Abstract
An accelerated carbonation test (at 5 % CO2, 22 °C and 55 % RH) was carried out on bulk and powdered cement paste samples incorporating two different supplementary cementitious materials: microsilica and nanosilica. Extensive characterization using thermogravimetric analysis, scanning electron microscopy with X-ray microanalysis, and image analysis was performed at various degrees of carbonation, to study the fundamental effects of nanosilica on carbonation of main hydration products, calcium hydroxide (CH) and calcium silicate hydrate (C–S–H). Results at every stage were compared with the effects of microsilica addition to cement paste. Results suggested that incorporation of small amounts of micro or nanosilica can decrease the total carbonation of cement paste. In particular, nanosilica could reduce carbonation (decalcification) of C–S–H and the depth of carbonation significantly.
Similar content being viewed by others
References
Gonzalez JA, Algaba JS, Andrade C (1980) Corrosion of reinforcing bars in carbonated concrete. Br Corros J 15:135–139
Francois R, Maso JC (1988) Effect of damage in reinforced concrete on carbonation or chloride penetration. Cem Concr Res 18:961–970
Gruyaert E, Heede PV, Belie ND (2013) Carbonation of slag concrete: effect of the cement replacement level and curing on the carbonation coefficient-effect of carbonation on the pore structure. Cem Conc Comp 35:39–48
Castellote M, Andrade C, Turrillas X, Campo J, Cuello GJ (2008) Accelerated carbonation of cement pastes in situ monitored by neutron diffraction. Cem Concr Res 38:1365–1373
Chen JJ, Thomas JJ, Jennings HM (2006) Decalcification shrinkage of cement paste. Cem Concr Res 36:801–809
Lim S, Mondal P (accepted) The effects of nanosilica addition on increased thermal stability of cement-based composite. ACI Mater J. doi:10.14359/51687177
Verbeck GJ (1958) Carbonation of Hydrated Portland Cement. J PCA Dev Labs 30:17–36
Houst YF, Wittmann FH (1994) Influence of porosity and water content on the diffusivity of CO2 and O2 through hydrated cement paste. Cem Concr Res 24:1165–1176
Dunster AM (1989) An investigation of the carbonation of cement paste using trimethylsilylation. Adv Cem Res 2:99–106
Richardson LG, Grove GW, Brough Dobson CM (1993) The carbonation of OPC and OPC/silica fume hardened cement pastes in air under conditions of fixed humidity. Adv Cem Res 5:81–86
Groves GW, Brough AR, Richardson IG, Dobson CM (1991) Progressive changes in the structure of hardened C3S cement pasted due to carbonation. J Am Ceram Soc 74:2891–2896
Papadakis VG (2000) Effect of supplementary cementing materials on concrete resistance against carbonation and chloride ingress. Cem Concr Res 30:291–299
Schubert P (1987) Carbonation behavior of mortars and concretes made with fly ash. ACI SP 100:1945–1962
Vennesland O, Gjorv OE (1983) Silica concrete: protection against corrosion of embedded steel. In: Proceedings of 1st international conference on the use of fly ash, silica fume and other mineral by-products in concrete, ACI SP 79:719–730
Kulakowski MP, Pereira FM, Molin DCCD (2009) Carbonation-induced reinforcement corrosion in silica fume concrete. Construt Build Mater 23:1189–1195
Mondal P, Shah SP, Marks LD (2010) Comparative study of the effect of microsilica and nanosilica in concrete. Trans Res Rec: J Transp Res Board 2141:6–9
Gaitero JJ, Campillo I, Guerrero A (2008) Reduction of the calcium leaching rate of cement paste by addition of silica nanoparticles. Cem Concr Res 38:1112–1118
Jain JA, Neithalath N (2009) Beneficial effects of small amount of nano-silica on the chemical stability of cement pastes exposed to neutral pH environments. ACI Mater J 267:59–74
Barneyback RS Jr, Diamond S (1981) Expression and analysis of pore fluids from hardened cement pastes and mortars. Cem Concr Res 11:279–285
Thiery M, Villian G, Dangla P, Platret G (2007) Investigation of the carbonation front shape on cementitious materials: effects of the chemical kinetics. Cem Concr Res 37:1047–1058
Lim S, Mondal P (2014) Micro- and nano-scale characterization to study thermal degradation of cement-based materials. Mater Charact 92:15–25
Hidalgo A, Domingo C, Garcia C, Petit S, Andrade C, Alonso C (2008) Microstructural changes in Portland cement-based materials due to natural and supercritical carbonation. J Mater Sci 43:3101–3111. doi:10.1007/s10853-008-2521-5
Borges PHR, Costa JO, Milestone NB, Lynsdale CJ, Streatfield RE (2010) Carbonation of CH and C–S–H in composite cement pastes containing high amounts of BFS. Cem Concr Res 40:284–292
Hidalgo A, Petit S, Domingo C, Alonso C, Andrade C (2007) Microstructural characterization of leaching effects of in cement pastes due to neutralization of their alkaline nature Part I: Portland cement pastes. Cem Concr Res 37:63–70
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Lim, S., Mondal, P. Effects of incorporating nanosilica on carbonation of cement paste. J Mater Sci 50, 3531–3540 (2015). https://doi.org/10.1007/s10853-015-8910-7
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-015-8910-7