Abstract
Barium strontium titanate (BST) and iron doped barium strontium titanate (BSTF) ceramics with general formula (Ba0.5Sr0.5Ti1−yFeyO3) and different iron (Fe) contents were prepared by slow rate injection sol–gel technique. The phase analysis, morphology and dielectric properties of BSTFs were investigated. The phase analysis was carried out using XRD which revealed the crystallization of BSTF in perovskite structure with single phase. The Fe doped BST peaks shifted toward higher angles and the calculated crystallite size was 19 nm on average. The BSTF morphology was studied using TEM which showed that the particle size was affected by Fe content. The average particle size was found to be 37 nm for (Ba0.5Sr0.5Ti1−yFeyO3) with Fe concentration of (y = 0.01, 0.05 and 0.1) calcined at (600, 800 and 1000 °C). The dielectric measurements were carried out using impedance analyzer at room temperature as a function of frequency in the range of 10 Hz to 1 MHz. The dielectric constant and dielectric loss of the 1 mol% Fe-doped Ba0.5Sr0.5TiO3 at 1 kHz were 1453.69 and 0.0063, respectively. The BSTF ceramics with high dielectric constant and low dielectric loss were obtained for the application DRAM cell capacitor.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
S.M. Rhim, S. Hong, H. Bak, O.K. Kim, J. Am. Ceram. Soc. 83(5), 1145–1148 (2004)
H.V. Alexandru, C. Berbecaru, A. Ioachim, L. Nedelcu, A. Dutu, Appl. Surf. Sci. 253(1), 354–357 (2006)
A. Ioachim, M.I. Toacsan, M.G. Banciu, L. Nedelcu, A. Dutu, S. Antohe, C. Berbecaru, L. Georgescu, G. Stoica, H.V. Alexandru, Thin Solid Films 515(16), 6289–6293 (2007)
A. Ianculescu, D. Berger, M. Viviani, C.E. Ciomaga, L. Mitoseriu, E. Vasile, N. Drăgan, D. Crişan, J. Eur. Ceram. Soc. 27(13–15), 3655–3658 (2007)
J.D. Baniecki, R.B. Laibowitz, T.M. Shaw, C. Parks, J. Lian, H. Xu, Q.Y. Ma, J. Appl. Phys. 89, 2873–2885 (2001)
C.L. Fu, C.R. Yang, H.W. Chen, Y.X. Wang, L.Y. Hu, L.Y. Mater, Sci. Eng. B 119(2), 185–188 (2005)
A.I. Kingon, J.P. Maria, S.K. Streiffer, Nature 406(6799), 1032–1038 (2000)
K.A. Razak, A. Asadov, J. Yoo, E. Haemmerle, W. Gao, J. Alloys Compd. 449(1), 19–23 (2008)
S. Suasmoro, S. Pratapa, D. Hartanto, D. Setyoko, U.M. Dani, J. Eur. Ceram. Soc. 20, 309–314 (2000)
L. Zhou, P.M. Vilarinho, J.L. Baptista, J. Eur. Ceram. Soc. 19, 2015–2020 (1999)
A. Ries, A.Z. Simoes, M. Cilense, M.A. Zaghete, J.A. Varela, Mater. Charact. 50(2), 217–221 (2003)
P. Vitanov, A. Harizanova, T. AIvanova, D. Velkov, Vacuum 69, 371–377 (2003)
L. Sharmistha, A. Mansingh, Thin Solid Films 516, 1656–1662 (2008)
K.T. Kim, C.I. Kim, Microelectron. Eng. 66, 835–841 (2003)
C. Shen, Q. Liu, Q.F. Liu, Mater. Sci. Eng. B 111, 31–35 (2004)
Y.L. Li, Y.F. Qu, Mater. Res. Bull. 44(1), 82–85 (2009)
K. Imai, S. Takeno, K. Nakamura, Jpn. J. Appl. Phys. Part 1 44, 6060–6064 (2002)
S.G. Dhumal, S.G. Chavan, Y.D. Kolekar, P.B. Joshi, D.J. Salunkhe, J. Mater. Sci. Mater. Electron. 26, 1466–1473 (2015)
K.B. Inas, S.A.F. Ibrahim, K. Mostafa, A. Mohamed, G. Emad, A. Hesham, G.E. Fawzi, New J. Glass Ceram. 4, 19–28 (2014)
Acknowledgments
The authors wish to acknowledge the Ministry of Science, Technology and Innovation (MOSTI), Malaysia, for financially supporting the present research under eScience fund research Grant (No. 03-02-01-SF-0186).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Saeed, A., Ruthramurthy, B., Yong, W.H. et al. Structural and dielectric properties of iron doped barium strontium titanate for storage applications. J Mater Sci: Mater Electron 26, 9859–9864 (2015). https://doi.org/10.1007/s10854-015-3661-4
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10854-015-3661-4