Structural, morphological and optical properties of undoped and Co-doped ZnO thin films prepared by sol–gel process

  • Published:
Journal of Materials Science: Materials in Electronics Aims and scope Submit manuscript

Abstract

Undoped and Co-doped ZnO thin films with different amounts of Co have been deposited onto glass substrates by sol–gel spin coating method. Zinc acetate dihydrate, cobalt acetate tetrahydrate, isopropanol and monoethanolamine (MEA) were used as a precursor, doping source, solvent and stabilizer, respectively. The molar ratio of MEA to metal ions was maintained at 1.0 and a concentration of metal ions is 0.6 mol L−1. The Co dopant level was defined by the Co/(Co + Zn) ratio it varied from 0 to 7 % mol. The structure, morphology and optical properties of the thin films thus obtained were characterized by X-ray diffraction (XRD), energy dispersive X-ray spectrometer (EDX), scanning electron microscopy (SEM), ultraviolet–visible (UV–Vis), photoluminescence (PL) and Raman. The XRD results showed that all films crystallized under hexagonal wurtzite structure and presented a preferential orientation along the c-axis with the maximum crystallite size was found is 23.5 nm for undoped film. The results of SEM indicate that the undoped ZnO thin film has smooth and uniform surface with small ZnO grains, and the doped ZnO films shows irregular fiber-like stripes and wrinkle network structure. The average transmittance of all films is about 72–97 % in the visible range and the band gap energy decreased from 3.28 to 3.02 eV with increase of Co concentration. DRX, EDX and optical transmission confirm the substitution of Co2+ for Zn2+ at the tetrahedral sites of ZnO. In addition to the vibrational modes from ZnO, the Raman spectra show prominent mode representative of ZnyCo3−yO4 secondary phase at larger values of Co concentration. PL of the films showed a UV and defect related visible emissions like violet, blue and green, and indicated that cobalt doping resulted in red shifting of UV emission and the reduction in the UV and visible emissions intensity.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8

Similar content being viewed by others

References

  1. H.S. Kang, B.D. Ahn, J.H. Kim, G.H. Kim, S.H. Lim, H.W. Chang, S.Y. Lee, Appl. Phys. Lett. 88, 202108 (2006)

    Article  Google Scholar 

  2. X.M. Zhang, W. Mai, Y. Zhang, Y. Ding, Z.L. Wang, Solid State Commun. 149, 293 (2009)

    Article  Google Scholar 

  3. T.F. Chung, L.B. Luo, Z.B. He, Y.H. Leung, I. Shafiq, Z.Q. Yao, S.T. Lee, Appl. Phys. Lett. 91, 233112 (2007)

    Article  Google Scholar 

  4. R. He, R.K. Hocking, T. Tsuzuki, Mater. Chem. Phys. 132, 1035 (2012)

    Article  Google Scholar 

  5. C. Xu, L. Cao, G. Su, W. Liu, X. Qu, Y. Yu, J. Alloys Compd. 497, 373 (2010)

    Article  Google Scholar 

  6. M.G. Nair, M. Nirmala, K. Rekha, A. Anukaliani, Mater. Lett. 65, 1797 (2011)

    Article  Google Scholar 

  7. Y. Caglar, A. Arslan, S. Ilican, E. Hur, S. Aksoy, M. Caglar, J. Alloys Compd. 574, 104 (2013)

    Article  Google Scholar 

  8. Y.J. Li, K.M. Li, C.Y. Wang, C.I. Kuo, L.J. Chen, Sens. Actuators, B 161, 734 (2012)

    Article  Google Scholar 

  9. M. Yang, T. Xie, L. Peng, Y. Zhao, D. Wang, Appl. Phys. A 89, 427 (2007)

    Article  Google Scholar 

  10. T. Ghosh, M. Dutta, S. Mridha, D. Basak, J. Electrochem. Soc. 156, H285 (2009)

    Article  Google Scholar 

  11. M.H. Mamat, M.Z. Sahdan, Z. Khusaimi, A.Z. Ahmed, S. Abdulah, M. Rusop, Opt. Mater. 32, 696 (2010)

    Article  Google Scholar 

  12. T. Dietl, H. Ohno, F. Matsukura, J. Cibert, D. Ferrand, Science 287, 1019 (2000)

    Article  Google Scholar 

  13. A. Fert, Thin Solid Films 517, 2 (2008)

    Article  Google Scholar 

  14. I. Djerdj, G. Garnweitner, D. Arčon, M. Pregelj, Z. Jagličić, M. Niederberger, J. Mater. Chem. 18, 5208 (2008)

    Article  Google Scholar 

  15. A. Bera, T. Ghosh, D. Basak, ACS Appl. Mater. Interfaces 2, 2898 (2010)

    Article  Google Scholar 

  16. M. Mahanti, T. Ghosh, D. Basak, Nanoscale 3, 4427 (2011)

    Article  Google Scholar 

  17. A. Kaushik, B. Dalela, R. Rathore, V.S. Vats, B.L. Choudhary, P.A. Alvi, S. Kumar, S. Dalela, J. Alloys Compd. 578, 328 (2013)

    Article  Google Scholar 

  18. N. Bahadur, A.K. Srivastava, S. Kumar, M. Deepa, B. Nag, Thin Solid Films 518, 5257 (2010)

    Article  Google Scholar 

  19. J. Xu, S. Shi, L. Li, X. Zhang, Y. Wang, Q. Shi, S. Li, H. Wang, J. Electron. Mater. 42, 3438 (2013)

    Article  Google Scholar 

  20. J. Hays, K.M. Reddy, N.Y. Graces, M.H. Engelhard, V. Shutthanandan, M. Luo, C. Xu, N.C. Giles, C. Wang, S. Thevuthasan, A. Punnoose, J. Phys.: Condens. Matter 19, 266203 (2007)

    Google Scholar 

  21. S. Shi, Y. Yang, J. Xu, L. Li, X. Zhang, G.H. Hu, Z.M. Dang, J. Alloys Compd. 576, 59 (2013)

    Article  Google Scholar 

  22. N. Hasuike, R. Deguchi, H. Katoh, K. Kisoda, K. Nishio, T. Isshiki, H. Harima, J. Phys.: Condens. Matter 19, 365223 (2007)

    Google Scholar 

  23. C. Sudakar, P. Kharel, G. Lawes, R. Suryanarayanan, R. Naik, V.M. Naik, J. Phys.: Condens. Matter 19, 026212 (2007)

    Google Scholar 

  24. J.S. Thakur, G.W. Auner, V.M. Naik, C. Sudakar, P. Kharel, G. Lawes, R. Suryanarayanan, R. Naik, J. Appl. Phys. 102, 093904 (2007)

    Article  Google Scholar 

  25. H.S. Alsalman, M.J. Abdullah, Superlattices Microstruct. 60, 349 (2013)

    Article  Google Scholar 

  26. Y. Belghazi, M.A. Aouaj, M. ElYadari, G. Schmerber, C.U. Bouillet, C. Leuvrey, S. Colis, M. Abd-lefdil, A. Berrada, A. Dinia, J. Microelectron. 40, 265 (2009)

    Article  Google Scholar 

  27. A. Wang, Z. Zhong, C. Lu, L. Lv, X. Wang, B. Zhang, Phys. B 406, 1049 (2011)

    Article  Google Scholar 

  28. M. Sharma, R.M. Mehra, Appl. Surf. Sci. 255, 2527 (2008)

    Article  Google Scholar 

  29. Y. Caglar, J. Alloys Compd. 560, 181 (2013)

    Article  Google Scholar 

  30. H. McMurdie, M. Morris, E. Evans, B. Paretzkin, W. Wong, L. Ettlinger, Powder Diffr. 1, 76 (1986)

    Article  Google Scholar 

  31. C.S. Barret, T.B. Massalski, Structure of Metals (Pergamon Press, Oxford, 1980)

    Google Scholar 

  32. M. Arshad, A. Azam, A. Ahmed, S. Mollah, A. Naqvi, J. Alloys Compd. 509, 8378 (2011)

    Article  Google Scholar 

  33. S. Ilican, M. Caglar, Y. Caglar, Appl. Surf. Sci. 256, 7204 (2010)

    Article  Google Scholar 

  34. M. Caglar, Y. Caglar, S. Aksoy, S. Ilican, Appl. Surf. Sci. 256, 4966 (2010)

    Article  Google Scholar 

  35. U.N. Maiti, P.K. Ghosh, S. Nandy, K.K. Chattopadhyay, Phys. B 387, 103 (2007)

    Article  Google Scholar 

  36. C.Y. Tsay, C.W. Wu, C.M. Lei, F.S. Chen, C.K. Lin, Thin Solid Films 519, 1516 (2010)

    Article  Google Scholar 

  37. C.Y. Tsay, K.S. Fan, S.H. Chen, C.H. Tsai, J. Alloys Compd. 495, 126 (2010)

    Article  Google Scholar 

  38. F. Yakuphanoglu, S. Ilican, M. Caglar, Y. Caglar, Superlattices Microstruct. 47, 732 (2010)

    Article  Google Scholar 

  39. F. Yakuphanoglu, Microelectron. Reliab. 51, 2195 (2011)

    Article  Google Scholar 

  40. N. Murugesan, A. Achuthanunni, Suranaree. J. Sci. Technol. 18, 81 (2011)

    Google Scholar 

  41. H.A. Weakliem, J. Chem. Phys. 36, 2117 (1962)

    Article  Google Scholar 

  42. K.H. Kim, K.C. Park, D.Y. Ma, J. Appl. Phys. 81, 7764 (1997)

    Article  Google Scholar 

  43. P. Li, S. Wang, J. Li, Y. Wei, J. Lumin. 132, 220 (2012)

    Article  Google Scholar 

  44. X. Xu, C. Cao, J. Alloys Compd. 501, 265 (2010)

    Article  Google Scholar 

  45. X. Wang, J. Xu, X. Yu, K. Xue, Appl. Phys. Lett. 91, 031908 (2007)

    Article  Google Scholar 

  46. M. Li, J. Xu, X. Chen, X. Zhang, Y. Wu, P. Li, X. Niu, C. Luo, L. Li, Superlattices Microstruct. 52, 824 (2012)

    Article  Google Scholar 

  47. N. Hasuike, K. Nishio, H. Katoh, A. Suzuki, T. Isshiki, K. Kisoda, H. Harima, J. Phys.: Condens. Matter 21, 064215 (2009)

    Google Scholar 

  48. F. Ahmed, S. Kumar, N. Arshi, M.S. Anwar, B.H. Koo, C.G. Lee, Microelectron. Eng. 89, 129 (2012)

    Article  Google Scholar 

  49. T.L. Phan, R. Vincent, D. Cherns, N.H. Dan, S.C. Yu, Appl. Phys. Lett. 93, 082110 (2008)

    Article  Google Scholar 

  50. Z.B. Gu, M.H. Lu, J. Wang, C.L. Du, C.S. Yuan, D. Wu, S.T. Zhang, Y.Y. Zhu, S.N. Zhu, Y.F. Chen, Thin Solid Films 515, 2361 (2006)

    Article  Google Scholar 

  51. L.J. Zhuge, X.M. Wu, Z.F. Wu, X.M. Yang, X.M. Chen, Q. Chen, Mater. Chem. Phys. 120, 480 (2010)

    Article  Google Scholar 

  52. K. Vanheusden, C.H. Seager, W.L. Warren, D.R. Tallant, J.A. Voigt, Appl. Phys. Lett. 68, 403 (1996)

    Article  Google Scholar 

  53. S.A. Studnikin, N. Golego, M. Cocivera, J. Appl. Phys. 84, 2287 (1998)

    Article  Google Scholar 

  54. P.S. Xu, Y.M. Sun, C.S. Shi, F.Q. Xu, H.B. Pan, Sci. China Ser. A44, 1174 (2001)

    Google Scholar 

  55. R. Elilarassi, G. Chandrasekaran, Mater. Sci Mater Electron. 24, 96 (2013)

    Article  Google Scholar 

  56. N.S. Sabri, A.K. Yahya, M.K. Talari, J. Lumin. 132, 1735 (2012)

    Article  Google Scholar 

  57. R. Elilarassi, G. Chandrasekaran, Mater. Sci. Semicond. Process. 14, 179 (2011)

    Article  Google Scholar 

  58. S. Mahamuni, K. Bendre, J. Appl. Phys. 85, 2861 (1999)

    Article  Google Scholar 

  59. B. Lin, Z. Fu, Y. Jia, Appl. Phys. Lett. 79, 943 (2001)

    Article  Google Scholar 

  60. C. Cheng, G. Xu, H. Zhang, Y. Luo, Y. Li, Mater. Lett. 62, 3733 (2008)

    Article  Google Scholar 

  61. R. Bhargava, P.K. Sharma, R.K. Dutta, S. Kumar, Mater. Chem. Phys. 120, 393 (2010)

    Article  Google Scholar 

  62. U.N. Maiti, P.K. Ghosh, S. Nandy, K.K. Chattopadhyay, Phys. B 387, 103 (2007)

    Article  Google Scholar 

  63. L.R. Reddy, P. Prathap, Y.P.V. Subbaiah, K.T.R. Reddy, J. Yi, Solid State Sci. 9, 718 (2007)

    Article  Google Scholar 

  64. X.T. Zhang, Y.C. Liu, J.Y. Zhang, Y.M. Lu, D.Z. Shen, X.W. Fan, X.G. Kong, J. Cryst. Growth 254, 80 (2003)

    Article  Google Scholar 

  65. G. Srinivasan, J. Kumar, J. Cryst. Growth 310, 1841 (2008)

    Article  Google Scholar 

Download references

Acknowledgments

The authors would like to thank the department of Chemistry, University of M’sila for help extended during the research in their laboratory.

Author information

Authors and Affiliations

  1. Department of Physics, M’sila University, 28000, M’sila, Algeria

    A. Mahroug & S. Hamrit

  2. Ceramics Laboratory, Department of Physics, Constantine-1 University, 25000, Constantine, Algeria

    A. Mahroug & S. Boudjadar

  3. Laser Department, Nuclear Research Center of Algiers-CRNA, 2 Building Frantz Fanon, B.P. 399, 16000, Alger, Algeria

    L. Guerbous

Authors
  1. A. Mahroug
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. S. Boudjadar
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. S. Hamrit
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. L. Guerbous
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to A. Mahroug.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Mahroug, A., Boudjadar, S., Hamrit, S. et al. Structural, morphological and optical properties of undoped and Co-doped ZnO thin films prepared by sol–gel process. J Mater Sci: Mater Electron 25, 4967–4974 (2014). https://doi.org/10.1007/s10854-014-2259-6

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s10854-014-2259-6

Keywords

Search

Navigation