Abstract
The thermal stability of nanostructured Fe100−x−y Ni x Zr y alloys with Zr additions up to 4 at.% was investigated. This expands upon our previous results for Fe–Ni base alloys that were limited to 1 at.% Zr addition. Emphasis was placed on understanding the effects of composition and microstructural evolution on grain growth and mechanical properties after annealing at temperatures near and above the bcc-to-fcc transformation. Results reveal that microstructural stability can be lost due to the bcc-to-fcc transformation (occurring at 700 °C) by the sudden appearance of abnormally grown fcc grains. However, it was determined that grain growth can be suppressed kinetically at higher temperatures for high Zr content alloys due to the precipitation of intermetallic compounds. Eventually, at higher temperatures and regardless of composition, the retention of nanocrystallinity was lost, leaving behind fine micron grains filled with nanoscale intermetallic precipitates. Despite the increase in grain size, the in situ formed precipitates were found to induce an Orowan hardening effect rivaling that predicted by Hall–Petch hardening for the smallest grain sizes. The transition from grain size strengthening to precipitation strengthening is reported for these alloys. The large grain size and high precipitation hardening result in a material that exhibits high strength and significant plastic straining capacity.
Similar content being viewed by others
References
Darling KA, VanLeeuwen BK, Semones JE, Koch CC, Scattergood RO, Kecskes LJ, Mathaudhu SN (2011) Mater Sci Eng A 528(13–14):4365
Darling KA, VanLeeuwen BK, Koch CC, Scattergood RO (2010) Mater Sci Eng A 527(15):3572
Kirchheim R (2007) Acta Mater 55(15):5129
Liu F, Kirchheim R (2004) Scripta Mater 51(6):521
Trelewicz JR, Schuh CA (2009) Phys Rev B 79(9):094112
Saber M, Kotan H, Koch CC, Scattergood RO (2013) J Appl Phys 113(6):063515
Millett PC, Selvam RP, Saxena A (2007) Acta Mater 55(7):2329
Dake JM, Krill CE (2012) Scripta Mater 66(6):390
Kotan H, Darling KA, Saber M, Scattergood RO, Koch CC (2013) J Mater Sci 48(5):2251. doi:10.1007/s10853-012-7002-1
Saber M, Kotan H, Koch CC, Scattergood RO (2013) A predictive model for thermodynamic stability of grain size in ternary alloys (submitted)
Cohen MU (1935) Rev Sci Instrum 6(3):68
Langford JI, Wilson AJC (1978) J Appl Crystallogr 11:102
Williamson GK, Hall WH (1953) Acta Metal 1(1):22
Guduru RK, Darling KA, Kishore R, Scattergood RO, Koch CC, Murty KL (2005) Mater Sci Eng A 395(1–2):307
Malow TR, Koch CC (1997) Acta Mater 45(5):2177
Kotan H, Saber M, Koch CC, Scattergood RO (2012) Mater Sci Eng A 552:310
Schramm RE, Reed RP (1976) Metall Trans A 7(3):359
Shen TD, Schwarz RB, Feng S, Swadener JG, Huang JY, Tang M, Zhang H, Vogel SC, Zhao YS (2007) Acta Mater 55(15):5007
Murray JL (1992) Binary phase diagram. ASM International, Metals Park, OH
Raghavan V (2009) J Phase Equilib 30(1):104
Hillert M (1965) Acta Metall 13(3):227
Gladman T (1966) Proc R Soc Lond Ser A 294(1438):298
Humphreys FJ, Hatherly M (2004) Recrystallization and related annealing phenomena. Elsevier, Oxford
Kotan H, Darling KA, Saber M, Koch CC, Scattergood RO (2013) J Alloys Compd 551:621
Guduru RK, Scattergood RO, Koch CC, Murty KL, Guruswamy S, McCarter MK (2006) Scripta Mater 54(11):1879
Stephens JR, Witzke WR (1976) J Less-Common Met 48(2):285
Labusch R (1970) Phys Status Solidi 41(2):659
Schmauder S, Kohler C (2011) Comput Mater Sci 50(4):1238
Jang D, Atzmon M (2006) J Appl Phys 99(8):083504
Gleiter H (1992) Adv Mater 4(7–8):474
Koch CC, Weertman J (2002) Nanostructured materials. Noyes Publications, Norwich
Rupert TJ, Trelewicz JR, Schuh CA (2012) J Mater Res 27(9):1285
Nazarov AA (2000) Interface Sci 8(4):315
Das N, Sengupta P, Roychowdhury S, Sharma G, Gawde PS, Arya A, Kain V, Kulkarni UD, Chakravartty JK, Dey GK (2012) J Nucl Mater 420(1–3):559
Stein F, Palm A, Sauthoff G (2005) Intermetallics 13(10):1056
Brailsford AD, Wynblatt P (1979) Acta Metall 27(3):489
Arzt E (1998) Acta Mater 46(16):5611
Bacon DJ, Kocks UF, Scatterg RO (1973) Philos Mag 28(6):1241
Ferguson JB, Lopez H, Kongshaug D, Schultz B, Rohatgi P (2012) Metall Mater Trans A 43(6):2110
Gladman T (1999) Mater Sci Technol 15(1):30
Palm M (2005) Intermetallics 13(12):1286
Morris DG, Munoz-Morris MA, Requejo LM, Baudin C (2006) Intermetallics 14(10–11):1204
Acknowledgements
The research reported in this paper was supported by NSF-DMR under Grant Number 1005677.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Kotan, H., Darling, K.A., Saber, M. et al. Thermal stability and mechanical properties of nanocrystalline Fe–Ni–Zr alloys prepared by mechanical alloying. J Mater Sci 48, 8402–8411 (2013). https://doi.org/10.1007/s10853-013-7652-7
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-013-7652-7