Abstract
In this work, the NiFe2O4–reduced graphene oxide (NiFe2O4–rGO) was achieved via a one-step hydrothermal method. The microstructure, permittivity and permeability and electromagnetic attenuation properties of NiFe2O4–rGO are investigated. The minimum reflection loss reaches −46.8 dB at d = 4.8 mm. The introduction of NiFe2O4 nanocrystals enhances electromagnetic attenuation due to the synergetic effect of dielectric and magnetic loss as well as the enhanced exchange resonance. It is believed that the deposition of magnetic nanocrystals is a way to generate light-weight and high-efficient microwave absorbers. The NiFe2O4–rGO is a promising candidate for electromagnetic attenuation in various fields.
Similar content being viewed by others
References
M.S. Cao, X.X. Wang, W.Q. Cao, J. Yuan, J Mater Chem C 3, 6589–6599 (2015)
X. Liu, H. Guo, Q. Xie, Q. Luo, L.S. Wang, D.L. Peng, J. Alloy. Compd. 649, 537–543 (2015)
A. Saboor, A.N. Khan, H.M. Cheema, K. Yaqoob, A. Shafqat, J. Mater. Sci.: Mater. Electron. (2016). doi:10.1007/s10854-016-5021-4
B.J. Madhu, M. Gurusiddesh, T. Kiran, B. Shruthi, H.S. Jayanna, J. Mater. Sci.: Mater. Electron. (2016). doi:10.1007/s10854-016-4764-2
D. Sarkar, A. Bhattacharya, P. Nandy, S. Das, Mater. Lett. 120, 259–262 (2014)
P. Smitha, I. Singh, M. Najim, R. Panwar, D. Singh, V. Agarwala, G.D. Varma, J. Mater. Sci.: Mater. Electron. (2016). doi:10.1007/s10854-016-4760-6
Z.T. Li, M.Q. Ye, A.J. Han, H. Du, J. Mater. Sci.: Mater. Electron. 27, 1031–1043 (2016)
K.K. Ji, Y. Li, M.S. Cao, J. Mater. Sci.: Mater. Electron. 27, 5128–5135 (2016)
Y.P. Duan, Z. Liu, H. Jing, Y.H. Zhang, S.Q. Li, J. Mater. Chem. 22, 18291–18299 (2012)
Y.P. Duan, Z. Liu, Y.H. Zhang, M. Wen, J. Mater. Chem. C 1, 1990–1994 (2013)
X.L. Shi, M.S. Cao, J. Yuan, X.Y. Fang, Appl. Phys. Lett. 95, 163108 (2009)
Y. Li, H.J. Yang, W.G. Yang, Z.L. Hou, J.B. Li, H.B. Jin, J. Yuan, M.S. Cao, Mater. Lett. 111, 130–133 (2013)
X. Liu, Z. Zhang, Y. Wu, Compos. B Eng. 42, 326–329 (2011)
J. Jiang, H. Wang, H. Guo, T. Yang, W.S. Tang, D. Li, S. Ma, D. Geng, W. Liu, Z. Zhang, Nanoscale Res. Lett. 7, 238 (2012)
Z.Q. Qiao, S.K. Pan, J.L. Xiong, L.C. Cheng, Q.R. Yao, J. Mater. Sci.: Mater. Electron. 27, 7487–7493 (2016)
Y.P. Duan, L. Wang, Z. Liu, S.C. Gu, Plast. Rubber Compos. 42, 82–87 (2013)
T.K. Gupta, J. Mater. Chem. A 2, 4256–4263 (2013)
X. Li, S. Yang, J. Sun, P. He, X. Pu, G. Ding, Synth. Met. 194, 52–58 (2014)
T. Hu, J. Wang, J.L. Wang, Mater. Lett. 158, 163–166 (2015)
D. Bo, R. Yong, G. Wang, Y. Ma, Z. Pei, S. Li, Nanoscale Res. Lett. 8, 1–6 (2013)
L. Liu, X.M. Bian, Z.L. Hou, J.Y. Zhu, X.D. Liu, C.Y. Wang, J. Mater. Sci.: Mater. Electron. (2016). doi:10.1007/s10854-016-4819-4
Y.H. Chen, Z.H. Huang, M.M. Lu, W.Q. Cao, J. Yuan, D.Q. Zhang, M.S. Cao, J. Mater. Chem. A 3, 12621–12625 (2015)
Y.M. Huang, Q.Qi, H. Pan, X.F. Lei, X.B. Liu, J. Mater. Sci.: Mater. Electron. (2016). doi:10.1007/s10854-016-5011-6
Y.P. Wang, Z. Peng, W. Jiang, J. Mater. Sci.: Mater. Electron. 27, 6010–6019 (2016)
Z. Peng, W. Jiang, Y.P. Wang, S.T. Zhong, J. Mater. Sci.: Mater. Electron. 27, 1304–1313 (2016)
X. Li, S. Yang, J. Sun, P. He, X. Pu, G. Ding, Synth. Met. 194, 52–58 (2014)
P.B. Liu, Y. Huang, L. Wang, M. Zong, W. Zhang, Mater. Lett. 107, 166–169 (2013)
X.Q. Guo, Z.Y. Bai, B. Zhao, R. Zhang, J.B. Chen, J. Mater. Sci.: Mater. Electron. (2016). doi:10.1007/s10854-016-4853-2
M. Zong, Y. Huang, H.W. Wu, Y. Zhao, Q.F. Wang, X. Sun, Mater. Lett. 114, 52–55 (2014)
Z.Y. Liu, G.L. Xu, M. Zhang, K. Xiong, P.Y. Meng, J. Mater. Sci.: Mater. Electron. (2016). doi:10.1007/s10854-016-4966-7
P.B. Liu, Y. Huang, X. Sun, Mater. Lett. 112, 117–120 (2013)
W.S. Hummers, R.E. Offeman, J. Am. Chem. Soc. 80, 1339 (1958)
R. Arias, P. Chu, D.L. Mills, Phys. Rev. B 71, 224410 (2005)
M.M. Lu, M.S. Cao, Y.H. Chen, W.Q. Cao, J. Liu, H.L. Shi, D.Q. Zhang, W.Z. Wang, J. Yuan, ACS Appl. Mater. Interfaces 7, 19408–19415 (2015)
M.S. Cao, R.R. Qin, C.J. Qiu, J. Zhu, Mater. Des. 24, 391–396 (2003)
Acknowledgment
This work is supported by the National Nature Science Foundation of China under Grant Nos. 51132002 and 51372282.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Zhao, X., Zhang, YL., Wang, XX. et al. Enhanced microwave absorption properties of NiFe2O4 nanocrystal deposited reduced graphene oxides. J Mater Sci: Mater Electron 27, 11518–11523 (2016). https://doi.org/10.1007/s10854-016-5280-0
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10854-016-5280-0