Abstract
In this study, a newly developed duplex coating method incorporating plasma carburization and CrN coating was applied to Ti–6Al–4V and its effects on the wear resistance and fatigue life were investigated. The carburized layer with approximately150 μm in depth and CrN coating film with 7.5 μm in thickness were formed after duplex coating. Hard carbide particles such as TiC And V4C3 were formed in the carburized layer. XRD diffraction pattern analysis revealed that CrN film had predominant [111] and [200] textures. The hardness (Hv) was significantly improved up to about 1,960 after duplex coating while the hardness value of original Ti–6Al–4V was 402. The threshold load for the modification and/or failure of CrN coating was measured to be 32 N using the acoustic emission technique. The wear resistance and fatigue life of duplex-coated Ti–6Al–4V improved significantly compared to those of un-treated specimen. The enhanced wear resistance can be attributed to the excellent adhesion and improved hardness of CrN coating film for the duplex-coated Ti–6Al–4V. The initiation of fatigue cracks is likely to be retarded by the presence of hard and strong layers on the surface, resulting in the enhanced fatigue life.
Similar content being viewed by others
References
J. FISHER, X. Q. HU, T. D. STEWART, S. WILLIAMS, J. L. TIPPER, E. INGHAM, M. H. STONE, C. DAVIES, P. HATTO, J. BOLTON, M. RILEY, C. HARDAKER, G. H. ISAAC and G. BERRY, J. Mater. Sci.: Mater. Med. 19 (1998) 1621
H. M. KIM, F. MIYAJI, T. KOKUBO and T. NAKAMURA, J. Mater. Sci.: Mater. Med. 8 (1997) 341
M. INAGAKI, Y. YOKOGAWA and T. KAMEYAMA, J. Mater. Sci. 14 (2003) 919
T. M. LEE, R. S. TSAI, E. CHANG, C. Y. YANG and M. R. YANG, J. Mater. Sci.: Mater. Med. 13 (2002) 341
P. M. BRETT, J. HARLE, V. SALIH, R. MIHOC, I. OLSEN, F. H. JONES and M. TONETTI, Bone 35 (2004) 124
A. COSTANTINI, G. LUCIANI, F. BRANDA, L. AMBROSIO and G. MATTOGNO, J. Mater. Sci.: Mater. Med. 13 (2002) 891
C. APARICIO, F. J. GIL, J. A. PLANELL and E. ENGEL, J. Mater. Sci.: Mater. Med. 13 (2002) 1105
H. S. DOBBS and M. J. MINSKI, Biomaterials 1 (1980) 193
D. LIU, B. TANG, X. ZHU, H. CHEN, J. HE and J.-P. CELIS, Surf. Coat. Technol. 116–119 (1999) 234
S. ORTMANN, A. SAVAN, Y. GERBIG and H. HAEFKE, Wear 254 (2003) 1099
E. CZARNOWSKA, T. WIERZCHON, A. MARANDA-NIEDBALA and E. KARCZMAREWICZ, J. Mater. Sci.: Mater. Med. 11 (2000) 73
S. K. YEN, M. J. GUO and H. Z. ZAN, Biomaterials 22 (2001) 125
D. V. SHATANSKY, N. A. GLOUSHANKOVA, A. N. SHEVEIKO, M. A. KHARITONOVA, H. MOIZHESS, E. A. LEVASHOV and F. ROSSI, Biomaterials 26 (2005) 2909
A. WILSON, A. MATTHEWS, J. HOUSDEN, R. TURNER and B. GARSIDE, Surf. Coat. Technol. 62 (1993) 600
M. MANSO-SILVAN, J. M. MARTÍNEZ-DUART, S. OGUETA, P. GARCÍA-RUIZ and J. PÉREZ-RIGUEIRO, J. Mater. Sci.: Mater. Med. 13 (2002) 289
P. V. KOLA, S. DANIELS, D. C. CAMERON and M. S. J. HASHIMI, J. Mater. Process. Technol. 56 (1996) 422
U. GLASER, “The toxicity of chromium in the zero and trivalent form.” In Biocompatibility of Co=Cr-Ni Alloys, edited by H. F. Hildeber and, M. Champy, Nato ASI Series (New York: Plenum Press, 1986), p. 21
S. MALL, S. A. NAMJOSHI and W. J. PORTER, Mater. Sci. Eng. A, 383 (2004) 334
B. D. CULLITY, Elements of X-ray Diffraction, 2nd edn. (Reading: Addison-Wesley Publishing Co., 1978). p. 123
S. I. HONG and M. A. HILL, Mater. Sci. Eng. A 281 (2000) 189
D. H. KOHN, P. DUCHEYNE and J. AWERBUCH, J. Biomed. Mater. Res. 26 (1992) 19
O. WÄNSTRAND, R. FELLA and N. AXËN, Surf. Coat. Technol. 94–95 (1997) 469
B. NAVINSEK, P. PANJAN and J. KRUSIC, Surf. Coat. Technol. 98 (1998) 809
Y. G. PARK, C. H. BAEK and M. Y. WEY, Kor. J. Mater. Res. 12 (2002) 669
S. I. HONG and C. LAIRD, Metall. Trans. 22A (1991) 415
Acknowledgment
This work was supported by Korea Research Foundation (2004–05, KRF-D000318).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Park, Y.G., Wey, M.Y. & Hong, S.I. Enhanced wear and fatigue properties of Ti–6Al–4V alloy modified by plasma carburizing/CrN coating. J Mater Sci: Mater Med 18, 925–931 (2007). https://doi.org/10.1007/s10856-006-0014-0
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10856-006-0014-0