Correction to: Journal of Materials Science (2023) 58:10108–10119 https://doi.org/10.1007/s10853-023-08642-w
The compound formula for the Sodium (Na) Super-Ionic Conductor (NaSICON) solid electrolyte (SE) powders was written incorrectly as Na3Zr2Si2PO4 (instead of Na3Zr2Si2PO12) three times in the article:
In the ‘Abstract’:
Sodium (Na) Super-Ionic CONductor (NaSICON) solid electrolyte (SE) powders (Na3Zr2Si2PO4) were prepared by the mixed oxide technique…
In ‘Experimental - Powder Synthesis’
NaSICON (Na3Zr2Si2PO4) solid electrolyte powders were synthesized via a solid-state synthesis route (mixed-oxide route). The starting raw materials of Na2CO3 (≥ 99%, Sigma Ald.), NH4H2PO4 (≥ 99.5%, Sigma Ald.), ZrO2 (99%, Sigma Ald.), and SiO2 (99.5%, Alfa Aesar) were weighed-in according to the stoichiometric ratio of Na3Zr2Si2PO4 and homogenized for…
All the calculations were carried out according to the correct compound composition Na3Zr2Si2PO12. However, the formula was mistakenly designated in the text as Na3Zr2Si2PO4.
X-ray diffraction analysis also shows that the powder exhibits monoclinic NaSICON (Na3Zr2Si2PO12) crystal structure.
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Sozak, M., Nazarenus, T., Exner, J. et al. Correction to: Room temperature manufacture of dense NaSICON solid electrolyte films for all-solid-state-sodium batteries. J Mater Sci (2024). https://doi.org/10.1007/s10853-024-09656-8
Published:
DOI: https://doi.org/10.1007/s10853-024-09656-8