Abstract
Copper-coated glass fabric was successfully fabricated via electroless plating method, and the copper layer on the surface of glass fabric was continuous and compact. The chemical composition of the copper coatings was investigated by X-ray diffraction, and the microstructures were invested by scanning electron microscopy. It was found that the quality of the copper layer was closely related to the dosage of NaOH and reducing reagent, respectively. These composites possessed excellent conductivity with the volume resistivity up to 2.57 × 10−3 Ω cm, and can be used as shielding materials.
Similar content being viewed by others
References
A. Rahaman, K.K. Kar, Fuller. Nanotub. Carbon Nanostruct. 19, 373–397 (2011)
C.J. Xu, R.H. Zhou, H.Y. Chen et al., J. Mater. Sci.: Mater. Electron. 25, 4638–4642 (2014)
G.L. Liu, C.J. Xu, H.Y. Chen, Micro. Nano Lett. 10(6), 315–317 (2015)
C.J. Xu, G.L. Liu, H.Y. Chen et al., J. Mater. Sci.: Mater. Electron. 25, 2611–2617 (2014)
H.Y. Chen, G.L. Liu, C.J. Xu et al., Mater. Lett. 173, 211–213 (2016)
Y. Tai, H.Y. Chen, C.J. Xu et al., Mater. Lett. 171, 158–161 (2016)
Y. Tai, C.J. Xu, H.Y. Chen, Mater. Lett. 180, 144–147 (2016)
M. Gopiraman, A.W. Jatoi, S. Hiromichi et al., Carbohydr. Polym. 149, 51–59 (2016)
P.K. Duy, P.T.H. Yen, S. Chun et al., Sens. Actuators B Chem. 225, 377–383 (2016)
H. Zhao, Y.X. Lu, Appl. Surf. Sci. 362, 154–162 (2016)
R.H. Guo, S.Q. Jiang, C.W.M. Yuen et al., J. Mater. Sci.: Mater. Electron. 20, 33–38 (2009)
E.G. Han, E.A. Kim, K.W. Oh, Synth. Met. 123, 469–476 (2001)
Y.X. Lu, Q. Liang, W.L. Li, Mater. Chem. Phys. 140, 553–558 (2013)
C. Liu, X. Huang, J.F. Zhou et al., J. Mater. Chem. C 4, 914–920 (2016)
E. Kim, N.S. Arul, L. Yang et al., RSC Adv. 5, 76729–76732 (2015)
Acknowledgments
This work was supported by Research Fund for the Doctoral Program of Higher Education of China (20121420120006), Shanxi Province Science Foundation for Youths (2014021016-1), Scientific and Technological Innovation Programs of Higher Education Institutions in Shanxi, and Scientific Research Foundation for the Returned Overseas Chinese Scholars, Ministry of Education of China.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Chen, H., Tai, Y. & Xu, C. Fabrication of copper-coated glass fabric composites through electroless plating process. J Mater Sci: Mater Electron 28, 798–802 (2017). https://doi.org/10.1007/s10854-016-5592-0
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10854-016-5592-0