Abstract
Nitrogen and fluorine co-doped three-dimensional(3D) graphene-like material, MP-700, is successfully prepared using a one-pot method by directly pyrolyzing melamine and PTFE in N2 flow. This 3D graphene-like material has a high specific surface area (1309 m2 g−1) and the N and F contents are is 19.03 and 0.41 at.%, respectively. Furthermore, it shows the high specific capacitance of 230 F g−1 at 0.5 A g−1; and exhibits long-term stability. After 10,000 cycles, the capacitance retention rate is 86.3% at 20 A g−1, which has a good prospect in the electrode materials of supercapacitors.
Similar content being viewed by others
References
A. Kulkarni, S. Siahrostami, A. Patel, J.K. Norskov, Chem. Rev. 118, 2302 (2018)
Q. Liu, S. Zhang, J. Liao, K. Feng, Y. Zheng, B.G. Pollet, H. Li, J. Power Sour. 355, 191 (2017)
Y. Zheng, L. Zhang, P. He, D. Dang, Q. Zeng, J. Zeng, M. Liu, Electrocatalysis 9, 495 (2018)
H. Song, A. Tang, G. Xu, L. Liu, Y. Pan, M. Yin, Int. J. Electrochem. Sci. 13, 6708 (2018)
X. Tian, J. Luo, H. Nan, H. Zou, R. Chen, T. Shu, X. Li, Y. Li, H. Song, S. Liao, R.R. Adzic, J. Am. Chem. Soc. 138, 1575 (2016)
Q. Yi, H. Chu, M. Tang, Z. Yang, Q. Chen, X. Liu, J. Electroanal. Chem. 739, 178 (2015)
F. Liu, X. Yang, D. Dang, X. Tian, ChemElectroChem 6, 2208 (2019)
A. Tang, Q. Zhong, G. Xu, H. Song, RSC Adv. 6, 84439 (2016)
M. Rahimi-Nasrabadi, H.R. Naderi, M.S. Karimi, F. Ahmadi, S.M. Pourmortazavi, J. Mater. Sci. 28, 1877 (2017)
C. Xiang, Q. Wang, Y. Zou, P. Huang, H. Chu, S. Qiu, F. Xu, L. Sun, J. Mater. Chem. A 5, 9907 (2017)
T. Wu, L. Sun, F. Xu, D. Cai, J. Mater. Sci. Technol. 34, 2384 (2018)
Y. Luo, L. Sun, F. Xu, S. Wei, Q. Wang, H. Peng, C. Chen, J. Mater. Sci. Technol. 34, 1412 (2018)
M. Acerce, D. Voiry, M. Chhowalla, Nat. Nanotechnol. 10, 313 (2015)
N. Choudhary, C. Li, J. Moore, N. Nagaiah, L. Zhai, Y. Jung, J. Thomas, Adv. Mater. 29, 1605336 (2017)
H. Yan, T. Li, Y. Lu, J. Cheng, T. Peng, J. Xu, L. Yang, X. Hua, Y. Liu, Y. Luo, Dalton Trans. 45, 17980 (2016)
H. Peng, F. Liu, X. Liu, S. Liao, C. You, X. Tian, H. Nan, L. Fan, H. Song, Z. Fu, ACS Catal. 4, 3797 (2014)
Q. Yi, Q. Chen, Electrochim. Acta 182, 96 (2015)
K. Deng, C. Li, X. Qiu, J. Zhou, Z. Hou, J. Electroanal. Chem. 755, 197 (2015)
L. Yu, Q. Yi, G. Li, Y. Chen, X. Yang, J. Electrochem. Soc. 165, A2502 (2018)
Q. Yi, Y. Zhang, X. Liu, Y. Yang, Sci. China Chem. 57, 739 (2014)
H. Peng, Z. Mo, S. Liao, H. Liang, L. Yang, F. Luo, H. Song, Y. Zhong, B. Zhang, Sci. Rep. 3, 1765 (2013)
Z. Deng, Q. Yi, G. Li, Y. Chen, X. Yang, H. Nie, Electrochim. Acta 279, 1 (2018)
Y.F. An, Z.M. Li, Y.Y. Yang, B.S. Guo, Z.Y. Zhang, H.Y. Wu, Z.A. Hu, Adv. Mater. Interfaces 4, 10 (2017)
B. Mendoza-Sanchez, Y. Gogotsi, Adv. Mater. 28, 6104 (2016)
J.P. Paraknowitsch, A. Thomas, Energy Environ. Sci. 6, 2839 (2013)
Q. Long, W. Chen, H. Xu, X. Xiong, Y. Jiang, F. Zou, X. Hu, Y. Xin, Z. Zhang, Y. Huang, Energy Environ. Sci. 6, 2497 (2013)
H. Peng, P. Huang, P. Yi, F. Xu, L. Sun, J. Mol. Struct. 1154, 590 (2018)
J. Ding, S. Ji, H. Wang, H. Gai, F. Liu, B.G. Pollet, R. Wang, Chem. Commun. 55, 2924 (2019)
Y. Deng, Y. Xie, K. Zou, X. Ji, J. Mater. Chem. A 4, 1144 (2016)
S.K. Singh, K. Takeyasu, J. Nakamura, Adv. Mater. 31, 1804297 (2019)
A. Akhundi, E.I. García-López, G. Marcì, A. Habibi-Yangjeh, L. Palmisano, Res. Chem. Intermed. 43, 5153 (2017)
A. Akhundi, A. Habibi-Yangjeh, J. Colloid Interface Sci. 504, 697 (2017)
M. Sevilla, R. Mokaya, Energy Environ. Sci. 7, 1250 (2014)
L.F. Chen, Z.H. Huang, H.W. Liang, H.L. Gao, S.H. Yu, Adv. Funct. Mater. 24, 5104 (2014)
J. Zhou, J. Lian, L. Hou, J. Zhang, H. Gou, M. Xia, Y. Zhao, T.A. Strobel, L. Tao, F. Gao, Nat. Commun. 6, 8503 (2015)
C.L. Wang, L. Sun, Y. Zhou, P. Wan, X. Zhang, J.S. Qiu, Carbon 59, 537 (2013)
M. Karuppannan, Y. Kim, Y.-E. Sung, O.J. Kwon, J. Appl. Electrochem. 49, 57 (2019)
P. Sivakumar, M. Jana, M. Kota, H.S. Lee, H.S. Park, J. Alloys Compd. 781, 515 (2019)
F. Bahmani, S.H. Kazemi, H. Kazemi, M. Kiani, S.Y. Feizabadi, J. Alloys Compd. 784, 500 (2019)
M. Aghazadeh, I. Karimzadeh, M.R. Ganjali, M.G. Maragheh, J. Mater. Sci. 29, 5163 (2018)
H. Peng, F. Liu, X. Qiao, Z. Xiong, X. Li, T. Shu, S. Liao, Electrochim. Acta 182, 963 (2015)
J. Chen, H.M. Wei, H.J. Chen, W.H. Yao, H.L. Lin, S. Han, Electrochim. Acta 271, 49 (2018)
C. Shao, S. Qiu, H. Chu, Y. Zou, C. Xiang, F. Xu, L. Sun, Catal. Today 318, 150 (2017)
J. Zhou, Z.S. Zhang, W. Xing, J. Yu, G.X. Han, W.J. Si, S.P. Zhuo, Electrochim. Acta 153, 68 (2015)
D.W. Wang, F. Li, M. Liu, G.Q. Lu, H.M. Cheng, J. Phys. Chem. C 112, 9950 (2008)
L. Miao, D.Z. Zhu, M.X. Liu, H. Duan, Z.W. Wang, Y.K. Lv, W. Xiong, Q.J. Zhu, L.C. Li, X.L. Chai, L.H. Gan, Chem. Eng. J. 347, 233 (2018)
D. Dastan, N. Chaure, M. Kartha, J. Mater. Sci. 28, 7784 (2017)
Y.L. Wang, B.B. Chang, D.X. Guan, X.P. Dong, J. Solid State Electrochem. 19, 1783 (2015)
D. Dastan, JAMCNP 2, 109 (2015)
D. Dastan, Appl. Phys. A 123, 699 (2017)
A. Reina, X. Jia, J. Ho, D. Nezich, H. Son, V. Bulovic, M.S. Dresselhaus, J. Kong, Nano Lett. 9, 30 (2008)
K. Yokoyama, S. Yokoyama, Y. Sato, K. Hirano, S. Hashiguchi, K. Motomiya, H. Ohta, H. Takahashi, K. Tohji, Y. Sato, J. Mater. Chem. A 4, 9184 (2016)
S. Kundu, W. Xia, W. Busser, M. Becker, D.A. Schmidt, M. Havenith, M. Muhler, Phys. Chem. Chem. Phys. 12, 4351 (2010)
K. Bushimata, S.I. Ogino, K. Hirano, T. Yabune, K. Sato, T. Itoh, K. Motomiya, K. Yokoyama, D. Mabuchi, H. Nishizaka, G. Yamamoto, T. Hashida, K. Tohji, Y. Sato, J. Phys. Chem. C 118, 14948 (2014)
J. Lahaye, G. Nanse, A. Bagreev, V. Strelko, Carbon 37, 585 (1999)
T. Sharifi, G. Hu, X.E. Jia, T. Wagberg, ACS Nano 6, 8904 (2012)
L. Chao, J. Zhuang, X. Yong, M. Zheng, H. Hang, H. Dong, B. Lei, H. Zhang, Y. Liu, J. Power Sour. 310, 145 (2016)
W. Qian, J. Yan, Y. Wang, W. Tong, M. Zhang, X. Jing, Z. Fan, Carbon 67, 119 (2014)
K. Ghosh, M. Kumar, T. Maruyama, Y. Ando, Carbon 48, 191 (2010)
W. Na, J. Jun, J.W. Park, G. Leea, J. Jang, J. Mater. Chem. A 5, 17379 (2017)
D.Y. Qu, X.K. Feng, X. Wei, L.P. Guo, H.P. Cai, H.L. Tang, Z.Z. Xie, Appl. Surf. Sci. 413, 344 (2017)
Acknowledgements
We gratefully acknowledge the financially supported by the National Science Foundation of China (51761006, 51671062, 51801041), the National Key Research and Development Program of China (2018YFB1502103), the National Science Foundation of Guangxi Province (2018JJA160046, AD17195073, 2017AD23029, 2017JJB150085) and Guangxi Bagui Scholar Foundation.
Author information
Authors and Affiliations
Corresponding authors
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Duan, D., Hu, F., Ma, J. et al. A facile one-pot method to prepare nitrogen and fluorine co-doped three-dimensional graphene-like materials for supercapacitors. J Mater Sci: Mater Electron 30, 19505–19512 (2019). https://doi.org/10.1007/s10854-019-02316-7
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10854-019-02316-7