Influence of deep cryogenic treatment on the thermal decomposition of Fe–C martensite

Journal of Materials Science volume 49, pages 8183–8191 (2014)Cite this article

Abstract

The beneficial effects of deep cryogenic treatment (DCT) at temperatures close to −180 °C on certain mechanical properties of steels are well known, although the metallurgical base mechanism of DCT still needs further clarification. In this study, the thermal decomposition of steel martensite (100Cr6) subjected to low-temperature soaking over different periods (SDCT = 5 min at −180 °C, LDCT = 24 h at −180 °C) is investigated by means of differential scanning calorimetry and dilatometry. The results were compared with those for the same conventionally quenched and tempered steel. Isochronal annealing experiments at different heating rates were performed, in order to highlight the main tempering stages and to obtain their relevant activation energies. DCT was clearly shown to lower the Ea of the pre-precipitation process more intensely than in the quenched steel. This result may probably be ascribed to an increased dislocation density and to the activation of the carbon segregation process in larger amounts of martensite. The precipitation of transition carbides was also enhanced by the low-temperature conditioning of martensite. As expected, DCT transformed the retained austenite, so that the corresponding peaks almost disappeared from both the dilatometric and the DSC patterns.

This is a preview of subscription content, access via your institution.

Access options

Buy single article

Instant access to the full article PDF.

USD 39.95

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5

References

  1. Brown J (1995) Big chill to extend gear life. Power Transm Des pp 59–61

  2. Zhirafar S, Rezaeian A, Pugh M (2007) Effect of cryogenic treatment on the mechanical properties of 4340 steel. J Process Technol 186(1–3):298–303

    Article  Google Scholar 

  3. Babu PS, Rajendran P, Rao KN (2005) Cryogenic treatment of M1, En19 and H13 tool steels to improve wear resistance. J Inst Eng India MM 86:64–67

    Google Scholar 

  4. Gulyaev AP (1998) Cold treatment of steel. Mat Sci Heat Treat 40(11):449–455

    Article  Google Scholar 

  5. Carlson EA (1991) Cold treating and cryogenic treatment of steel, ASM Handbook 4. ASM International, Metals Park, pp 203–206

    Google Scholar 

  6. Collins DN (1996) Deep cryogenic treatment of tool steels: a review. Heat Treat Met 23:40–42

    Google Scholar 

  7. Das D, Dutta AK, Ray KK (2009) Influence of varied cryotreatment on the wear behaviour of AISI D2 steel. Wear 266(1–2):297–309

    Article  Google Scholar 

  8. Barron RF (1982) Cryogenic treatment of metals to improve wear resistance. Cryogenics 8:409–413

    Article  Google Scholar 

  9. Meng F, Tagashira K, Sohma H (1994) Wear resistance and microstructure of cryogenic treated Fe-1.4Cr-1C bearing steel. Scr Metall Mater 31(7):865–868

  10. Gill S, Singh J, Singh R, Singh H (2011) Metallurgical principles of cryogenically treated tool steels –a review on the current state of science. Int J Adv Manuf Technol 54:59–82

    Article  Google Scholar 

  11. Gavriljuk VG, Sirosh VA, Petrov YUN, Tyshchenko AI, Theisen W, Kortmann A (2014) Carbide precipitation during tempering of a tool steel subjected to deep cryogenic treatment. Metall Mater Trans A 45A:2453–2465

    Article  Google Scholar 

  12. Dong Y, Xiaoping L, Hongshen X (1998) Deep cryogenic treatment of high-speed steel and its mechanism. Heat Treat Met 3:55–59

    Google Scholar 

  13. Lal DM, Renganarayanan S, Kalanidhi A (2001) Cryogenic treatment of argument wear resistance of tool and die steels. Cryogenics 41(3):149–155

    Article  Google Scholar 

  14. Yan XG, Li DY (2013) Effects of the sub-zero treatment condition on microstructure, mechanical behaviour and wear resistance of W9Mo3Cr4 V high speed steel. Wear 302:854–862

    Article  Google Scholar 

  15. Pellizzari M, Molinari A, Girardini L, Maldarelli L (2008) Deep cryogenic treatment of AISI M2 high speed steel. Int J Microstruct Mat 3(2–3):383–390

    Google Scholar 

  16. Pellizzari M (2008) Influence of deep cryogenic treatment on the properties of conventional and PM high speed steels. Metall Ital 9:7–22

    Google Scholar 

  17. Tyshchenko AI, Theisen W, Oppenkowski A (2010) Low-temperature martensitic transformation and deep cryogenic treatment of a tool steel. Mater Sci and Eng A 527:7027–7039

    Article  Google Scholar 

  18. Wierszyllowski I, Samolczyk J, Wieczorek S, Adrzejewska E, Marcinkowska A (2008) The influence of deep cryogenic treatment on transformation during tempering of quenched D2 steel Studies of XRD structures, DSC, dilatometry hardness and impact energy. Defect Diffus Forum 273–276:731–739

    Google Scholar 

  19. Gavriljuk VG, Theisen W, Sirosh VV (2013) Low-temperature martensitic transformation in tool steels in relation to their deep cryogenic treatment. Acta Mater 61:1705–1715

    Article  Google Scholar 

  20. Villa M, Pantleon K, Somers MAJ (2014) Evolution of compressive strains in retained austenite during sub-zero Celsius martensite formation and tempering. Acta Mater 65:383–392

    Article  Google Scholar 

  21. Villa M, Pantleon K, Somers MAJ (2013) Enhanced carbide precipitation during tempering of sub-zero celsius treated AISI 52100 bearing steel. In: Proceedings of the heat & surface engineering conference and expo, Chennai

  22. Huang JY, Zhu YT, Liao XZ, Beyerlein IJ, Bourke MA, Mitchell TE (2003) Microstructure of cryogenic treated M2 tool steel. Mater Sci and Eng A A339:241–244

    Article  Google Scholar 

  23. Akhbarizadeh A, Shafyei A, Golozar MA (2009) Effects of cryogenic treatment on wear behaviour of D6 tool steel. Mater Des 30:3259–3264

    Article  Google Scholar 

  24. Yen PL (1997) Formation of fine eta Carbides in special cryogenic and tempering process key lo improved properties of alloy steels. Ind Heat l.1:40–44

  25. Kelkar R, Nash P, Zhu Y (2003) The mechanism of property enhancement in M2 tool steel by cryogenic treatment. In: 45th MWSP Conference Proceedings pp 13–19

  26. Cheng L, Brakman CM, Korevaar BM, Mittemeijer EJ (1988) Stages in tempering of a martensitic 1.13 per cent carbon steel. Met Trans A 19A:2415–2426

    Article  Google Scholar 

  27. Mittermeijer E (1992) Analysis of the kinetics of phase transformations. J Mater Sci 27:3977–3987. doi:10.1007/BF01105093

    Article  Google Scholar 

  28. Haseeb ASMA, Arita M, Hayasi Y (2001) Thermal decomposition study of electrodeposited Fe-C and Fe-Ni-C alloys by differential scanning calorimetry. J Mat Sci 36:4739–4743. doi:10.1023/A:1017931106376

    Article  Google Scholar 

  29. Morra PV, Bottger AJ, Mittemeijer EJ (2001) Decomposition of iron based martensite. A kinetic analysis by means of differential scanning calorimetry and dilatometry. J Therm Anal Cal 64:905–914

    Article  Google Scholar 

  30. Pellizzari M, Molinari A, Gialanella S, Straffelini G (2001) Effetto del trattamento criogenico sulle proprietà microstrutturali dell’acciaio AISI H13. Metallurgia Italiana 1(1):21–27. doi:10.1023/A:1017931106376

    Google Scholar 

  31. Pellizzari M, Molinari A (2002) A deep cryogenic treatment of cold work tool steel. In: Proceedings of 6th International Tooling Conference, pp 547–557

  32. Cohen M (1970) Self-diffusion during plastic deformation. Inst Met Trans J I M 11:145–151

    Article  Google Scholar 

  33. Van Genderen MJ, Isac M, Bottger A, Mitemeijer EJ (1997) Aging and tempering behaviour of Iron-Nickel-Carbon and Iron-Carbon Martensite. Metall Trans A 28A:545–561

    Article  Google Scholar 

  34. Lee SH, Lee JC, Choi JY, Nam WJ (2010) Effects of deformation strain and ageing temperature on strain aging behaviour in a 304 stainless steel. Met Mater Int 16:21–26

    Article  Google Scholar 

  35. Villa M, Hansen MF, Pantleon K, Somers MAJ, (2013) In situ investigation of martensite formation in AISI 52100 bearing steel at subzero Celsius temperature. In: Proceedings of 2nd Mediterranean Conference & new Challenges on heat treatment and surface engineering, Dubrovnik, pp 237–244

  36. Wierszgyllowski I, Jakubowski J (1986) The influence of transformation progress on the activation energy changes during low temperature tempering of quenched steel. Scri Metall 20:49–54

    Article  Google Scholar 

  37. King HW, Glover SG (1906) Influence of alloying elements on the first stage of tempering in high-carbon steels. J Iron Steel Inst 193:281–288

    Google Scholar 

  38. Batz W, Mehl RF (1950) Diffusion coefficient of carbon in austenite. Trans AIME 188:553–560

    Google Scholar 

  39. Han K, Van Genderen MJ, Bottger A, Zandbergen HW, Mittemeijer EJ (2001) Initial stages of Fe-C martensite decomposition. Phil Mag A 81(3):741–757

    Article  Google Scholar 

  40. Perez M, Sidoroff C, Vincent A, Esnouf C (2009) Microstructural evolution of martensitic 100Cr6 bearing steel during tempering: from thermoelectric power measurements to the prediction of dimensional changes. Acta Mater 57:3170–3181

    Article  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. Department of Civil Engineering, University of Burgos, Avda. Cantabria s/n, 09006, Burgos, Spain

    M. Preciado

  2. Department of Industrial Engineering, University of Trento, Via Sommarive 9, 38123, Trento, Italy

    M. Pellizzari

Authors
  1. M. Preciado
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. M. Pellizzari
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to M. Preciado.

Electronic supplementary material

Below is the link to the electronic supplementary material.

Supplementary material 1 (PDF 63 kb)

Rights and permissions

Reprints and Permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Preciado, M., Pellizzari, M. Influence of deep cryogenic treatment on the thermal decomposition of Fe–C martensite. J Mater Sci 49, 8183–8191 (2014). https://doi.org/10.1007/s10853-014-8527-2

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s10853-014-8527-2

Keywords

search

Navigation