A new two-step process to prepare microcellular epoxy foams based on kinetic analysis

  • Polymers
  • Published:
Journal of Materials Science Aims and scope Submit manuscript

Abstract

The foaming behavior of a diglycidyl ether of bisphenol-A (DGEBA) epoxy resin–anhydride hardener system at varying accelerator (tertiary amine) concentration, using chemical foaming agent (CFA), was investigated. The microstructure of foams revealed a smaller cell size, higher cell density, and more homogeneous distribution of cells at higher curing rate by varying accelerator contents, whereas not the same by varying foaming temperatures. The curing of epoxy system was studied by a differential scanning calorimetry, while the decomposition process of CFA was investigated by the foaming pressure measurement. Kinetics data showed that the addition of CFA in epoxy system produced obvious influence on the curing process of epoxy mixture; meanwhile, the decomposition reaction of CFA in epoxy system showed an autocatalytic behavior, which can be well predicted by Šesták–Berggren equation. Reaction rate constants of the curing of epoxy foaming system (k t ) and the degradation of CFA (k d ) were calculated, and the competition between these two simultaneously occurring reactions was expressed by the kinetic parameter k t /k d . The high specific value of k t /k d , which can be tuned by both accelerator concentration and foaming temperature, indicated that the curing rate was much higher than degradation rate of CFA. By further accelerating the curing rate in the foaming stage, a new two-step method was introduced to fabricate microcellular epoxy foam at relatively low viscosity.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Subscribe and save

Springer+ Basic
$34.99 /Month
  • Get 10 units per month
  • Download Article/Chapter or eBook
  • 1 Unit = 1 Article or 1 Chapter
  • Cancel anytime
Subscribe now

Buy Now

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Figure 1
Figure 2
Figure 3
Figure 4
Figure 5
Figure 6
Figure 7
Figure 8
Figure 9
Figure 10
Figure 11
Figure 12

Similar content being viewed by others

Explore related subjects

Discover the latest articles and news from researchers in related subjects, suggested using machine learning.

References

  1. Karthikeyan CS, Sankaran S (2004) Elastic behavior of plain and fibre-reinforced syntactic foams under compression. Mater Lett 58(6):995–999

    Article  Google Scholar 

  2. Alonso MV, Auad ML, Nutt S (2006) Short-fiber-reinforced epoxy foams. Compos A 37(11):1952–1960

    Article  Google Scholar 

  3. Stefani PM, Tejeira BA, Sabugal J, Vazguez A (2003) Characterization of epoxy foams. J Appl Polym Sci 90(11):2992–2996

    Article  Google Scholar 

  4. Wan Hamad WNF, The PL, Yeoh CK (2013) Effect of acetic acid as catalyst on the properties of epoxy foam. Polymer-plast Technol Eng 52(8):754–760

    Article  Google Scholar 

  5. Takiguchi O, Ishikawa D, Sugimoto M (2008) Effect of rheological behavior of epoxy during precuring on foaming. J Appl Polym Sci 110(2):657–662

    Article  Google Scholar 

  6. Chen K, Tian C, Lu A et al (2014) Effect of SiO2 on rheology, morphology, thermal, and mechanical properties of high thermal stable epoxy foam. J Appl Polym Sci 131(7):2113–2124

    Article  Google Scholar 

  7. Gu R, Sain M, Konar S (2014) Development and characterization of flexible epoxy foam with reactive liquid rubber and starch. J Mater Sci 49(8):3125–3134. doi:10.1016/j.matlet.2003.08.012

    Article  Google Scholar 

  8. Thomas R, Durix S, Sinturel C et al (2007) Cure kinetics, morphology and miscibility of modified DGEBA-based epoxy resin–Effects of a liquid rubber inclusion. Polymer 48(6):1695–1710

    Article  Google Scholar 

  9. Roşu D, Caşcaval CN, Mustatǎ F et al (2002) Cure kinetics of epoxy resins studied by non-isothermal DSC data. Thermochim Acta 383(1–2):119–127

    Google Scholar 

  10. Ramis X, Cadenato A, Morancho JM et al (2003) Curing of a thermosetting powder coating by means of DMTA, TMA and DSC. Polymer 44(7):2067–2079

    Article  Google Scholar 

  11. Vyazovkin S (2001) Modification of the integral isoconversional method to account for variation in the activation energy. J Comput Chem 22(2):178–183

    Article  Google Scholar 

  12. Barton JM (1985) The application of differential scanning calorimetry (DSC) to the study of epoxy resin curing reactions, Epoxy resins and composites I. Springer, Berlin, pp 111–154

    Google Scholar 

  13. Harsch M, Karger-Kocsis J, Holst M (2007) Influence of fillers and additives on the cure kinetics of an epoxy/anhydride resin. Eur Polym J 43(4):1168–1178

    Article  Google Scholar 

  14. Tanaka Y, Kakiuchi H (1963) Study of epoxy compounds. Part I. curing reactions of epoxy resin and acid anhydride with amine and alcohol as catalyst. J Appl Polym Sci 7(3):1063–1081

    Article  Google Scholar 

  15. Tanaka Y, Kakiuchi H (1964) Study of epoxy compounds. Part VI. Curing reactions of epoxy resin and acid anhydride with amine, acid, alcohol, and phenol as catalysts. J Polym Sci A Gene Pap 2(8):3405–3430

    Article  Google Scholar 

  16. Fava RA (1968) Differential scanning calorimetry of epoxy resins. Polymer 9:137–151

    Article  Google Scholar 

  17. Robledo-Ortiz JR, Zepeda C, Gomez C et al (2008) Non-isothermal decomposition kinetics of azodicarbonamide in high density polyethylene using a capillary rheometer. Polym Test 27(6):730–735

    Article  Google Scholar 

  18. Tai HJ, Wang JB (1997) A study of the reaction kinetics involved in a crosslinked LDPE foam. J Cell Plast 33(4):304–317

    Article  Google Scholar 

  19. Tai HJ (2005) Bubble size distribution and elastic retraction in crosslinked metallocene polyolefin elastomer foams. J Polym Res 12(12):457–464

    Article  Google Scholar 

  20. Kim JH, Choi KC, Yoon JM (2006) The foaming characteristics and physical properties of natural rubber foams: effects of carbon black content and foaming pressure. J Ind Eng Chem 12(5):795–801

    Google Scholar 

  21. Wang BQ, Peng ZL, Zhang Y et al (2006) Study on foaming kinetics and preparation of EPDM foams. Plast Rubber Compos 35(9):360–367

    Article  Google Scholar 

  22. Charoeythornkhajhornchai P, Samthong C, Boonkerd K et al (2017) Effect of azodicarbonamide on microstructure, cure kinetics and physical properties of natural rubber foam. J Cell Plast 53(3):287–303

    Article  Google Scholar 

  23. Wang L, Yang X, Jiang T et al (2015) Cell morphology, bubbles migration, and flexural properties of non-uniform epoxy foams using chemical foaming agent. J Appl Polym Sci 131(23):205–212

    Google Scholar 

  24. Wang L, Yang X, Zhang J et al (2014) The compressive properties of expandable microspheres/epoxy foams. Compos B Eng 56:724–732

    Article  Google Scholar 

  25. Karger-Kocsis J (2009) Thermal Analysis of polymers: fundamentals and applications. Macromol Chem Phys 39(2):131–142

    Google Scholar 

  26. Vyazovkin S, Sbirrazzuoli N (1999) Kinetic methods to study isothermal and nonisothermal epoxy-anhydride cure. Macromol Chem Phys 200(10):2294–2303

    Article  Google Scholar 

  27. Ozawa T (1965) Kinetics in differential thermal analysis. Bull Chem Soc Jpn 38:1881–1886

    Article  Google Scholar 

  28. Matuana LM, Faruk O, Diaz CA (2009) Cell morphology of extrusion foamed poly (lactic acid) using endothermic chemical foaming agent. Biores Technol 100(23):5947–5954

    Article  Google Scholar 

  29. Peyser P, Bascom WD (1974) Kinetics of an anhydride-epoxy polymerization as determined by differential scanning calorimetry[M]//Analytical Calorimetry. Springer, Berlin, pp 537–554

    Google Scholar 

  30. Park SJ, Kim TJ, Lee JR (2000) Cure behavior of diglycidylether of bisphenol A/trimethylolpropane triglycidylether epoxy blends initiated by thermal latent catalyst. J Polym Sci B Polym Phys 38(16):2114–2123

    Article  Google Scholar 

  31. Park SJ, Jin FL (2004) Thermal stabilities and dynamic mechanical properties of sulfone-containing epoxy resin cured with anhydride. Polym Degrad Stab 86(3):515–520

    Article  Google Scholar 

  32. Sun L, Pang SS, Sterling AM et al (2002) Dynamic modeling of curing process of epoxy prepreg. J Appl Polym Sci 86(8):1911–1923

    Article  Google Scholar 

  33. Xia L, Zuo L, Zha S et al (2014) Kinetic research on low-temperature cure of epoxy adhesive. Int J Adhes Adhes 50:255–264

    Article  Google Scholar 

  34. Šesták J, Berggren G (1971) Study of the kinetics of the mechanism of solid-state reactions at increasing temperatures. Thermochim Acta 3(1):1–12

    Article  Google Scholar 

Download references

Acknowledgements

The authors greatly appreciate the financial support by National Nature Science foundation of China (Nos. 51503047; 51573063), Science and Technology Project of Guizhou Province ([2015]2077), International S&T Cooperation Program of Guizhou Province ([2014]7016), the Guangdong Science and Technology Planning Project (Nos. 2014B010104004 and 2013B090600126), and the Guangzhou Science and Technology Planning Project (No. 201604010013).

Author information

Authors and Affiliations

  1. National Engineering Research Center of Novel Equipment for Polymer Processing, The Key Laboratory for Polymer Processing Engineering of Ministry of Education, South China University of Technology, Guangzhou, 510640, China

    Lijun Wang & Xiangfang Peng

  2. Guizhou Material Industrial Technology Institute, Guiyang, 550014, Guizhou, China

    Lijun Wang & Yubi Ji

Authors
  1. Lijun Wang
    View author publications

    Search author on:PubMed Google Scholar

  2. Yubi Ji
    View author publications

    Search author on:PubMed Google Scholar

  3. Xiangfang Peng
    View author publications

    Search author on:PubMed Google Scholar

Corresponding author

Correspondence to Xiangfang Peng.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Wang, L., Ji, Y. & Peng, X. A new two-step process to prepare microcellular epoxy foams based on kinetic analysis. J Mater Sci 53, 1540–1555 (2018). https://doi.org/10.1007/s10853-017-1583-7

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s10853-017-1583-7

Keywords