Abstract
Using an Indium tin oxide (ITO) ceramic target (In2O3:SnO2, 90:10 wt%), ITO thin films were deposited by conventional direct current magnetron sputtering technique onto glass substrates at room temperature. The obtained ITO films were annealed at 400 °C for different annealing times (1, 2, 5, 7, and 9 h). The effect of annealing time on their structural, optical and electrical properties was investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), atomic force microcopy (AFM), ultra violet–visible (UV–Vis) spectrometer, and temperature dependence Hall measurements. XRD data of obtained ITO films reveal that the films were polycrystalline with cubic structure and exhibit (222), (400) and (440) crystallographic planes of In2O3. AFM and Scanning Electron Microscopy SEM have been used to probe the surface roughness and the morphology of the films. The refractive index (n), thickness and porosity (%) of the films were evaluated from transmittance spectra obtained in the range 350–700 nm by UV–Vis. The optical band gap of ITO film was found to be varying from 3.35 to 3.47 eV with the annealing time. The annealing time dependence of resistivity, carrier concentration, carrier mobility, sheet resistance, and figure of merit values of the films at room temperature were discussed. The carrier concentration of the films increased from 1.21 × 1020 to 1.90 × 1020 cm−3, the Hall mobility increased from 11.38 to 18 cm2 V−1 s−1 and electrical resistivity decreased from 3.97 × 10−3 to 2.13 × 10−3 Ω cm with the increase of annealing time from 1 to 9 h. Additionally, the temperature dependence of the carrier concentration, and carrier mobility for the as-deposited and 400 °C annealed ITO films for 2 and 9 h were analysed in the temperature range of 80–350 K.
Similar content being viewed by others
References
R.B.H. Tahar, T. Ban, Y. Ohya, Y. Takahashi, J. Appl. Phys. 83, 2139 (1998)
K.L. Chopra, S. Mayor, D.K. Pandya, Thin Solid Films 102, 1 (1983)
T. Minami, Thin Solid Films 516, 5822 (2008)
H. Kim, A. Dique, J.S. Horwitz, D.B. Chrisey, Appl. Phys. Lett. 74, 3444 (1999)
H. Liu, V. Avrutin, N. Izyumskaya, U. Ozgur, H. Morkoç, Superlattices Microstruct. 48, 458 (2010)
S. Major, K.L. Chopra, Sol. Energy Mater. 17, 319 (1988)
Y. Djaoued, V.H. Phong, S. Badilescu, P.V. Ashrit, F.E. Girouard, V.V. Truong, Thin Solid Films 293, 108 (1997)
J. Vetrone, Y.W. Chung, J. Vac. Sci. Technol. A9, 3041 (1991)
F. Zhu, C.H.A. Huan, K. Zhang, A.T.S. Wee, Thin Solid Films 359, 244 (2000)
M. Quaas, C. Eggs, M.L. Ma, H. Wulff, Thin Solid Films 322, 277 (1998)
J.P. Zheng, H.S. Kwok, Appl. Phys. Lett. 63, 1 (1993)
S. Ray, R. Banerjee, N. Basu, A.K. Batabyal, A.K. Barua, J. Appl. Phys. 54, 3497 (1983)
Y. Hu, X. Diao, C. Wang, W. Hao, T. Wang, Vacuum 75, 183 (2004)
M. Gulen, G. Yildirim, S. Bal, A. Varilci, I. Belenli, M. Oz, J. Matter. Sci Mater. Electron. 24, 467 (2013)
N. Nadaud, N. Lequeux et al., J. Solid State Chem. 135, 140 (1998)
R. Jenkins, J.L. deVries, Worked Examples in X-ray Analysis, 2nd ed. edn. (Philips Technical Library, Macmillan, 1978)
J.C. Manifacier, J. Gasiot, J.P. Fillard, J. Phys. E 9, 1002 (1976)
H.N. Cui, V. Teixeria, A. Monteria, Vacuum 67, 589 (2002)
B.E. Yoldas, P.W. Partlow, Thin Solid Films 129, 1 (1985)
W.W. Mobzen, J. Vac. Sci. Technol. 12, 99 (1975)
V. Malathy, S. Sivaranjani, V.S. Vidhya, T. Balasubramanian, J. Joseph Prince, C. Sanjeeviraja, M. Jayachandran, J. Mater. Sci. Mater. Electron 21, 1299 (2010)
A.N.H. Al-Ajit, S.C. Bayliss, Thin Solid Films 305, 116 (1997)
C.H. Lee, C.S. Huang, Mater. Sci. Eng. B 22, 223 (1994)
J.I. Parkove, Optical Process in Semiconductors (Dover Publications Inc., New York, 1971)
W.F. Wu, B.S. Shiou, S.T. Hsich, Semi Conduct. Sci. Technol 9, 1242 (1994)
C.H.L. Weijtens, P.A.C. Vanloon, Thin Solid Films 196, 1 (1991)
C.G. Granqvist, A. Hultaker, Thin Solid Films 411, 1 (2002)
L. Meng, M.P. Dos Santos, Thin Solid Films 322, 56 (1998)
S. Noguchi, H. Sakata, J. Phys. D Appl. Phys. 13, 1129 (1980)
B. Radha Krishna, T.K. Subramanyam, B. Srinivasulu Naidu, S. Uthanna, Opt. Mater. 15, 217 (2000)
J. Joseph Prince, S. Ramamurthy, B. Subramanian, C. Sanjeeviraja, M. Jayachandran, J. Cryst. Growth 240, 142 (2002)
A.V. Moholkar, S.M. Pawar et al., JTTEE5 19, 531 (2010)
L.J. van der Pauw, Philips Res. Rep. 13, 1 (1958)
L.J. van der Pauw, Philips Tech. Rev. 20, 220 (1958)
G. Haacke, Ann. Rev. Mater. Sci. 7, 73 (1977)
O. Tuna, Y. Selamet, G. Aygun, L. Ozyuzer, J. Phys. D Appl. Phys. 43, 055402 (2010)
Acknowledgments
A.S. would like to thank Abant Izzet Baysal University Department of Physics where this study was carried out, for their hospitality. Authors would like to thank A. Varilci and C. Terzioglu for valuable suggestions and comments.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Senol, S.D., Senol, A., Ozturk, O. et al. Effect of annealing time on the structural, optical and electrical characteristics of DC sputtered ITO thin films. J Mater Sci: Mater Electron 25, 4992–4999 (2014). https://doi.org/10.1007/s10854-014-2262-y
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10854-014-2262-y