Abstract
The magnetic and magnetoelectric properties of magnetoelectric (ME) composites consisting of with nickel ferrite (NiFe2O4) and barium strontium titanate (Ba0.7Sr0.3TiO3) were investigated. The composites were prepared by standard double sintering ceramic method. The X-ray diffraction analysis was carried out to confirm the phases formed during sintering and also to calculate the lattice parameters. The hysteresis measurements were done to determine saturation magnetization (Ms), remenance magnetization (Mr) and coercivity (Hc) of the samples. The magnetoelectric voltage coefficient (dE/dH)H was studied as a function of intensity of the magnetic field. The measured magnetoelectric (ME) response demonstrated strong dependence on the volume fraction of NiFe2O4 and the applied magnetic field. A large ME voltage coefficient of about 560 μVcm−1Oe−1 was observed for 15% NiFe2O4 + 85% Ba0.7Sr0.3TiO3 composite.
Similar content being viewed by others
References
J.V. Suchtelen, Philips Res. Rep. 27, 28 (1972)
G.A. Smolenski, I.E. Chupis, Sovt. Phys. Usp. 25, 475 (1982). doi:10.1070/PU1982v025n07ABEH004570
C.W. Nan, D.R. Clarke, J. Am. Ceram. Soc. 80, 1333 (1997)
K.H. Shin, M. Inoue, K.I. Arai, Smart. Mater. Struct. 9, 357 (2000)
J. Ryu, S. Priya, K. Uchino, H.E. Kim, J. Electroceram. 8, 107 (2002). doi:10.1023/A:1020599728432
D.N. Astrov, Sovt. Phys. JETP. 13, 729 (1961)
M.I. Bichurin, Ferroelectrics 282, 1 (2002)
C.W. Nan, Appl. Phys. Lett. 81, 3831 (2002)
N. Cai, C.W. Nan, J. Zhai, Y. Lin, Appl. Phys. Lett. 84, 3516 (2004)
G. Srinivasan, E.T. Rasmussen, B.J. Levin, R. Hayes, Phys. Rev. B 65, 134402 (2002). doi:10.1103/PhysRevB.65.134402
J. Van den Boomgaard, D.R. Terrel, R.A.J. Born, H.F.J.I. Giller, J. Mater. Sci. 9, 1705 (1974)
A.M.J.G. Van Run, D.R. Terrel, J.H. Schooling, J. Mater. Sci. 9, 1710 (1974). doi:10.1007/BF00540771
J. Wang, Mater. Sci. Eng. B 127, 81 (2006). doi:10.1016/j.mseb.2005.09.003
H. Abdelkefi, H. Khemakhem, G. Velu, J.C. Carru, R.V. Mubll, J. Alloy. Compos. 399, 1–6 (2005). doi:10.1016/j.jallcom.2005.03.007
S.K. Rout, J. Bera, in Ferroelectrics and Dielectrics, ed. by A.P. Tandon (Allied Publishers Pvt. Ltd., New Delhi, 2004), p. 3
J. Appel, F. Seitz, D. Thurnbull, H. Ehrenreich, Solid State Phys. 21, 193 (1968)
L. Mitoseriu, I. Pallecchi, V. Buscaglia, A. Testono, C.E. Ciomaga, A. Stancu, Magn. Magn. Mater 316, e603 (2007). doi:10.1016/j.jmmm.2007.03.036
S. Mazumder, G.S. Bhattacharyya, Ceram. Int. 30, 389 (2004)
J. Zhai, N. Cai, Z. Shi, Y. Lin, C.W. Nan, J. Phys. D: Appl. Phys. 37, 823 (2004). doi:10.1088/0022-3727/37/6/002
Acknowledgement
The work was carried out with financial assistance from UGC, New Delhi under UGC-DRS-II Program.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Patil, D.R., Chougule, B.K. Studies on magnetic and magnetoelectric properties of the NiFe2O4–Ba0.7Sr0.3TiO3 composites. J Mater Sci: Mater Electron 20, 398–402 (2009). https://doi.org/10.1007/s10854-008-9742-x
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10854-008-9742-x