Abstract
We have synthesized Eu2+ doped CaS red emitting and SrS orange emitting phosphors by carbo-thermal reduction method. The phase purity and surface morphology of prepared material was investigated by using X-ray diffraction (XRD) and Scanning Electron Microscope. The photoluminescence property was studied under blue excitation. The XRD pattern of prepared phosphor well matches with ICDD (International center for diffraction data) file. Surface morphology of prepared phosphors was found to be in submicron range. Photoluminescence emission spectra of Eu2+ doped CaS and SrS exhibits broad emissions centered at 630 and 602 nm respectively corresponding to 4F6 5D1 → 4F7 transition. It was also observed that the samples showed an emission that persisted for a few seconds after the excitation beam is turned off. CIE coordinates are (0.6263, 0.3328) and (0.5772, 0.4166) respectively under the excitation at 469 nm. The prominent excitation peaks located at 469 nm (blue light i.e. 440–480 nm), which indicates that the phosphors are promising material for a color converter using blue LED as the primary light (pumping) source in phosphor converted white LED (pc wLED) for solid state lighting.
Similar content being viewed by others
References
K. Sakuma, N. Hirosaki, R.J. Xie, J. Lumin. 126, 843 (2007)
X.F. Hu, S.R. Yan, L. Ma, G.J. Wan, J.G. Hu, Powder Technol. 188, 242 (2009)
S. Nakamura, G. Fasol, The Blue Laser Diode (Springer, Berlin Heidelberg, 1997). doi:10.1007/978-3-662-03462-0
R.J. Xie, N. Hirosaki, N. Kimura, K. Sakuma, M. Mitomo, Appl. Phys. Lett. 90, 191101 (2007)
J. Ruan, R.J. Xie, N. Hirosaki, T. Takeda, J. Am. Ceram. Soc. 94, 536 (2011)
R.J. Xie, N. Hirosaki, M. Mitomo, K. Takahashi, K. Sakuma, Appl. Phys. Lett. 88, 101104 (2006)
R.J. Xie, N. Hirosaki, M. Mitomo, K. Sakuma, N. Kimura, Appl. Phys. Lett. 89, 241103 (2006)
A. Bessière, S. Jacquart, K. Priolkar, A. Lecointre, B. Viana, D. Gourier, Opt. Express 19, 10131 (2011)
Y. Huang, Y. Nakai, T. Tsuboi, H.J. Seo, Opt. Express 19, 6303 (2011)
C.J. Duan, A.C.A. Delsing, H.T. Hintzen, Chem. Mater. 21, 1010 (2009)
M. Ando, Y.A. Ono, J. Appl. Phys. 68, 3578 (1990)
V. Kumar, S.S. Pitale, V. Mishra, I.M. Nagpure, M.M. Biggs, O.M. Ntwaeaborwa, H.C. Swart, J. Alloys Compd. 492, L8 (2010)
T. Liu, B.M. Cheng, S.F. Hu, R.-S. Liu, Chem. Mater. 23, 3698 (2011)
C. Hecht, F. Stadler, P.J. Schmidt, J. Schmedt auf der Günne, V. Baumann, W. Schnick, Chem. Mater. 21, 1595 (2009)
N.B. Ingale, S.K. Omanwar, P.L. Muthal, S.M. Dhopte, V.K. Kondawar, T.K. Gundurao, S.V. Moharil, Radiat. Meas. 43, 1191 (2008)
C.B. Palan, N.S. Bajaj, S.K. Omanwar, St. Petersb. Polytech. Univ. J.: Phys. Math. 1, 410 (2015)
A. Sahai, Y. Kumar, V. Agarwal, S. Olive-Méndez, N. Goswami, J. Appl. Phys. 116, 164315 (2014)
B.K. Grandhea, V.R. Bandia, K. Janga, S.S. Kima, D.S. Shinb, Y.I. Leeb, J.M. Limb, T. Songc, J. Alloys Compd. 509, 7937 (2011)
B. Yan, C. Wang, Solid State Sci. 10, 82 (2008)
C.H. Huang, P.J. Wu, J.F. Lee, T.M. Chen, J. Mater. Chem. 21, 10489 (2011)
C. Qin, Y. Huang, L. Shi, G. Chen, X. Qiao, H.J. Seo, J. Phys. D Appl. Phys. 42, 185105 (2009)
J. Gu, B. Yue, G. Yin, X. Liao, Z. Huang, Y. Yao, Y. Kang, Front. Mater. Sci. China 4, 90 (2010)
P. Dorenbos, J. Electrochem. Soc. 152, H107 (2005)
Acknowledgments
Author, DNG, is thankful to the Head of the Department of Physics, Sant Gadge Baba Amravati University, Amravati for providing all the necessary research facilities and also to the Head, Deccan Education Society’s Technical Institute, Fergusson College Campus, Pune for constant encouragement and guidance.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Game, D.N., Ingale, N.B. & Omanwar, S.K. Synthesis and photoluminescence properties of Eu2+ doped CaS and SrS phosphor for phosphor converted white light emitting diodes. J Mater Sci: Mater Electron 28, 915–922 (2017). https://doi.org/10.1007/s10854-016-5607-x
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10854-016-5607-x