Abstract
The microwave dielectric properties of Nd2MoO6 ceramics were investigated with a view to their application in mobile communication. The Nd2MoO6 ceramics were prepared by the conventional solid-state method with various sintering temperatures and sintering times. A maximum density of 6.05 g/cm3 was obtained for Nd2MoO6 ceramic, sintered at 1,350 °C for 4 h. Dielectric constants (ɛ r ) of 10.9–15.4 and quality factor (Q × f) of 7,300–19,200 GHz were obtained at sintering temperatures in the range 1,200–1,400 °C for 4 h. Dielectric constants (ɛ r ) of 14.6–15.4 and quality factor (Q × f) of 11,100–19,200 GHz were obtained for sintering times in the range 2–6 h at a sintering temperature of 1,350 °C. A dielectric constants (ɛ r ) of 15.4, a quality factor (Q × f) of 19,200 GHz, and a temperature coefficient of resonant frequency (τ f ) of −59 ppm/°C were obtained when Nd2MoO6 ceramics were sintered at 1,350 °C for 4 h.
Similar content being viewed by others
References
Y.C. Chen, M.Z. Weng, K.C. Chang, J. Mater. Sci. Mater. Electron. 25, 2475–2481 (2014)
Y.C. Chen, M.Z. Weng, K.C. Chang, J. Mater. Sci. Mater. Electron. 25, 844–851 (2014)
Y.C. Chen, C.H. Li, J. Mater. Sci. Mater. Electron. doi:10.1007/s10854-014-2167-9
F. De Smet, M. Devillers, C. Poleunis, P. Bertrand, J. Chem. Soc. Faraday Trans. 94, 941–947 (1998)
F. De Smet, P. Ruiz, B. Delmon, M. Devillers, J. Phys. Chem. B 105, 12355 (2001)
B.W. Hakki, P.D. Coleman, IEEE Trans. Microwave Theory Tech. 8, 402–410 (1960)
Y. Kobayashi, M. Katoh, IEEE Trans. Microwave Theory Tech. 33, 586–592 (1985)
American Society for Testing and Materials, C830-00: standardtest methods for apparent porosity, liquid absorption, apparent specific gravity and bulk density of refractory shapes by vacuum pressure, ASTM Annual Book of Standards, Volume 15.01: Refractions; Activated Carbon; Advanced Ceramics 141–145 (2002)
Y. Tohdo, K. Kakimoto, H. Ohsato, H. Yamada, T. Okawa, J. Eur. Ceram. Soc. 26, 2039–2043 (2006)
B.D. Silverman, Phys. Rev. 125, 1921–1930 (1962)
W.S. Kim, T.H. Hong, E.S. Kim, K.H. Yoon, Jpn. J. Appl. Phys. 37, 3567–3571 (1998)
A.J. Bosman, E.E. Havinga, Phys. Rev. 129, 1593 (1963)
Acknowledgments
The authors would like to thank the National Science Council in Taiwan, for financially supporting this research under Contract No. NSC 102-2622-E-262-009-CC3.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Chen, YC., Weng, MZ. Effect of sintering temperature and time on microwave dielectric properties of Nd2MoO6 ceramics. J Mater Sci: Mater Electron 26, 853–859 (2015). https://doi.org/10.1007/s10854-014-2474-1
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10854-014-2474-1