Synthesis, characterization, magnetic and catalytic properties of graphene oxide/Fe3O4

  • Babak JalehEmail author
  • Azam Khalilipour
  • Safdar Habibi
  • Mohammad Niyaifar
  • Mahmoud Nasrollahzadeh


In this paper, graphene oxide/Fe3O4 (GO/Fe3O4) nanocomposites were prepared by using co-precipitation method at low temperature. The formation of the GO/Fe3O4 nanocomposites was confirmed by X-ray diffraction (XRD), Energy dispersive X-ray analysis and Fourier transform infrared analysis. The morphology and particle size of the GO/Fe3O4 nanocomposites were investigated by Transmission electron microscopy (TEM) and Scanning electron microscopy. The grain size of the Fe3O4 nanoparticles was estimated about 10–20 nm from XRD. Also, the particle size of the Fe3O4 nanoparticles (according to TEM image) was found to be smaller than 20 nm. Finally magnetite property of the GO/Fe3O4 nanocomposites was studied by vibrating sample magnetometer (VSM) and Mössbauer spectroscopy. The VSM and Mössbauer results were confirmed each other and shown the magnetite property decrease by decreasing the Fe3O4 amount of samples. Also, catalytic activity of the GO/Fe3O4 nanocomposites has been tested for the reduction of methylene blue at room temperature. It was found that the GO/Fe3O4 nanocomposites are highly active and recyclable catalysts and due to the magnetic separability can be recovered and reused several times without marked loss of activity.


Fe3O4 Graphene Oxide Methylene Blue Isomer Shift Fe3O4 Nanoparticles 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.



We gratefully acknowledge the Iranian Nano Council and the University of Bu Ali Sina and Qom for the support of this work.


  1. 1.
    V. Štengl, S. Bakardjieva, T.M. Grygar, J. Bludská, M. Kormunda, TiO2-graphene oxide nanocomposite as advanced photocatalytic materials. Chem. Cent. J. 7, 41–53 (2013)CrossRefGoogle Scholar
  2. 2.
    G. Liu, W. Jiang, D. Sun, Y. Wang, F. Li, One-pot synthesis of urchinlike Ni nanoparticles/RGO composites with extraordinary electromagnetic absorption properties. Appl. Surf. Sci. 314, 523–529 (2014)CrossRefGoogle Scholar
  3. 3.
    Q.H. Wua, B. Qu, J. Tang, C. Wang, D.Y. Wang, J. Li, G. Ren, An alumina-coated Fe3O4-reduced graphene oxide composite electrode as a stable anode for lithium-ion battery. Electrochim. Acta 156, 147–153 (2015)CrossRefGoogle Scholar
  4. 4.
    H. Wang, X. Yuan, Y. Wu, X., H. Chen, L., Leng, Wang, H. Li, G. Zeng, Facile synthesis of polypyrrole decorated reduced graphene oxide-Fe3O4 magnetic composites and its application for the Cr (VI) removal. Chem. Eng. J. 262, 597–606 (2015)CrossRefGoogle Scholar
  5. 5.
    M. Nasrollahzadeh, M. Atarod, B. Jaleh, M. Gandomi, In situ green synthesis of Ag nanoparticles on graphene oxide/TiO2 nanocomposite and their catalytic activity for the reduction of 4-nitrophenol, congo red and methylene blue. Ceram. Int. 42, 8587–8596 (2016)CrossRefGoogle Scholar
  6. 6.
    M. Vinothkannana, C. Karthikeyan, G.G. Kumar, A.R. Kim, D.J. Yoo, One-pot green synthesis of reduced graphene oxide (RGO)/Fe3O4 nanocomposites and its catalytic activity toward methylene blue dye degradation. Spectrochim. Acta A 136, 256–264 (2015)CrossRefGoogle Scholar
  7. 7.
    P. Fakhri, B. Jaleh, M. Nasrollahzadeh, Synthesis and characterization of copper nanoparticles supported on reduced graphene oxide as a highly active and recyclable catalyst for the synthesis of formamides and primary amines. J. Mol. Catal. A Chem. 383–384, 17–22 (2014)CrossRefGoogle Scholar
  8. 8.
    J. Wang, B. Tang, T. Tsuzuki, Q. Liu, X. Hou, L. Sun, Synthesis, characterization and adsorption properties of superparamagnetic polystyrene/Fe3O4/graphene oxide. Chem. Eng. J. 204–206, 258–263 (2012)CrossRefGoogle Scholar
  9. 9.
    X. Liu, H. Zhu, X. Yang, An amperometric hydrogen peroxide chemical sensor based on graphene-Fe3O4 multilayer films modified ITO electrode. Talanta 87, 243–248 (2011)CrossRefGoogle Scholar
  10. 10.
    B. Jaleh, A. Jabbari, Evaluation of reduced graphene oxide/ZnO effect on properties of PVDF nanocomposite films. Appl. Surf. Sci. 320, 339–347 (2014)CrossRefGoogle Scholar
  11. 11.
    S. Naghdi, K.Y. Rhee, B. Jaleh, S.J. Park, Altering the structure and properties of iron oxide nanoparticles and graphene oxide/iron oxide composites by urea”. Appl. Surf. Sci. 364, 686–693 (2016)CrossRefGoogle Scholar
  12. 12.
    M.P. Deosarkara, S.M. Pawar, B.A. Bhanvase, In situ sonochemical synthesis of Fe3O4-graphene nanocomposite for lithium rechargeable batteries. Chem. Eng. Process. 83, 49–55 (2014)CrossRefGoogle Scholar
  13. 13.
    Ö. Metin, Ş. Aydoğan, K. Meral, A new route for the synthesis of graphene oxide Fe3O4 (GO-Fe3O4) nanocomposites and their Schottky diode applications. J. Alloy. Compd. 585, 681–688 (2014)CrossRefGoogle Scholar
  14. 14.
    H. Chengen, L. Zixiu, L. Yun, H. Leping, Y. Yingkui, Graphene-supported silver nanoparticles with high activities toward chemical catalytic reduction of Methylene Blue and electrocatalytic oxidation of hydrazine. Int. J. Electrochem. Sci. 11, 9566–9574 (2016)Google Scholar
  15. 15.
    D. Ghanbari, M. Salavati-Niasari, M. Ghasemi-Kooch, A sonochemical method for synthesis of Fe3O4 nanoparticles and thermal stable PVA-based magnetic nanocomposite. J. Ind. Eng. Chem. 20, 3970–3974 (2014)CrossRefGoogle Scholar
  16. 16.
    P. Hu, S. Zhang, H. Wang, D. Pan, J. Tian, Z. Tang, A.A. Volinsky, Heat treatment effects on Fe3O4 nanoparticles structure and magnetic properties prepared by carbothermal reduction. J. Alloy. Compd. 509, 2316–2319 (2011)CrossRefGoogle Scholar
  17. 17.
    L. Blaney, Magnetite (Fe3O4): properties, synthesis, and applications. Lehigh Rev. 15, 33–81 (2007)Google Scholar
  18. 18.
    T. Perez-Gonzalez, A. Rodriguez-Navarro, C. Jimenez-Lopez, Inorganic magnetite precipitation at 25 °C: a low-cost inorganic coprecipitation method. J. Supercond. Nov. Magn. 24, 549–557 (2011)CrossRefGoogle Scholar
  19. 19.
    M. Günay, A. Baykal, H. Sözeri, Structural and magnetic properties of triethylene glycol stabilized monodisperse Fe3O4 nanoparticles. J. Supercond. Nov. Magn. 25, 2415–2420 (2012)CrossRefGoogle Scholar
  20. 20.
    A.A. Shal, A. Jafari, Study of structural and magnetic properties of superparamagnetic Fe3O4-ZnO core–shell nanoparticles. J. Supercond. Nov. Magn. 27, 1531–1538 (2014)CrossRefGoogle Scholar
  21. 21.
    K. Chinnaraj, A. Manikandan, P. Ramu, S.A. Antony, P. Neeraja, Comparative studies of microwave and sol–gel assisted combustion methods of fe3o4 nanostructures: structural, morphological, optical, magnetic, and catalytic properties. J. Supercond. Nov. Magn. 28, 179–190 (2015)CrossRefGoogle Scholar
  22. 22.
    P.H. Linh, D.H. Manh, P.T. Phong, L.V. Hong, N.X. Phuc, Magnetic properties of Fe3O4 nanoparticles synthesized by coprecipitation method. J. Supercond. Nov. Magn. 27, 2111–2115 (2014)CrossRefGoogle Scholar
  23. 23.
    N.S. Sidorov, A.V. Palnichenko, I.I. Zver’kova, Superconductivity at 125 K in the metallic-oxidized iron interface. J. Supercond. Nov. Magn. 24, 1433–1435 (2011)CrossRefGoogle Scholar
  24. 24.
    M. Nasrollahzadeh, B. Jaleh, A. Jabbari, Synthesis, characterization and catalytic activity of graphene oxide/ZnO nanocomposites. RSC Adv. 4, 36713–36720 (2014)CrossRefGoogle Scholar
  25. 25.
    X. Liu, L. Pan, T. Lv, Z. Sun, C.Q. Sun, Visible light photocatalytic degradation of dyes by bismuth oxide-reduced graphene oxide composites prepared via microwave-assisted method. J. Colloid Interface Sci. 408, 145–150 (2013)CrossRefGoogle Scholar
  26. 26.
    L. Shahriary, A. Athawale, Graphene oxide synthesized by using modified Hummers approach. Int. J. Renew. Energy Environ. Eng. 2, 2348–0157 (2014)Google Scholar
  27. 27.
    J.C. Qu, C.L. Ren, Y.L. Dong, Y.P. Chang, M.G. Zhou, X. Chen, Facile synthesis of multifunctional graphene oxide/AgNPs-Fe3O4 nanocomposite: a highly integrated catalysts. Chem. Eng. J. 211–212, 412–420 (2012)CrossRefGoogle Scholar
  28. 28.
    S. Jafari, S.F. Shayesteh, M. Salouti, K. Boustani, Effect of annealing temperature on magnetic phase transition in Fe3O4 nanoparticles. J. Magn. Magn. Mater. 379, 305–312 (2015)CrossRefGoogle Scholar
  29. 29.
    S. Morup, H. Topsoe, J. Lipka, Modified theory for Mössbauer spectra of superparamagnetic particles: application to Fe3O4. J. Phys. Colloq. 37, 287–290 (1976)CrossRefGoogle Scholar
  30. 30.
    V.I. Goldanskii, R.H. Herber, Chemical Applications of Mössbauer Spectroscopy (Academic Press, New York and London, 1968)Google Scholar
  31. 31.
    U. Gonser, Mössbauer spectroscopy І and II: the exotic side of the method. Topics Appl. Phys. 5 and Topics Curr. Phys. 25, (Springer, Berlin, Heidelberg 1975 and 1981)Google Scholar
  32. 32.
    J.M. Greneche, Metallic glasses: Mössbauer contribution, physical properties and applications. Hyperfine Interact. 111, 261–268 (1998)CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media New York 2016

Authors and Affiliations

  • Babak Jaleh
    • 1
    Email author
  • Azam Khalilipour
    • 1
  • Safdar Habibi
    • 1
  • Mohammad Niyaifar
    • 2
  • Mahmoud Nasrollahzadeh
    • 3
    • 4
  1. 1.Department of Physics, Faculty of ScienceBu-Ali Sina UniversityHamedanIran
  2. 2.Department of Physics, Ahvaz BranchIslamic Azad UniversityAhvazIran
  3. 3.Department of Chemistry, Faculty of ScienceUniversity of QomQomIran
  4. 4.Center of Environmental ResearchesUniversity of QomQomIran

Personalised recommendations