and solubility. The volumes of the specimens were measured according to Archimedes principle. The contact angle was measured with a contact angle goniometer at various stages of the sorption/solubility test.
Wettability changed over the test period, but not according to theory. The addition type silicones showed little or no sorption and solubility, but two of the condensation type polymers tested had a significant sorption and solubility. This study showed that condensation type polymers may show too large volumetric changes when exposed to fluids, and therefore should no longer be used in prosthetic devices. The results of this study also suggests that it might be of interest to test sorption and solubility of materials that are to be implanted, since most of the materials had some solubility.
Similar content being viewed by others
References
D. J. CASTLEBERRY, In Dental Biomaterials, Research Priorities edited by L.W. Wachtel. (Department of Health, Education and Welfare Publication No. 74-548, Washington DC, August 7–8; 1973) p. 255
D. J. MOORE, Z. R. GLASER, M. J. TABACCO, G. LINEBAUGH, J. Prosthet. Dent. 38 (1977) 319
B.F. CONROY. Co-ordinator. In Proceedings of the International Congress on Maxillo-facial Prosthetics and Technology 1978 (1979); p. 218
R. CANTOR, R. L. WEBBER, L. STROUD, G. RYGE, J. Prosthet. Dent. 21 (1969) 324
ISO standard 14949:2001 Implants for Surgery—Two-Part Addition-Cure Silicone Elastomers
A. K. HULTERSTRÖM, I. E. RUYTER, Int. J. Prosthodont. 12 (1999) 498
M. G. J. WATERS, R. G. JAGGER, V. JEROLIMOV, K. R. WILLIAMS, J. Prosthet. Dent. 74 (1995) 644
P. H. MONSÉNÉGO, A. BASZKIN, M. De LOURDES COSTA, J. LEJOYEUX, J. Prosthet. Dent. 62 (1989) 308
E. M. VERES, J. F. WOLFAARDT, P. J. BECKER, J. Prosthet. Dent. 63 (1990) 466
M. G. J. WATERS, R. G. JAGGER, G. L. POLYZOIS, J. Prosthet. Dent. 81 (1999) 439
J. Y. CHAI, T. -C. YEUNG, Int. J. Prosthodont. 4 (1991) 555
G. L. POLYZOIS, R. W. WINTER, G. D. STAFFORD, Biomaterials 12 (1991) 79
J. VAN DIJK, F. HERKSTRÖTER, H. BUSSCHER, A. WEERKAMP, H. JANSEN, J. ARENDS, J. Clin. Periodontol. 14, (1987) 300
M. G. J. WATERS, D. W. WILLIAMS, R. G. JAGGER and M. A. O. LEWIS, J. Prosthet. Dent. 77, (1997) 306
S. C. DEXTER, J. D. SULLIVAN Jr, J. WILLIAMS III and S. W. WATSON, Appl. Microbiol. 30, (1975) 298
ISO 1567:1999 Denture Base Polymers
ISO 10477:1992 Dentistry—Polymer Based Crown and Bridge Materials
R. J. GOOD, In Contact Angle, Wettability and Adhesion. Festschrift in Honor of Professor Robert J Good, edited by K. L. Mittal (Netherlands VSP BV: Zeist, 1993) p. 3
R. E. JOHNSON and R.H. DETTRE, In Surface and Colloid Science, edited by E. Matijevic (New York: Wiley-Interscience, 1969) p. 85
T. R. NEU, G. J. VERKERKE, I. F. HERRMANN and H. K. SCHUTTE, J. Appl. Bacteriol. 76, (1994) 521
T. R. NEU, H. C. VAN DER MEI, H. J. BUSSCHER, F. DIJK and G. J. VERKERKE, Biomaterials 14, (1993) 459
H. J. BUSSCHER, G. I. GEERTSEMA-DOORNBUSCH and H. C. VAN DER MEI, J. Biomed. Mater. Res. 34, (1997) 201
E. P. J. M. EVERAERT, H. F. MATHIEU, B. VAN DE BELT GRITTER, A. J. G. E. PEETERS, G. J. VERKERKE, H. C. VAN DER MEI and H. J. BUSSCHER, Ach. Otolartngol. Head. Neck. Surg. 125, (1999) 1329
F. KAWANO, E. R. DOOTZ, A. KORAN III and R. G. CRAIG, J. Prosthet. Dent. 72, (1994) 393
C. J. ANDRES, S. P. HAUG, D. T. BROWN and G. BERNAL, J. Prosthet. Dent. 68, (1992) 519
Acknowledgements
The authors thank Torbjørn Knarvang, NIOM- Scandinavian Institute of Dental Materials, for his invaluable assistance in carrying out the contact angle measurements and the measurements in the sorption and solubility tests.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Hulterström, A.K., Berglund, A. & Ruyter, I.E. Wettability, water sorption and water solubility of seven silicone elastomers used for maxillofacial prostheses. J Mater Sci: Mater Med 19, 225–231 (2008). https://doi.org/10.1007/s10856-006-0027-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10856-006-0027-8