Abstract
Soda alumina borosilicate glasses of composition (24-y)Na2O·yAl2O3·14B2O3·37SiO2·25Fe2O3, y = 8, 12, 14, 16 mol%, were melted using Fe2O3 as raw material. Besides, samples with y = 12 and Fe2O3 concentrations of 14.32, 17.8, and 25.0 mol% were prepared from FeC2O4·2H2O as raw material. The X-ray diffraction analyses showed the presence of magnetite for the samples from all the investigated compositions. Transmission electron microscopy (TEM) evidenced that all the samples are phase separated and droplets in the diameter range 100–1000 nm, enriched in iron, are formed. Inside these droplets, numerous small magnetite particles, with size in the 25–40 nm interval, are crystallized.
Similar content being viewed by others
Abbreviations
- XRD:
-
X-ray diffraction
- SEM:
-
Scanning electron microscopy
- TEM:
-
Transmission electron microscopy
- EDX analysis:
-
Energy dispersive micro X-ray analysis
- JCPDS:
-
Joint Committee on Powder Diffraction Standards
References
Karamanov A, Pelino M (2001) J Non-Cryst Solids 281:139
Ehrt D, Reiß H, Vogel W (1976) Silikattechnik 27:304
Kingery WD, Bowen HK, Uhlmann DR (1991) Introduction to ceramics. Wiley, Singapore
Kunath-Fandrei G, Ehrt D, Jäger C (1995) Z Naturforsch 50a:413
El-Egili K (2003) Phys B 325:340
Hornschuh S, Messerschmidt B, Possner T, Possner U, Rüssel C (2004) J Non-Cryst Solids 347:121
Hong L, Hrma P, Vienna JD, Qian M, Su Y, Smith DE (2003) J Non-Cryst Solids 331:202
Benne D, Rüssel C, Menzel M, Becker K (2004) J Non-Cryst Solids 337:232
Schirmer H, Keding R, Rüssel C (2004) J Non-Cryst Solids 336:37
Benne D, Rüssel C, Niemer D, Menzel M, Becker KD (2004) J Non-Cryst Solids 345–346:203
Romero M, Rincon JM (1999) J Am Ceram Soc 82:1313
Woltz S, Hiergeist R, Görnert P, Rüssel C (2006) J Magn Magn Mater 298:7
Woltz S, Rüssel C (2004) J Non-Cryst Solids 337:226
Odenbach S (2004) J Phys Condens Matter 16:1135
Zhou GY et al (2004) Smart Mater Struct 13:309
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Harizanova, R., Völksch, G. & Rüssel, C. Microstructures formed during devitrification of Na2O·Al2O3·B2O3·SiO2·Fe2O3 glasses. J Mater Sci 45, 1350–1353 (2010). https://doi.org/10.1007/s10853-009-4090-7
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-009-4090-7