Abstract
The Ba5SiO4Cl6:Bi3+ phosphor was synthesized by high-temperature solid-state reaction and its luminescence property was investigated. The results showed that the Bi3+-doped Ba5SiO4Cl6 phosphors exhibited an intense blue–white light emission located at 480 nm and a broad excitation band from 230 to 340 nm. The Bi3+-doped Ba5SiO4Cl6 phosphors can be efficiently excited by the incident light of 220–340 nm, and the emission properties of the Bi3+-doped Ba5SiO4Cl6 samples are strongly dependent on the excitation wavelength. The emission color tunability can be obtained by changing the excitation wavelength. The visible region emission characteristics of Ba5SiO4Cl6:Bi3+ indicates that it can potentially be used as a new efficient blue–white luminescent material.
Similar content being viewed by others
References
Seo YS, Fujimoto Y, Nakatsuka M (2006) Opt Commun 266:169
Gorbenko V, Krasnikov A, Mihokova E, Nikl M, Zazubovich S, Zorenko Y (2013) J Lumin 134:469
Zorenko Y, Gorbenko V, Voznyak T, Jary V, Nikl M (2010) J Lumin 130:1963
Nakajima T, Isobe M, Tsuchiya T, Ueda Y, Manabe T (2010) Opt Mater 32:1618
Trnovcová V, Furár I, Schultze D (2008) Solid State Ion 179:131
Li C, Song ZG, Qiu JB, Yang ZW, Yu X, Zhou DC et al (2012) J Lumin 132:1807
Ding WJ, Wang J, Zhang M, Zhang QH, Su Q (2006) J Solid State Chem 179:3582
Poort SHM, Reijnhoudt HM et al (1996) J Alloy Compd 241:75
Ding WJ, Wang J, Liu ZM, Zhan M g, Su Q, Tang JK (2008) J Electrochem Soc 155:122
Ding WJ, Wang J, Zhang M, Zhang QH, Su Q (2007) Chem Phys Lett 435:301
Zhang XG, Wang XX, Huang JQ, Shi JX, Gong ML (2009) Opt Mater 32:75
Griscom DL (1977) J Non-Cryst Solids 24:155
Lobo RPSM, Gervais F (1996) Solid State Commun 98:61
Fujimoto Y (2010) J Am Ceram Soc 93:581
Ren JJ, Qiu JR, Chen DP, Hu X, Jiang XW, Zhu CG (2008) J Alloy Compd 463:L5
Srivastava AM (1998) J Lumin 78:239
Wang XL, Sheng QC, Hu LL, Zhang JJ (2012) Mater Lett 66:156
Rambabu U, Han SD (2013) Ceram Int 39:701
Lei BF, Liu YL, Liu J, Ye ZR, Shi CS (2004) J Rare Earths 22:443
Corazza A, Crivelli B, Martini M, Spinolo G, Vedda A (1995) Phys Rev B 53:9739
Garcia-Guinea J, Townsend PD, Sanchez-Munoz L, Rojo JM (1999) Phys Chem Miner 26:658
Acknowledgements
This work was supported by the National Natural Science Foundation of China (51002068) and Natural Science Foundation of Yunnan Province (2010ZC038).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Lai, S., Yang, Z., Wang, R. et al. Preparation and blue–white luminescence properties of Bi3+-doped Ba5SiO4Cl6 . J Mater Sci 48, 8566–8570 (2013). https://doi.org/10.1007/s10853-013-7676-z
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-013-7676-z