Abstract
In spite of toxicity, hydrogen embrittlement susceptibility, and environmental issues, cadmium electroplating is usually applied on high strength AISI 4340 aeronautical steel due to its efficient protection against electrochemical corrosion. Ion vapor deposition (IVD) process with pure aluminum also offers good protection against corrosion with the advantages of decreasing hydrogen embrittlement susceptibility and improving the fatigue strength of metallic components. In this research, the effects of aluminum electroplating and IVD aluminum coating on the rotating bending fatigue strength of AISI 4340 steel were evaluated in comparison with cadmium electroplated specimens. Experimental fatigue results showed that both aluminum electroplating and IVD aluminum coatings are possible alternatives to cadmium electroplating.
Similar content being viewed by others
References
Nascimento MP, Voorwald HJC, Souza RC, Pigatin WL (2000) Plat Surf Finish 80:84
Nascimento MP, Souza RC, Pigatin WL, Voorwald HJC (2001) Int J Fatigue 23:607
Natishan PM, Lawrence SH, Foster RL, Lewis J, Sartwell BD (2000) Surf Coat Technol 130:218
Nevill BT (1993) Plat Surf Finish 80:14
Yu Q, Deffeyes J, Yasuda H (2001) Prog Org Coat 42:100
Camargo JAM, Voorwald HJC, Cioffi MOH, Costa MYP (2007) Surf Coat Technol 211:9448
Mattox DM (1998) Handbook of physical vapor deposition (PVD) processing: film formation, adhesion, surface preparation and contamination control. Noyes Publications, Westwood
Acknowledgement
Authors are grateful for the support by FAPESP through the process number 2006/03570-9 and to the CNPq through the processes number 304155/2006-3, 470074/2006-0, and 507240/2004-9.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Voorwald, H.J.C., Peres, M.P., Costa, M.Y.P. et al. Evaluation on fatigue strength of AISI 4340 steel aluminum coated by electroplating and IVD processes. J Mater Sci 45, 6094–6100 (2010). https://doi.org/10.1007/s10853-010-4695-x
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-010-4695-x