Abstract
An Mg95.50Zn3.71Y0.79 fine-grained solidified alloy with a grain size of 16 μm was prepared by high-pressure solidification. The microstructure characteristics and hot compressive deformation behavior of the alloy solidified under high pressure were compared with the atmospheric-pressure solidified alloy by carrying out the unilateral compression tests under a strain rate in the range of 0.001–1.0 s−1 and at a deformation temperature in the range of 523–573 K. The true stress-true strain curve of the high-pressure solidified alloy shows the typical dynamic recrystallization rheological curve. EBSD results show that when the deformation was carried out at 573 K, nearly 90% dynamic recrystallization occurred in the high-pressure solidified alloy, and the newly formed grains were distortionless and had low dislocation density. The high-pressure solidified alloy showed a double-peak basal texture at a strain rate of 1.0 s−1. The two peak points showed a maximum pole density of 9.88 and 7.91, less than that in atmospheric-pressure alloy. When the deformation was carried out at the following conditions: deformation temperature = 573 K, strain rate = 0.001, and true strain = 0.9, the average Schmid factor (SF) for basal slip of the grains in the high-pressure solidified alloy was 0.419, and SF value for basal slip in 91% grains was greater than 0.3.
Similar content being viewed by others
References
Wen K, Liu K, Wang ZW, Li SB, Du WB (2015) Effect of microstructure evolution on mechanical property of extruded Mg–12Gd–2E−1Zn–0.6Zr alloys. J Magnes Alloy 3:23–28
Tahreen N, Zhang DF, Pan FS, Jiang XQ, Li DY, Chen DL (2015) Hot deformation and processing map of an as-extruded Mg–Zn–Mn–Y alloy containing I and W phases. Mater Des 87:245–255
Chang H, Wang XJ, Hu SH, Wang YQ, Nie KB, Wu K (2014) Effects of reinforced particles on dynamic recrystallization of Mg base alloys during hot extrusion. Rare Metal Mater Eng 43:1821–1825
Tong LB, Li X, Zhang DP, Cheng LR, Meng J, Zhang HJ (2014) Dynamic recrystallization and texture evolution of Mg–Y–Zn alloy during hot extrusion process. Mater Charact 92:77–83
Wu WX, Jin L, Dong J, Zhang ZY, Ding WJ (2012) Effect of initial microstructure on the dynamic recrystallization behavior of Mg–Gd–Y–Zr alloy. Mater Sci Eng, A 556:519–525
Koike J, Ohyama R (2005) Geometrical criterion for the activation of prismatic slip in AZ61 Mg alloy sheets deformed at room temperature. Acta Mater 53:1963–1972
Barnett MR, Beer AG, Atwell D, Oudin A (2004) Influence of grain size on hot working stresses and microstructures in Mg–3Al–lZn. Scripta Mater 51:19–24
Li NL, Huang GJ, Zhong XY, Liu Q (2013) Deformation mechanisms and dynamic crystallization of AZ31 Mg alloy with different initial textures during hot tension. Mater Design 50:382–391
Li NL, Huang GJ, Xin RL, Liu Q (2013) Effect of initial texture on dynamic recrystallization and deformation mechanisms in AZ31 Mg alloy extruded at 573 K. Mater Sci Eng, A 569:18–26
Lv BJ, Peng J, Zhu LL, Wang YJ, Tang AT (2014) The effect of 14H LPSO phase on dynamic recrystallization behavior and hot workability of Mg–2.0Zn–0.3Zr–5.8Y alloy. Mater Sci Eng, A 599:150–159
Lin XP, Dong Y, Xu R, Sun GF, Jiao SH (2011) Crystal morphologies and the phases in the Mg–6Zn–3Y alloy solidified under super-high pressure. Acta Metall Sin 47:1550–1554
Lin XP, Dong Y, Xu R, Zheng RG, Jiao SH (2013) Solidification microstructures and crystalline morphologies of Mg–6Zn–Y alloy solidified under GPa level super-high pressure. Rare Metal Mater Eng 42:2309–2314
Lin XP, Dong Y, Xu R, Liu SJ, Tian SS (2014) Solidification process and formation of quasi-crystal phase in Mg–6Zn–1Y alloy under pressure in the order of GPa. Rare Metal Mater Eng 43:1117–1122
Jie JC, Zou CM, Wang HW, Wei ZJ (2010) Microstructure evolution and precipitation of Al–12 Mg alloy solidified under high pressure. J Alloy Compd 506:L12–L15
Zhao SS, Peng QM, Li H (2014) Effects of super-high pressure on microstructures, nano-mechanical behaviors and corrosion properties of Mg–Al alloys. J Alloy Compd 584:56–58
Quey R, Driver JH (2011) Microtexture tracking of sub-boundary evolution during hot deformation of aluminium. Mater Charact 62:1222–1227
Liu MP, Roven HJ, Murashkin M, Valiev RZ (2009) Structural characterization by high-resolution electron microscopy of an Al–Mg alloy processed by high-pressure torsion. Mater Sci Eng, A 503:122–125
Tang LH, Liu CM, Chen ZY, Ji DW, Xiao HC (2013) Microstructures and tensile properties of Mg–Gd–Y–Zr alloy during multidirectional forging at 773 K. Mater Des 50:587–596
Mao PL, Yu JH, Liu Z, Dong Y (2013) Microstructure evolution of extruded Mg–Gd–Y magnesium alloy under dynamic compression. J Magnes Alloy 1:64–75
Wu LY, Yang Z, Xia WJ, Chen ZH, Yang L (2012) The cyclic softening and evolution of microstructures for Mg–10Gd–2.0Y–0.46Zr alloy under low cycle fatigue at 573 K. Mater Des 36:47–53
Acknowledgements
The authors would like to thank the National Natural Science Foundation of China (Nos. 51675092, 51775099) for financial support.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
The authors declare no conflict of interest.
Rights and permissions
About this article
Cite this article
Zhibin, F., Xiaoping, L., Yun, D. et al. Hot compressive deformation behavior and electron backscattering diffraction analysis of Mg95.50Zn3.71Y0.79 fine-grained alloy solidified under high pressure. J Mater Sci 53, 2880–2891 (2018). https://doi.org/10.1007/s10853-017-1698-x
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-017-1698-x