Effect of pulsed voltage on electrochemical migration of tin in electronics

  • Published:
Journal of Materials Science: Materials in Electronics Aims and scope Submit manuscript

Abstract

The effect of pulsed voltage on electrochemical migration of tin was studied on size 0805 surface mount capacitors. The study was performed under water droplet condition using 0.0156 and 0.156 g L−1 concentrations of NaCl. The amplitude and the offset of rectangular shape pulse were fixed respectively at 10 and 5 V, while the duty cycle and the pulse width were varied in the range of ms. The results showed that varying of pulse width at fixed duty cycle has a minor effect under investigated conditions, whereas increasing duty cycle significantly reduces the time to short due to dendrite formation and increases the charge transferred between the electrodes over time. With increase of duty cycle, increases the anodic dissolution of tin, which was visualized using a tin ion indicator applied on the components prior to applying the voltage. The anodic dissolution of tin significantly influences the dendritic growth, although a tendency for more hydroxide precipitation was observed for lower duty cycles. The precipitation of tin hydroxides was identified as influencing factor for the reduction of charge transfer under pulsed voltage with low duty cycles, therefore resulting in the suppression of dendrite growth.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10

Similar content being viewed by others

References

  1. J.J. Steppan, J.A. Roth, L.C. Hall, A review of corrosion failure mechanisms during accelerated tests electrolytic metal migration. J. Electrochem. Soc. 134(1), 175–190 (1987)

    Article  Google Scholar 

  2. G. Harsányi, G. Inzelt, Comparing migratory resistive short formation abilities of conductor systems applied in advanced interconnection systems. Microelectron. Reliab. 41(2), 229–237 (2001)

    Article  Google Scholar 

  3. D.Q. Yu, W. Jillek, E. Schmitt, Electrochemical migration of Sn–Pb and lead free solder alloys under distilled water. J. Mater. Sci. Mater. Electron. 17(3), 219–227 (2006)

    Article  Google Scholar 

  4. B. Medgyes, B. Illés, G. Harsányi, Electrochemical migration behaviour of Cu, Sn, Ag and Sn63/Pb37. J. Mater. Sci. Mater. Electron. 23(2), 551–556 (2011)

    Article  Google Scholar 

  5. D. Minzari, M.S. Jellesen, P. Møller, R. Ambat, On the electrochemical migration mechanism of tin in electronics. Corros. Sci. 53(10), 3366–3379 (2011)

    Article  Google Scholar 

  6. D. Minzari, M.S. Jellesen, P. Møller, P. Wahlberg, R. Ambat, Electrochemical migration on electronic chip resistors in chloride environments. IEEE Trans. Device Mater. Reliab. 9(3), 392–402 (2009)

    Article  Google Scholar 

  7. V. Verdingovas, M.S. Jellesen, R. Ambat, Influence of sodium chloride and weak organic acids (flux residues) on electrochemical migration of tin on surface mount chip components. Corros. Eng. Sci. Technol. 48(6), 426–435 (2013)

    Article  Google Scholar 

  8. S.-B. Lee, M.-S. Jung, H.-Y. Lee, T. Kang, Y.-C. Joo, Effect of bias voltage on the electrochemical migration behaviors of Sn and Pb. IEEE Trans. Device Mater. Reliab. 9(3), 483–488 (2009)

    Article  Google Scholar 

  9. B. Noh, J. Yoon, W. Hong, S. Jung, Evaluation of electrochemical migration on flexible printed circuit boards with different surface finishes. J. Electron. Mater. 38(6), 902–907 (2009)

    Article  Google Scholar 

  10. B. Noh, J. Lee, S. Jung, Effect of surface finish material on printed circuit board for electrochemical migration. Microelectron. Reliab. 48, 652–656 (2008)

    Article  Google Scholar 

  11. M.-S. Jung, S.-B. Lee, H.-Y. Lee, C.-S. Ryu, Y.-G. Ko, H.-W. Park, Y.-C. Joo, Improvement of electrochemical migration resistance by Cu/Sn intermetallic compound barrier on Cu in printed circuit board. IEEE Trans. Device Mater. Reliab. 14(1), 382–389 (2014)

  12. X. Zhong, G. Zhang, Y. Qiu, Z. Chen, W. Zou, X. Guo, In situ study the dependence of electrochemical migration of tin on chloride. Electrochem. Commun. 27, 63–68 (2013)

    Article  Google Scholar 

  13. X. Zhong, G. Zhang, Y. Qiu, Z. Chen, X. Guo, Electrochemical migration of tin in thin electrolyte layer containing chloride ions. Corros. Sci. 74, 71–82 (2013)

    Article  Google Scholar 

  14. C. Xie, X. Tang, J. Chen, B. Song, J. Jin, H. Zhang, Reliability analysis and accelerated statistical model of CNC PCB for electrochemical migration. IEEE Trans. Device Mater. Reliab. 14(1), 90–98 (2014)

    Article  Google Scholar 

  15. X. He, M. Azarian, M. Pecht, Evaluation of electrochemical migration on printed circuit boards with lead-free and tin–lead solder. J. Electron. Mater. 40(9), 1921–1936 (2011)

    Article  Google Scholar 

  16. S. Zhan, M.H. Azarian, M. Pecht, Reliability of printed circuit boards processed using no-clean flux technology in temperature—humidity—bias conditions. IEEE Trans. Device Mater. Reliab. 8(2), 426–434 (2008)

    Article  Google Scholar 

  17. V. Verdingovas, M.S. Jellesen, R. Ambat, Impact of NaCl contamination and climatic conditions on the reliability of printed circuit board assemblies. IEEE Trans. Device Mater. Reliab. 14(1), 42–51 (2014)

    Article  Google Scholar 

  18. L.C. Zou, C. Hunt, Characterization of the conduction mechanisms in adsorbed electrolyte layers on electronic boards using AC impedance. J. Electrochem. Soc. 156(1), C8–C15 (2009)

    Article  Google Scholar 

  19. S.W. Chaikin, J.J. Janney, F.M. Church, C.W. McClelland, Silver migration and printed wiring. Ind. Eng. Chem. 51(3), 299–304 (1959)

    Article  Google Scholar 

  20. J. Kim, M. Park, D. Nam, H. Kwon, Electrochemical migration behavior of a fine-pitch IC substrate by alternating current. J. Nanosci. Nanotechnol. 14(11), 8258–8263 (2014)

    Article  Google Scholar 

  21. O. Short, Silver migration in electric circuits. Tele-Tech. Electron. Ind. (1956), pp. 64–65, 110–113

  22. K.J. Harry, D.T. Hallinan, D.Y. Parkinson, A.A. MacDowell, N.P. Balsara, Detection of subsurface structures underneath dendrites formed on cycled lithium metal electrodes. Nat. Mater. 13(1), 69–73 (2014)

    Article  Google Scholar 

  23. M.Z. Mayers, J.W. Kaminski, T.F. Miller, Suppression of dendrite formation via pulse charging in rechargeable lithium metal batteries. J. Phys. Chem. C 116(50), 26214–26221 (2012)

    Article  Google Scholar 

  24. A. Aryanfar, D. Brooks, B.V. Merinov, W.A. Goddard, A.J. Colussi, M.R. Hoffmann, Dynamics of lithium dendrite growth and inhibition: pulse charging experiments and Monte Carlo calculations. J. Phys. Chem. Lett. 5(10), 1721–1726 (2014)

    Article  Google Scholar 

  25. H. Yang, E.O. Fey, B.D. Trimm, N. Dimitrov, M.S. Whittingham, Effects of pulse plating on lithium electrodeposition, morphology and cycling efficiency. J. Power Sources 272, 900–908 (2014)

    Article  Google Scholar 

  26. B. Tsenter, M. Golod, Safe and efficient charging algorithm for lithium batteries. J. Power Sources 65(1–2), 284–285 (1997)

    Article  Google Scholar 

  27. X. Zhong, X. Guo, Y. Qiu, Z. Chen, G. Zhang, In situ study the electrochemical migration of tin under unipolar square wave electric field. J. Electrochem. Soc. 160(11), 495–500 (2013)

    Article  Google Scholar 

  28. R.B. Abernethy (ed.), The New Weibull Handbook, 5th edn. (North Palm Beach, FL, 2006)

  29. S. Lee, M. Jung, H. Lee, Y. Joo, Effect of initial anodic dissolution current on the electrochemical migration phenomenon of Sn solder. In Electronic Components and Technology Conference (2009), pp. 1737–1740

Download references

Acknowledgments

The research reported here was conducted as part of the CELCORR/CreCon consortium (www.celcorr.com) and the authors would like to acknowledge the funding and help received from the consortium partners. Shruti Borgaonkar (Technical University of Denmark), Daniel Minzari (IPU), and Lutz Müller (Robert Bosch GmbH) are acknowledged for their contributions to the preparation of the manuscript.

Author information

Authors and Affiliations

  1. Materials and Surface Engineering, Department of Mechanical Engineering, Technical University of Denmark, 2800, Lyngby, Denmark

    Vadimas Verdingovas, Morten Stendahl Jellesen & Rajan Ambat

Authors
  1. Vadimas Verdingovas
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Morten Stendahl Jellesen
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Rajan Ambat
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Vadimas Verdingovas.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Verdingovas, V., Jellesen, M.S. & Ambat, R. Effect of pulsed voltage on electrochemical migration of tin in electronics. J Mater Sci: Mater Electron 26, 7997–8007 (2015). https://doi.org/10.1007/s10854-015-3454-9

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s10854-015-3454-9

Keywords

Search

Navigation