Abstract
Polyaniline (PANI)/CoFe2O4/Ba3Co2Fe24O41 composite was prepared by an in-situ polymerization method. The phase structure, morphology and magnetic properties of the as-prepared PANI/CoFe2O4/Ba3Co2Fe24O41 composite were characterized by XRD, FT-IR, SEM, TEM, and VSM, respectively. The microwave absorption properties of the composite were investigated by using a vector network analyzer in the 2–18 GHz frequency range. The results show that the maximum reflection loss value of the PANI/CoFe2O4/Ba3Co2Fe24O41 composite reaches −30.5 dB at 10.5 GHz with a thickness of 3 mm and the bandwidth of reflection loss below −10 dB reaches up to 1.2 GHz. The excellent microwave absorption properties of the as-prepared PANI/CoFe2O4/Ba3Co2Fe24O41 composite due to the enhanced impedance match between dielectric loss and magnetic loss.
Similar content being viewed by others
References
H. Zaigham, F.A. Khalid, J. Mater. Sci. Technol. 27, 218–222 (2011)
N. Chen, K. Yang, M. Gu, J. Alloys Compd. 490, 609–612 (2010)
L. Yan, J. Wang, X. Han et al., Nanotechnology 21, 95708–95712 (2010)
X. Guo, Y. Deng, D. Gu et al., J. Mater. Chem. 19, 6706–6712 (2009)
T. Chen, J. Qiu, K. Zhu, J. Mater. Sci. 25, 3664–3673 (2014)
X.L. Dong, X.F. Zhang, H. Huang, Appl. Phys. Lett. 92, 13127–13130 (2008)
W. Wang, Q. Li, C. Chang, Synth. Met. 161, 44–50 (2011)
G. Liu, L. Wang, G. Chen, J. Alloys Compd. 514, 183–188 (2012)
P. Xu, X.J. Han, C. Wang, Synth. Met. 159, 430–434 (2009)
H. Liu, H. Cheng, H. Tian, Mater. Sci. Eng. B 179, 17–24 (2014)
S.H. Hosseini, A. Moghimi, M. Moloudi, Mater. Sci. Semicond. Process. 24, 272–277 (2014)
J. Zhan, Y. Yao, C. Zhang, J. Alloy Compd 585, 240–244 (2014)
R. Moučka, M. Mravčáková, J. Vilčáková, Mater. Des. 32, 2006–2011 (2011)
T.H. Ting, R.P. Yu, Y.N. Jau, Mater. Chem. Phys. 126, 364–368 (2011)
S.H. Hosseini, S.H. Mohseni, A. Asadnia, J. Alloys Compd. 509, 4682–4687 (2011)
J. Jiang, C. Chen, L.H. Ai, Mater. Lett. 63, 560–562 (2009)
N.G. Sahoo, C.J. Yong, H.H. So, Synth. Met 157, 374–379 (2007)
A. Pud, N. Ogurtsov, A. Korzhenko et al., Prog. Polym. Sci. 28, 1701–1753 (2003)
M.G. Han, Y.J. Lee, S.W. Byun et al., Synth. Met. 24, 337–343 (2001)
H.M. Xiao, X.M. Liu, S.Y. Fu, Compos. Sci. Technol. 66, 2003–2008 (2006)
A. Verma, A.K. Saxena, D.C. Dube, J. Magn. Magn. Mater. 263, 228–34 (2003)
S. Khasim, S.C. Raghavendra, M. Revanasiddappa, Bull. Mater. Sci. 34, 1557–1561 (2011)
H.M. Kuo, T.F. Hsui, Y.S. Tuo et al., J. Mater. Sci. 47, 2264–2270 (2012)
Y. Zhang, X. Zhuang, Y. Su, J. Mater. Chem. A 2, 7742–7746 (2014)
C.C. Yang, Y.J. Gung, W.C. Hung, Compos. Sci. Technol. 70, 466–471 (2010)
H.B. Yang, Y. Lin, F. Wang et al., J. Mater. Technol. 23, 138–141 (2008)
Y.S. Yang, M.X. Wan, J. Mater. Chem. 12, 897–901 (2002)
J.J. Xu, K. Wang, S.Z. Zu et al., ACS Nano 4, 5019–5026 (2010)
D. Poussin, H. Morgan, J.S. Foot, Polym. Int. 52, 433–438 (2003)
K.K. Pandey, J. Appl. Polym. Sci. 71, 1969–1975 (2015)
M.K. Ray, K. Bagani, S. Banerjee, J. Alloys Compd. 600, 55–64 (2014)
C. Colbeau-Justin, M. Kunst, D. Huguenin, J. Mater. Sci. 38, 2429–2437 (2003)
W. Zhou, X. Peng, L.I. Yang et al., J. Inorg. Mater. 28, 479–484 (2013)
D.Z. Chen, G.S. Wang, S. He, J. Mater. Chem. A 1, 5996–6003 (2013)
X. Chen, F. Meng, Z.J. Zhou, Nanoscale 6, 8140–8148 (2014)
M.M. Du, Z.J. Yao, J.T. Zhou, P.J. Liu, T.T. Yao, R. Yao, Synth. Met. 223, 49–57 (2017)
J.T Feng, Y.C. Wang, Y.H. Hou, J.B. Li, L.C. Li, Ceram. Int. 42, 17814–17821 (2016)
C.J. Ge, J.P. Zou, M.Q. Yan, H. Bi, Mater. Lett. 137, 41–44 (2014)
H.B. Yang, T. Ye, Y. Lin, M. Liu, Appl. Surf. Sci. 357, 1289–1293 (2015)
Acknowledgements
This work is supported by the National Natural Science Foundation of China (Grant No. 51572159), the Chinese Postdoctoral Science Foundation (Grant No. 2016M590916), the Scientific Research Foundation for the Returned Overseas Chinese Scholars, State Education Ministry, the Science and Technology Foundation of Weiyang District of Xi’an City (Grant No. 201605), the Industrialization Foundation of Education Department of Shaanxi Provincial Government (Grant No. 16JF002).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Yang, H., Dai, J., Lin, Y. et al. Synthesis and microwave absorption property of ternary composites: polyaniline/CoFe2O4/Ba3Co2Fe24O41 . J Mater Sci: Mater Electron 28, 10853–10861 (2017). https://doi.org/10.1007/s10854-017-6863-0
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10854-017-6863-0