Effects of sintering temperature on structural, infrared, magnetic and electrical properties of Cd0.5Zn0.5FeCrO4 ferrites prepared by sol–gel route

  • Published:
Journal of Materials Science: Materials in Electronics Aims and scope Submit manuscript

Abstract

In this work, an attempt is made to study the effects of sintering temperature on the structural, infrared, magnetic and electrical properties of Cd0.5Zn0.5FeCrO4 ferrites. Samples were prepared by sol–gel route and sintered at 900 and 1100 °C. The structural characterization of the synthesized powders by X-ray powder diffraction showed that only single phase with cubic spinel structure existed. Estimated values of unit cell parameter and average grains size show an increase with sintering temperature. The intensities of absorption bands, spontaneous magnetization, electrical conductivity, and dielectric constants were found to increase with increasing sintering temperature. The non-overlapping small polaron tunneling (NSPT) model dominates the conduction process for the studied samples which present a relaxation phenomenon with non-Debye nature. Close activation energies values were found from analyzes of relaxation time and dc-conductivity indicating that the relaxation and the conduction processes may be attributed to the same type of charge carriers. The equivalent electrical circuit (Rg+ Rgb//CPEgb) was used for modeling the Nyquist data.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11
Fig. 12
Fig. 13
Fig. 14
Fig. 15

Similar content being viewed by others

References

  1. Y.D. Kolekar, L. Sanchez, E.J. Rubio, C.V. Ramana, Solid State Commun. 184, 34 (2014)

    CAS  Google Scholar 

  2. R. Nongjai, S. Khan, K. Asokan, H. Ahmed, I. Khan, J. Appl. Phys. 112, 084321 (2012)

    Google Scholar 

  3. Z. Gao, B. Xu, M. Ma, A. Feng, Y. Zhang, X. Liu, Z. Jia, G. Wu, Composites Part B 179, 107417 (2019)

    CAS  Google Scholar 

  4. J. Wang, B. Wang, A. Feng, Z. Jia, G. Wu, J. Alloys Compd. 834, 155092 (2020)

    CAS  Google Scholar 

  5. X. Zhou, C. Zhang, M. Zhang, A. Feng, S. Qu, Y. Zhang, X. Liu, Z. Jia, G. Wu, Composites Part A 127, 105627 (2019)

    CAS  Google Scholar 

  6. G. Wu, Y. Cheng, Z. Yang, Z. Jia, H. Wu, L. Yang, H. Li, P. Guo, H. Lv, Chem. Eng. J. 333, 519 (2018)

    CAS  Google Scholar 

  7. R. Sharma, P. Thakur, P. Sharma, V. Sharma, J. Alloys Compd. 704, 7 (2017)

    CAS  Google Scholar 

  8. Z.A. Gilani, M.F. Warsi, M.N. Anjum, I. Shakir, S. Naseem, S. Riaz, M.A. Khan, J. Alloys Compd. 639, 268 (2015)

    CAS  Google Scholar 

  9. A. Šutka, K.A. Gross, Sensors Actuators B Chem. 222, 95 (2016)

    Google Scholar 

  10. S. Amiri, H. Shokrollahi, Mater. Sci. Eng., C 33, 1 (2013)

    CAS  Google Scholar 

  11. E. Oumezzine, S. Hcini, M. Baazaoui, E.K. Hlil, M. Oumezzine, Powder Technol. 278, 189 (2015)

    CAS  Google Scholar 

  12. W. Zhang, A. Sun, X. Zhao, X. Pan, Y. Han, N. Suo, L. Yu, Z. Zuo, J. Alloys Compd. 816, 152501 (2020)

    CAS  Google Scholar 

  13. J. Pei, Z. Wang, Y. Gao, H. Zhang, Curr. Appl. Phys. 19, 440 (2019)

    Google Scholar 

  14. E. Oumezzine, S. Hcini, E.K. Hlil, E. Dhahri, M. Oumezzine, J. Alloys Compd. 615, 553 (2014)

    CAS  Google Scholar 

  15. P.P. Hankarea, S.D. Jadhava, U.B. Sankpala, S.S. Chavana, K.J. Waghmareb, B.K. Chougule, J. Alloys Compd. 475, 926 (2009)

    Google Scholar 

  16. S.A.S. Ebrahimi, S.M. Masoudpanah, J. Magn. Magn. Mater. 357, 77 (2014)

    Google Scholar 

  17. J. Liu, Y. Mei, W. Liu, X. Li, F. Hou, G.Q. Lu, J. Magn. Magn. Mater. 454, 6 (2018)

    CAS  Google Scholar 

  18. J. Balavijayalakshmi, N. Suriyanarayanan, R. Jayaprakash, J. Magn. Magn. Mater. 362, 135 (2014)

    CAS  Google Scholar 

  19. N. Kouki, S. Hcini, M. Boudard, R. Aldawas, A. Dhahri, RSC Adv. 9, 1990 (2019)

    CAS  Google Scholar 

  20. S. Hcini, N. Kouki, A. Omri, A. Dhahri, M.L. Bouazizi, J. Magn. Magn. Mater. 464, 91 (2018)

    CAS  Google Scholar 

  21. M.F. Valan, A. Manikandan, S.A. Antony, J. Nanosci. Nanotechnol. 15, 4543 (2015)

    CAS  Google Scholar 

  22. S. Ghatak, G. Chakraborty, M. Sinha, S.K. Pradhan, A.K. Meikap, Mater. Sci. Appl. 2, 226 (2011)

    CAS  Google Scholar 

  23. M. Chakrabarti, D. Sanyal, A. Chakrabarti, J. Phys.: Condens. Matter 19, 236210 (2007)

    Google Scholar 

  24. M. Siddique, M. Anwar-ul-Islam, N.M. Butt, T. Abbas, Misbah-ul-Islam, Phys. Status Solidi B 216, 1069 (1999)

    CAS  Google Scholar 

  25. K.N. Harish, H.S.B. Naik, P.N.P. Kumar, R. Viswanath, Catal. Sci. Technol. 2, 1033 (2012)

    CAS  Google Scholar 

  26. S.M. Patange, S.E. Shirsath, B.G. Toksha, S.S. Jadhav, K.M. Jadhav, J. Appl. Phys. 106, 023914 (2009)

    Google Scholar 

  27. S. Nasir, M. Anis-ur-Rehman, M.A. Malik, Phys. Scr. 83, 025602 (2011)

    Google Scholar 

  28. S.M. Patange, S.E. Shirsath, S.S. Jadhav, K.M. Jadhav, Phys. Status Solidi A 209, 347 (2012)

    CAS  Google Scholar 

  29. A.M. Gismelseed, A.A. Yousif, Physica B 370, 215 (2005)

    CAS  Google Scholar 

  30. M.S. Anwar, F. Ahmed, B.H. Koo, Acta Mater. 71, 100 (2014)

    CAS  Google Scholar 

  31. M.A. Hakim, S.K. Nath, S.S. Sikder, K.H. Maria, J. Phys. Chem. Solids 74, 1316 (2013)

    CAS  Google Scholar 

  32. K.A.M. Khalaf, A.D. Al Rawas, A.M. Gismelssed, A. Al Jamel, S.K.J. Al Ani, M.S. Shongwe, K.O. Al Riyami, S.R. Al Alawi, J. Alloys Compd. 701, 474 (2017)

  33. H.M. Rietveld, J. Appl. Crystallogr. 2, 65 (1969)

    CAS  Google Scholar 

  34. R.P. Patil, P.P. Hankare, K.M. Garadkar, R. Sasikala, J. Alloys Compd. 523, 66 (2012)

    CAS  Google Scholar 

  35. M. Rahimi, P. Kameli, M. Ranjbar, H. Salamati, J. Nanopart. Res. 15, 1865 (2013)

    Google Scholar 

  36. K. Sabri, A. Rais, K. Taibi, M. Moreau, B. Ouddane, A. Addou, Physica B 501, 38 (2016)

    CAS  Google Scholar 

  37. R.M. Thankachan, J. Cyriac, B. Raneesh, N. Kalarikkal, D. Sanyalc, P.M.G. Nambissan, RSC Adv. 5, 64966 (2015)

    CAS  Google Scholar 

  38. R.D. Shannon, Acta Crystallogr. A 32, 751 (1976)

    Google Scholar 

  39. S. Hcini, S. Zemni, A. Triki, H. Rahmouni, M. Boudard, J. Alloys Compd. 509, 1394 (2011)

    CAS  Google Scholar 

  40. A. Gholizadeh, E. Jafari, J. Magn. Magn. Mater. 422, 328 (2017)

    CAS  Google Scholar 

  41. E. AlArfaj, S. Hcini, A. Mallah, M.H. Dhaou, M.L. Bouazizi, J. Supercond. Nov. Magn. 31, 4107 (2018)

    CAS  Google Scholar 

  42. B.P. Ladgaonkar, C.B. Kolekar, A.S. Vaingankar, Bull. Mater. Sci. 25(4), 351 (2002)

    CAS  Google Scholar 

  43. M.D. Rahaman, M.D. Mia, M.N.I. Khan, A.K.M.A. Hossain, J. Magn. Magn. Mater. 404, 238 (2016)

    CAS  Google Scholar 

  44. H. Shokrollahi, K. Janghorban, J. Mater. Process. Technol. 189, 1 (2007)

    CAS  Google Scholar 

  45. Ch. Sujatha, K.V. Reddy, K.S. Babu, A.R. Reddy, K.H. Rao, Ceram. Int. 38, 5813 (2012)

    CAS  Google Scholar 

  46. V. Manikandan, A. Vanitha, E.R. Kumar, S. Kavita, J. Magn. Magn. Mater. 426, 11 (2017)

    CAS  Google Scholar 

  47. A.E. Berkowitz, J.A. Lahut, I.S. Jacobs, L.M. Levinson, D.W. Forester, Phys. Rev. Lett. 34, 594 (1975)

    CAS  Google Scholar 

  48. A.E. Berkowitz, J.A. Lahut, C.E. Van Buren, IEEE Trans. Magn. Magn. 16, 184 (1980)

    Google Scholar 

  49. J.M.D. Coey, Phys. Rev. Lett. 27, 1140 (1971)

    CAS  Google Scholar 

  50. J. Nogues, I.K. Schuller, J. Magn. Magn. Mater. 192, 203 (1999)

    CAS  Google Scholar 

  51. J. Nogues, J. Sort, V. Langlias et al., Phys. Rep. Rev. Sect. Phys. Lett. 422(3), 65 (2005)

    Google Scholar 

  52. K. Maaz, S. Karim, A. Mumtaz, S.K. Hasanain, J. Liu, J.L. Duan, J. Magn. Magn. Mater. 321, 1838 (2009)

    CAS  Google Scholar 

  53. M. Artus, L.B. Tahar, F. Herbst, L. Smiri, F. Villain, N. Yaacoub, J.M. Grenèche, S. Ammar, F. Fiévet, J. Phys. Condens. Matter 23, 506001 (2011)

    Google Scholar 

  54. S. Hcini, S. Khadhraoui, A. Triki, S. Zemni, M. Boudard, M. Oumezzine, J. Supercond. Nov. Magn. 27, 195 (2014)

    CAS  Google Scholar 

  55. K. Funke, Prog. Solid State Chem. 22, 111 (1993)

    CAS  Google Scholar 

  56. M.H. Dhaou, S. Hcini, A. Mallah, M.L. Bouazizi, A. Jemni, Appl. Phys. A 123, 8 (2017)

    Google Scholar 

  57. A. Selmi, S. Hcini, H. Rahmouni, A. Omri, M.L. Bouazizi, A. Dhahri, Phase Transit. 90, 942 (2017)

    CAS  Google Scholar 

  58. Sh.A. Mansour, I.S. Yahia, G.B. Sakr, Solid State Commun. 150, 1386 (2010)

    CAS  Google Scholar 

  59. F.B. Abdallah, A. Benali, S. Azizi, M. Triki, E. Dhahri, M.P.F. Graça, M.A. Valente, J. Mater. Sci. Mater. Electron. 30, 8457 (2019)

    CAS  Google Scholar 

  60. A. Sutka, S. Lagzdina, G. Mezinskis, A. Pludons, I. Vitina, L. Timma, IOP Conf. Ser. Mater. Sci. Eng. 25, 012019 (2011)

    Google Scholar 

  61. E. Oumezzine, S. Hcini, F.I.H. Rhouma, M. Oumezzine, J. Alloys Compd. 726, 187 (2017)

    CAS  Google Scholar 

  62. J.C. Maxwell, Electricity and Magnetism (Oxford University Press, London, 1973)

    Google Scholar 

  63. M. Idrees, M. Nadeem, M. Atif, M. Siddique, M. Mehmood, M.M. Hassan, Acta Mater. 59, 1338 (2011)

    CAS  Google Scholar 

  64. J.C. Giuntini, J.V. Zanchetta, D. Jullien, R. Eholie, P. Houenou, J. Non-Cryst. Solids 45, 57 (1981)

    CAS  Google Scholar 

  65. M. Chebaane, N. Talbi, A. Dhahri, M. Oumezzine, K. Khirouni, J. Magn. Magn. Mater. 426, 646 (2017)

    CAS  Google Scholar 

  66. D. Johnson, ZView: A Software Program for IES Analysis, Version 2.8 (Scribner Associates, Inc., Southern Pines, 2008)

    Google Scholar 

  67. R. Charguia, S. Hcini, M. Boudard, A. Dhahri, J. Mater. Sci. Mater. Electron. 30, 2975 (2019)

    CAS  Google Scholar 

  68. C.B. Mohamed, K. Karoui, S. Saidi, K. Guidara, A.B. Rhaiem, Physica B 451, 87 (2014)

    CAS  Google Scholar 

  69. N. Sivakumar, A. Narayanasamy, N. Ponpandian, G. Govindaraj, J. Appl. Phys. 101, 084116 (2007)

    Google Scholar 

  70. S. Hcini, A. Omri, M. Boudard, M.L. Bouazizi, A. Dhahri, K. Touileb, J. Mater. Sci. Mater. Electron. 29, 6879 (2018)

    CAS  Google Scholar 

Download references

Acknowledgements

This project was supported by the Deanship of Scientific Research at Prince Sattam Bin Abdulaziz University under the Research Project No. 2020/01/16565.

Author information

Authors and Affiliations

  1. Laboratory of Physical Chemistry of Materials, Physics Department, Faculty of Sciences of Monastir, Monastir University, 5019, Monastir, Tunisia

    Fakher Hcini, Sobhi Hcini & Sadok Zemni

  2. Research unit of valorization and optimization of exploitation of resources, Faculty of Science and Technology of Sidi Bouzid, Kairouan University, 9100, Sidi Bouzid, Tunisia

    Fakher Hcini

  3. College of Engineering, Prince Sattam Bin Abdulaziz University, P.O. Box 655, Al Kharj, 11942, Saudi Arabia

    Bandar Alzahrani & Mohamed Lamjed Bouazizi

Authors
  1. Fakher Hcini
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Sobhi Hcini
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Bandar Alzahrani
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Sadok Zemni
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Mohamed Lamjed Bouazizi
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding authors

Correspondence to Fakher Hcini or Mohamed Lamjed Bouazizi.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Hcini, F., Hcini, S., Alzahrani, B. et al. Effects of sintering temperature on structural, infrared, magnetic and electrical properties of Cd0.5Zn0.5FeCrO4 ferrites prepared by sol–gel route. J Mater Sci: Mater Electron 31, 14986–14997 (2020). https://doi.org/10.1007/s10854-020-04061-8

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s10854-020-04061-8

Search

Navigation